Negative ion ecological silicon crystal material, production method and application in decorative panels

A production method and technology of negative ions, applied in the field of architectural decoration, can solve the problems of inappropriate use, easy discoloration and yellowing, etc., and achieve the effect of eliminating indoor peculiar smell

Active Publication Date: 2017-01-11
湖北星立方科技有限公司
View PDF4 Cites 0 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

The shortcomings of photocatalytic technology are mainly manifested in two aspects: 1. Photocatalytic materials must be exposed to light or ultraviolet rays to function, and the application will not work in an environment where they are not exposed to light or ultraviolet rays; 2. The main photocatalysts Nano TiO2 is used. After TiO2 is added to the material, it is easy to change color and turn yellow. It is not suitable for use in occasions with high requirements on appearance.

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • Negative ion ecological silicon crystal material, production method and application in decorative panels
  • Negative ion ecological silicon crystal material, production method and application in decorative panels
  • Negative ion ecological silicon crystal material, production method and application in decorative panels

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0062] Example 1: Prepare a 600mm*600mm negative ion ecological silicon crystal plate

[0063] Negative ion ecological silicon crystal material:

[0064] Premixed powder: water: modified polymer solution: silicone gypsum waterproofing agent: glass fiber chopped strands = 1000: (750-825): (27-60): (30-90): (10-20) ;:

[0065] Wherein, the mass ratio of premixed powder raw materials is:

[0066] Hemihydrate gypsum powder: negative ion powder: white Portland cement = 100: (3 ~ 30): (2.5 ~ 5.0);

[0067] Water in the modified polymer solution: polyvinyl alcohol aqueous solution: silicone defoamer=1000:500:(0.3~5);

[0068] The polyvinyl alcohol aqueous solution is prepared by hydrolyzing 6 mass parts of polyvinyl alcohol in 1000 mass parts (90-100° C.) of hot water.

[0069] The production method of negative ion ecological silicon crystal material:

[0070] Include the following steps:

[0071] (1) Pre-mixed powder pretreatment step: Pre-mixed hemihydrate gypsum powder, nega...

Embodiment 2

[0090] Prepare a 600mm*600mm negative ion ecological silicon crystal plate

[0091] Negative ion ecological silicon crystal material:

[0092] Premix powder: water: modified polymer solution: silicone gypsum waterproofing agent: glass fiber chopped strands = 1000: 780: 35: 50: 15

[0093] Wherein, the mass ratio of premixed powder raw materials is:

[0094] Hemihydrate gypsum powder: negative ion powder: white Portland cement = 100:8:3;

[0095] Water in the modified polymer solution: polyvinyl alcohol aqueous solution: silicone defoamer=1000:500:3;

[0096] The polyvinyl alcohol aqueous solution is prepared by hydrolyzing 6 mass parts of polyvinyl alcohol in 1000 mass parts (90-100° C.) of hot water.

[0097] The production method of negative ion ecological silicon crystal material:

[0098] Include the following steps:

[0099] (1) Pre-mixed powder pretreatment step: pre-mixed hemihydrate gypsum powder, negative ion powder and white Portland cement according to the mass...

Embodiment 3

[0116] The application of the negative ion ecological silicon crystal material in the decorative plate made in embodiment 1 and embodiment 2.

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

PropertyMeasurementUnit
whitenessaaaaaaaaaa
lengthaaaaaaaaaa
specific surface areaaaaaaaaaaa
Login to View More

Abstract

The invention discloses an anion ecological crystalline silicon material which comprises premixed powder, water, a modified polymer solution, an organic silicon gypsum waterproof agent and glass fiber chopped strands, which are mixed at a ratio, wherein the premixed powder comprises raw materials of hemihydrate gypsum powder, anion powder and white portland cement; the modified polymer solution comprises water, a polyvinyl alcohol water solution and an organic silicon defoamer. The invention further discloses a production method for the anion ecological crystalline silicon material. The anion ecological crystalline silicon material, the production method and the application have the advantages that air can be purified, indoor smell, various harmful gases, irritant gases such as benzene, formaldehyde, ketone and ammonia volatilizing from a decorative material in the indoor decoration process as well as peculiar smell harm to human body in daily life can be effectively eliminated; excellent antibacteria and sterilization functions and excellent water resistance are achieved.

Description

technical field [0001] The invention relates to the field of architectural decoration, in particular to an anion ecological silicon crystal material and a decorative plate, and also to a production method of an anion ecological silicon crystal material and a decorative plate. Air can be made into building materials such as plates, lines, pipes, and putty; it can also be made into decorative materials such as background walls, partition walls, and ceilings; it can also be made into functional products such as decorations and handicrafts. Background technique [0002] In the existing air purification technology, it is mainly divided into pollution adsorption technology and photocatalytic technology. [0003] Pollution adsorption technology is to use porous fixed adsorbent to treat air, so that one or several substances in the air are adsorbed on the surface of solid adsorbent. The adsorbents that are widely used now are granular activated carbon and activated carbon fiber, an...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
Patent Type & Authority Patents(China)
IPC IPC(8): C04B28/04C04B14/42
Inventor 李俊唐红定
Owner 湖北星立方科技有限公司
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Patsnap Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Patsnap Eureka Blog
Learn More
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic, Popular Technical Reports.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap|About US| Contact US: help@patsnap.com