Water-borne inorganic anti-corrosive paint added with lithium stearate

A technology of lithium octadecanoate and anti-corrosion paint, applied in anti-corrosion coatings, alkali metal silicate coatings, coatings and other directions, can solve problems such as poor electrical conductivity, and achieve the effects of good stability and simple preparation process

Inactive Publication Date: 2015-10-28
严致迪
View PDF5 Cites 5 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

However, the organic film formers of organic zinc-rich paints have poor electrical conductivity

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0017] Pour 200g of sodium silicate solution into a heatable container and heat it slowly. When the temperature of the solution reaches 60°C, add 100g of silicon acrylic emulsion dropwise into the container and keep stirring. After the dropwise addition, stop Heating, after the system temperature drops to room temperature, add 30g of titanate coupling agent to the container, and increase the stirring speed, then add 600g of 500 mesh ultrafine zinc powder, and finally add 30g of MgCl 2 Aqueous solution and 40g octadecanoic acid lithium salt promptly get a kind of water-based inorganic anticorrosion paint that adds octadecanoic acid lithium salt.

Embodiment 2

[0019] Pour 500g of sodium silicate solution into a heatable container and heat it slowly. When the temperature of the solution reaches 65°C, add 200g of silicon acrylic emulsion dropwise into the container and keep stirring. After the dropwise addition, stop Heating, after the system temperature drops to room temperature, add 100g of titanate coupling agent to the container, and increase the stirring speed, then add 1000g of 550 mesh ultrafine zinc powder, and finally add 80g of MgCl 2 Aqueous solution and 120g octadecanoic acid lithium salt promptly get a kind of water-based inorganic anticorrosion paint that adds octadecanoic acid lithium salt.

Embodiment 3

[0021] Pour 1500g of sodium silicate solution into a heatable container and heat it slowly. When the temperature of the solution reaches 75°C, add 750g of silicon acrylic emulsion dropwise into the container and keep stirring. After the dropwise addition, stop Heating, after the system temperature drops to room temperature, add 150g of titanate coupling agent to the container, and increase the stirring speed, then add 2550g of 600 mesh ultrafine zinc powder, and finally add 150g of MgCl 2 Aqueous solution and 200g octadecanoic acid lithium salt promptly get a kind of water-based inorganic anticorrosion paint that adds octadecanoic acid lithium salt.

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

No PUM Login to View More

Abstract

The invention relates to water-borne inorganic anti-corrosive paint added with lithium stearate serving as a stabilizer. A preparation method of the paint comprises the steps that an appropriate amount of sodium silicate solution is taken and poured into a vessel which can be heated, slow heating is conducted through a heat source, when the temperature rises to about 70 DEG C, silicone acrylic emulsion is added into the vessel, heating is stopped after the mixture is thoroughly mixed, a titanate coupling agent and zinc powder are sequentially added, stirring is accelerated for mixing, a MgC12 aqueous solution and the lithium stearate serving as a stabilizer are added at last, and the water-borne inorganic anti-corrosive paint added with the lithium stearate is obtained after the mixture is evenly mixed. The prepared paint is good in stability performance, the preparation technology is simple, and the water-borne inorganic anti-corrosive paint added with the lithium stearate has better application prospect.

Description

technical field [0001] The invention relates to an anti-corrosion paint and a preparation method thereof, in particular to a water-based inorganic zinc-rich anti-corrosion paint added with stearate and a preparation method thereof, belonging to the field of paint chemical industry. Background technique [0002] Steel is widely used in our lives, such as the automobile industry, manufacturing industry, construction industry, transportation industry and other industries, but the corrosion resistance of steel is poor, and corrosion resistance is very important for steel. According to statistics, every year due to corrosion The loss accounts for about 10%-20% of the annual output. Corrosion is generally caused by chemical or electrochemical multiphase reactions between the metal surface and the medium. After corrosion, the mechanical properties such as strength and toughness of the steel material will be significantly reduced, and the metal will be damaged. The geometric shape o...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
Patent Type & Authority Applications(China)
IPC IPC(8): C09D1/02C09D5/10C09D7/12
Inventor 严致迪
Owner 严致迪
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Patsnap Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Patsnap Eureka Blog
Learn More
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic, Popular Technical Reports.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap|About US| Contact US: help@patsnap.com