A kind of preparation method of mesh cloth for shoes

A technology for shoes and mesh cloth, applied in the field of mesh cloth, can solve the problems of no moisture absorption, deodorization, antibacterial, etc., and achieve the effect of improving washing resistance, antibacterial performance, and adhesion

Active Publication Date: 2016-02-17
FUJIAN JINJIANG HUAYU WEAVING
View PDF9 Cites 10 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

The mesh material used in traditional sports shoe fabrics is conventional polyester monofilament or nylon monofilament, which has no functions such as moisture absorption, deodorization, and antibacterial, so it is difficult to apply it to high value-added shoe fabrics and develop functional materials. The mesh products meet the needs of high value-added shoe materials. The development of fabrics is of great significance to enhance the competitiveness of enterprises and meet market demand.

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0033] A preparation method of mesh cloth for shoes, the specific steps are:

[0034] (1) Preparation of modifier for shoes

[0035] Treat the tea waste residue in hydrogen peroxide with a mass fraction of 3% at 90-95°C for 30-45 minutes to oxidize the tea waste residue, filter and wash, and then use 0.5-2.0mol / L sulfuric acid or nitric acid solution to re-heat at 90-95 ℃ heat treatment for 45-60 minutes to acidify and activate the oxidized tea waste residue, then filter and wash, then soak the acidified tea waste residue in 0.2mol / L zinc chloride solution for 90 minutes, and filter it in the air at 5°C Raise the heating rate to 300°C / min, stay for 60min, and then raise the heating rate to 600°C at a rate of 10°C / min in an oxygen-poor atmosphere, and stay for 60min to obtain an antibacterial matrix containing nano-zinc oxide; use three-roll grinding Coarsely grind the antibacterial matrix in a three-roller mill for 3-4 hours, then use a sieve to filter out a powder of less th...

Embodiment 2

[0053] A preparation method of mesh cloth for shoes, the specific steps are:

[0054] (1) Preparation of modifier for shoes

[0055] Treat the tea waste residue in hydrogen peroxide with a mass fraction of 5% at 90-95°C for 30-45 minutes to oxidize the tea waste residue, filter and wash, and then use 0.5-2.0mol / L sulfuric acid or nitric acid solution to re-heat at 90-95 ℃ heat treatment for 45-60min to acidify and activate the oxidized tea waste residue, then filter and wash, then soak the acidified tea waste residue in 0.8mol / L zinc chloride solution for 90min, filter and place in the air at 5°C Raise the heating rate to 300°C / min, stay for 60min, and then raise the heating rate to 600°C at a rate of 10°C / min in an oxygen-poor atmosphere, and stay for 60min to obtain an antibacterial matrix containing nano-zinc oxide; use three-roll grinding Coarsely grind the antibacterial matrix in a three-roller mill for 3-4 hours, then use a sieve to filter out a powder of less than 100 ...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

PropertyMeasurementUnit
particle diameteraaaaaaaaaa
quality scoreaaaaaaaaaa
quality scoreaaaaaaaaaa
Login to View More

Abstract

The invention relates to a manufacturing method of screen cloth for shoes. The manufacturing method comprises the steps of 1 preparing a modifying agent for shoes, 2 preparing an anti-microbial spinning oil solution for shoes, 3 preparing modified polyester master batches for shoes, 4 preparing modified polyester monofilaments for shoes, and 5 manufacturing the screen cloth for shoes. The manufactured screen cloth for shoes has good anti-microbial healthcare effect.

Description

【Technical field】 [0001] The invention relates to the technical field of mesh cloth, in particular to a preparation method of mesh cloth for shoes. 【Background technique】 [0002] Mesh is a kind of warp knitted fabric with mesh structure. Due to its excellent air permeability and moisture permeability, the materials used are mainly polyester, nylon, etc., which have excellent wear resistance, good resilience, light material, and easy cleaning. It is widely used in shoe materials and other fabrics. At present, the consumption of sports shoes has exceeded 40% of the total amount of footwear, reaching 6 billion per year, and the wearing comfort and functionality have put forward higher requirements for high-end products. At present, the domestic demand for functional mesh materials The method of coating is mainly used, and the three-dimensional mesh structure of the mesh is inevitably blocked during the coating process, which affects the air permeability and moisture permeabil...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
Patent Type & Authority Patents(China)
IPC IPC(8): D06M13/513D06M15/03D06M15/53D01F6/92D01F1/10C08B15/04C08B15/02D01D5/08D01D5/092D01D5/16
Inventor 苏成喻柯文新陈志鹏石建良杨孝清
Owner FUJIAN JINJIANG HUAYU WEAVING
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Patsnap Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Patsnap Eureka Blog
Learn More
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic, Popular Technical Reports.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap|About US| Contact US: help@patsnap.com