Preparation method of water-soluble palladium nitrate

A palladium nitrate and water-soluble technology, which is applied in the field of catalysis, can solve the problems affecting the loading and dispersion of active component palladium, the low water solubility of nitrate compounds, and the corrosion of the purifier shell, so as to simplify transportation procedures, save transportation costs, and save The effect of production costs

Active Publication Date: 2015-08-05
KUNMING GUIYI METAL MATERIAL
View PDF3 Cites 5 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

However, in the production process, it is also found that the use of such nitrate precursors also has some disadvantages and shortcomings: 1) The water solubility of nitrate compounds is very small, and it needs to be dissolved with nitric acid
Therefore, the impregnation solution has a strong acidity, which will dissolve the surface of the carrier material (γ-Al2O3) and the modified material (rare earth oxide), destroy the original struc

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0035] A kind of preparation method of water-soluble palladium nitrate, comprises the steps:

[0036] Step (1), after mixing aqua regia and equal volume of water evenly, add the raw material palladium to it, the solid-liquid ratio is 0.9:3, keep boiling for 2 hours, filter, and take the filtrate;

[0037] Step (2), adding ammonia water to the filtrate obtained in step (1) until the pH value is 8, then performing hydrolysis for 8 minutes, filtering, and washing the filter residue with hot water at 40°C until the pH is 7 to obtain palladium material;

[0038] Step (3), add the palladium material obtained in step (2) into concentrated nitric acid and record the total volume. The solid-to-liquid ratio of palladium material to concentrated nitric acid is 1:2.4, and the mass of palladium material to be dissolved is 1 / 1 of the total mass. At 3 o'clock, add the dilute nitric acid that massfraction is 50% to original total volume, then be heated to constant boiling, until palladium mat...

Embodiment 2

[0042] A kind of preparation method of water-soluble palladium nitrate, comprises the steps:

[0043] Step (1), after mixing aqua regia and equal volume of water evenly, add the raw material palladium to it, the solid-liquid ratio is 1.1:3, keep boiling for 3 hours, filter, and take the filtrate;

[0044] Step (2), adding ammonia water to the filtrate obtained in step (1) until the pH value is 8, then performing hydrolysis for 12 minutes, filtering, washing the filter residue with hot water at 70°C until the pH is 7, and obtaining palladium material;

[0045] Step (3), add the palladium material obtained in step (2) into concentrated nitric acid and record the total volume. The solid-to-liquid ratio of palladium material to concentrated nitric acid is 1:2.6, and the mass of palladium material to be dissolved is 1 / 1 of the total mass. At 3 o'clock, add the dilute nitric acid that massfraction is 50% to original total volume, then be heated to constant boiling, until palladium m...

Embodiment 3

[0049] A kind of preparation method of water-soluble palladium nitrate, comprises the steps:

[0050] Step (1), after mixing aqua regia and equal volume of water evenly, add the raw material palladium to it, the solid-liquid ratio is 1:3, keep boiling for 2.5h, filter, and take the filtrate;

[0051] Step (2), adding ammonia water to the filtrate obtained in step (1) until the pH value is 8, then performing hydrolysis for 10 minutes, filtering, washing the filter residue with hot water at 60°C until the pH is 7, and obtaining palladium material;

[0052] Step (3), add the palladium material obtained in step (2) into the concentrated nitric acid and record the total volume. The solid-liquid ratio of the palladium material to the concentrated nitric acid is 1:2.5, and the mass of the palladium material to be dissolved is 1 / 2 of the total mass. At 3 o'clock, add the dilute nitric acid that massfraction is 50% to original total volume, then be heated to constant boiling, until pal...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

PUM

No PUM Login to view more

Abstract

The invention relates to a preparation method of water-soluble palladium nitrate and belongs to the technical field of catalysis. By means of the method, Pd(NO3)2.nH2O can be prepared in batches, wherein the content of palladium in the Pd(NO3)2.nH2O crystal can reach 41%. The Pd(NO3)2.nH2O product is good in water solubility and an aqueous solution thereof is not less than eight hours. The reparation method is safe and reliable. The Pd(NO3)2.nH2O crystal product is stable in performances and is good in uniformity, and can satisfy a requirement of catalyst precursors. The preparation method changes a situation that the Pd(NO3)2.nH2O crystal in the prior art does not have water solubility and is difficult to use, can simplify transportation procedure and save transportation cost, reduces loss of palladium and acid, can reduce emission of waste gas and is easy to popularize.

Description

technical field [0001] The invention belongs to the technical field of catalysis, and in particular relates to a preparation method of water-soluble palladium nitrate. Background technique [0002] With the rapid development of my country's economy, noble metal functional material catalysts are widely used in industry. Especially the automotive industry. Since the 1970s, a large number of functional material catalysts for automobile exhaust purification have been popularized and used, and soon developed into the largest functional material catalysts in China. As a "noble cluster catalyst" among domestic noble metal functional material catalysts, palladium nitrate is mainly used as one of the coating formulations on the carrier of automobile exhaust gas purification catalysts. The annual demand for palladium nitrate in the automobile exhaust purifying agent market is about 70-120 tons / year, which is equivalent to 30-50 tons / year for metal palladium. 20%~30% of the gross ou...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

Application Information

Patent Timeline
no application Login to view more
IPC IPC(8): B01J27/25C01G55/00
Inventor 李雄郑恩华黄言生许思勇向明才
Owner KUNMING GUIYI METAL MATERIAL
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Try Eureka
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap