Preparation method of high-temperature resistant conveying belt covering glue

A conveyor belt and covering rubber technology, which is applied in the field of preparation of high-temperature-resistant conveyor belt covering rubber, can solve the problems of small profit margins, delamination of covering rubber, and high cost of EPDM rubber, so as to improve service life, reduce costs, The effect of improving the economic efficiency and experience benefit of the enterprise

Inactive Publication Date: 2015-09-30
SHANDONG LONGYUAN RUBBER
View PDF4 Cites 9 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

Nowadays, many high-temperature-resistant covering rubber materials are EPDM rubber. Using EPDM rubber alone not only has poor adhesion performance, but also causes delamination of the covering rubber, and the processing performance of EPDM rubber is poor, which affects production during production. Efficiency, the most important thing is that the cost of EPDM is higher and the profit margin is small

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0019] The formula ratio is based on parts by weight: 30 parts of EPDM rubber, 70 parts of styrene butadiene rubber, 40 parts of carbon black N220, 10 parts of mica powder, 10 parts of light calcium carbonate, 5 parts of dicumyl peroxide, 1 part of sulfur Parts, sulfenamide accelerator CZ 1.2 parts, thiuram accelerator DTDM 1.2 parts, zinc oxide 10 parts, magnesium oxide 5 parts, stearic acid 2 parts, coupling agent Si-69 1 part, carbon 5 resin 10 parts, 10 parts of high temperature paraffin oil, 2 parts of antioxidant 4010NA, 2 parts of antioxidant RD, 1 part of antioxidant BLE.

[0020] The specific steps of the method for preparing cover rubber for high temperature resistant conveyor belt are as follows:

[0021] (1) One-stage mixing: Put EPDM rubber and styrene butadiene rubber into the internal mixer, mix for 2-4 minutes, add carbon black N220, mica powder, light calcium carbonate, zinc oxide, and oxidation Magnesium, stearic acid, coupling agent Si-69, carbon 5 petroleum res...

Embodiment 2

[0024] The formula ratio is based on parts by weight: 45 parts of EPDM rubber, 55 parts of styrene butadiene rubber, 50 parts of carbon black N234, 10 parts of mica powder, 10 parts of light calcium carbonate, 4.5 parts of dicumyl peroxide, 1 part of sulfur Parts, sulfenamide accelerator NS 1.2 parts, thiuram accelerator DTDM 1 part, zinc oxide 10 parts, magnesium oxide 8 parts, stearic acid 1 part, coupling agent Si-69 1 part, terpene resin 10 parts, 12 parts of high temperature paraffin oil, 2 parts of antioxidant 4010NA, 2 parts of antioxidant RD, 1 part of antioxidant BLE.

[0025] The specific steps of the method for preparing cover rubber for high temperature resistant conveyor belt are as follows:

[0026] (1) One-stage mixing: first put EPDM rubber and styrene butadiene rubber into the internal mixer, mix for 2-4 minutes, add carbon black N234, mica powder, light calcium carbonate, zinc oxide, and oxidation Magnesium, stearic acid, coupling agent Si-69, terpene resin, anti...

Embodiment 3

[0029] The formula ratio is based on parts by weight: 55 parts of EPDM rubber, 45 parts of styrene butadiene rubber, 45 parts of carbon black N234, 7 parts of white carbon black, 12 parts of light calcium carbonate, 4.0 parts of dicumyl peroxide, sulfur 1 part, sulfenamide accelerator NS 1.2 parts, thiuram accelerator DTDM 1.2 parts, zinc oxide 10 parts, magnesium oxide 8 parts, stearic acid 1 part, coupling agent Si-69 1 part, terpene 10 parts of resin, 12 parts of high temperature paraffin oil, 2 parts of antioxidant 4010NA, 2 parts of antioxidant RE, 1 part of antioxidant BLE.

[0030] The specific steps of the method for preparing cover rubber for high temperature resistant conveyor belt are as follows:

[0031] (1) One-stage mixing: first put EPDM rubber and styrene butadiene rubber into the internal mixer, mix for 2-4min, add carbon black N234, white carbon black, light calcium carbonate, zinc oxide in proportion, Magnesium oxide, stearic acid, coupling agent Si-69, terpene ...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

No PUM Login to View More

Abstract

The invention discloses a preparation method of high-temperature resistant conveying belt covering glue. The high-temperature resistant conveying belt covering glue comprises the following components in parts by weight: 30-50 parts of ethylene propylene diene monomer rubber, 40-70 parts of butadiene styrene rubber, 40-80 parts of reinforcing fillers, 2.5-8 parts of a vulcanizing agent, 0.2-8 parts of a vulcanizing accelerator, 2-20 parts of a vulcanizing activator, 5-10 parts of a coupling agent, 5-35 parts of a plasticizer and 1-5 parts of anti-aging agent. The preparation method comprises the following steps: (1) primarily mixing; and (2) secondarily mixing. The preparation method has the beneficial effects that a high-temperature severe environment in an sintered ore workshop can be adapted, the cost of the high-temperature resistant conveying belt is lowered, the service life of the high-temperature resistant conveying belt is prolonged, and the economic efficiency and the experience benefit of an enterprise are increased; the preparation method is suitable for being generally popularized and used.

Description

Technical field: [0001] The invention relates to the technical field of wood conveyor belts, in particular to a method for preparing high temperature resistant conveyor belt covering rubber. Background technique: [0002] EPDM rubber is a carbon chain saturated non-polar rubber. It does not react with strong oxidants, strong reducing agents, strong acids, and strong bases at room temperature, and is not easily polarized. It is an ideal high temperature resistant covering rubber material. Nowadays, many high-temperature resistant covering rubber materials are EPDM rubber. Single use of EPDM rubber not only has poor adhesion performance, but also causes delamination of the cover rubber, and the processing performance of EPDM rubber is poor, which affects production. Efficiency, the most important thing is that EPDM rubber has a higher cost and a small profit margin. Summary of the invention [0003] The purpose of the present invention is to overcome the shortcomings of the prior a...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
IPC IPC(8): C08L9/06C08L23/16C08K13/02
CPCC08L9/06C08L23/16C08L2201/08C08L2205/035C08L57/02C08L91/06C08K13/02C08K3/04C08K3/36C08K5/14C08K2003/2296C08K2003/222
Inventor 陈志瑞陈玉斌禹振文王凯
Owner SHANDONG LONGYUAN RUBBER
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Patsnap Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Patsnap Eureka Blog
Learn More
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic, Popular Technical Reports.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap|About US| Contact US: help@patsnap.com