Insulating material

A technology of insulating materials and clay, applied in the field of materials, can solve the problems of single performance of insulating materials and limiting the service life of on-load tap-changers.

Inactive Publication Date: 2015-11-18
CHONGQING YANGDI ELECTROMECHANICAL
View PDF1 Cites 14 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

[0004] The invention provides an insulating material to solve the problem that the existing insul

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0015] Insulating materials, the ingredients and parts by weight are: 20 parts of nano-scale silicon dioxide, 20 parts of polycarbonate resin, 20 parts of aluminum hydroxide, 10 parts of clay, 80 parts of polyethylene, 3 parts of metallocene polyethylene, polyethylene 1 part of glycol, 30 parts of silicone rubber, 2 parts of vulcanizing agent, 4 parts of diluent, 2 parts of fumed silica, 20 parts of quartz powder, 4 parts of silicone oil, 54 parts of polyether ether ketone resin, talcum powder 10 parts, 13 parts of light calcium carbonate, 9 parts of lubricant, 8 parts of antioxidant, 10 parts of calcined mica.

[0016] After testing, the insulating material of the present invention has an insulation resistance of 4.3*10 after soaking in water 7 In Europe, the bending strength is 125MPa, the compressive strength is 130MPa, the parallel layer breakdown voltage is 50KV, and the heat resistance temperature is 190 degrees, which is 5.6% higher than the temperature of the same grad...

Embodiment 2

[0018] Insulating materials, the ingredients and parts by weight are: 28 parts of nano-scale silicon dioxide, 28 parts of polycarbonate resin, 40 parts of aluminum hydroxide, 20 parts of clay, 100 parts of polyethylene, 10 parts of metallocene polyethylene, polyethylene 5 parts of glycol, 50 parts of silicone rubber, 5 parts of vulcanizing agent, 8 parts of diluent, 5 parts of fumed silica, 40 parts of quartz powder, 8 parts of silicone oil, 72 parts of polyether ether ketone resin, talcum powder 17 parts, 20 parts of light calcium carbonate, 18 parts of lubricant, 16 parts of antioxidant, 16 parts of calcined mica.

[0019] After testing, the insulating material of the present invention has an insulation resistance of 5.0*10 after soaking in water 7 In Europe, the bending strength is 134MPa, the compressive strength is 142MPa, the parallel layer breakdown voltage is 55KV, and the heat resistance temperature is 200 degrees, which is 11.1% higher than the temperature of the sam...

Embodiment 3

[0021] Insulating materials, the ingredients and parts by weight are: 24 parts of nano-scale silicon dioxide, 24 parts of polycarbonate resin, 30 parts of aluminum hydroxide, 15 parts of pottery clay, 90 parts of polyethylene, 6.5 parts of metallocene polyethylene, polyethylene 3 parts of glycol, 40 parts of silicone rubber, 3.5 parts of vulcanizing agent, 6 parts of diluent, 3.5 parts of fumed silica, 30 parts of quartz powder, 6 parts of silicone oil, 63 parts of polyetheretherketone resin, talcum powder 13.5 parts, 16.5 parts of light calcium carbonate, 13.5 parts of lubricant, 12 parts of antioxidant, 13 parts of calcined mica.

[0022] After testing, the insulation resistance of the insulating material of the present invention after soaking in water is 4.7*10 7 In Europe, the bending strength is 130MPa, the compressive strength is 136MPa, the parallel layer breakdown voltage is 53KV, and the heat resistance temperature is 195 degrees, which is 8.3% higher than the tempera...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

PUM

PropertyMeasurementUnit
Insulation resistanceaaaaaaaaaa
Bending strengthaaaaaaaaaa
Insulation resistanceaaaaaaaaaa
Login to view more

Abstract

The invention discloses an insulating material, which belongs to the technical field of electric engineering. The insulating material is characterized by comprising, by weight, 20 to 28 parts of nanometer silica, 20 to 28 parts of polycarbonate resin, 1 to 3 parts of aluminum hydroxide, 10 to 20 parts of potter's clay, 80 to 100 parts of polyethylene, 1 to 5 parts of polyethylene glycol, 30 to 50 parts of silicone rubber, 2 to 5 parts of a vulcanizing agent, 4 to 8 parts of a diluent, 2 to 5 parts of fumed silica, 20 to 40 parts of a fire retardant, 20 to 40 parts of quartz powder, 4 to 8 parts of silicone oil, 54 to 72 parts of polyether-ether-ketone resin, 10 to 17 parts of talcum powder, 13 to 20 parts of light calcium carbonate, 9 to 18 parts of lubricant, 8 to 16 parts of anti-oxidant and 10 to 16 parts of calcined mica.

Description

technical field [0001] The invention relates to a material, in particular to an insulating material. Background technique [0002] With the rapid development of the national economy, people's electricity consumption has risen sharply, and the power system is also constantly developing and improving, so the requirements for power quality are getting higher and higher. In order to stabilize voltage fluctuations caused by unbalanced power generation and power consumption and ensure voltage quality, on-load tap changers are used in modern transformer equipment to regulate system voltage. [0003] The insulating material coated on the wall of the oil drum of the on-load tap-changer not only needs to be insulated, but also needs to be moisture-proof, anti-corrosion, and high-temperature resistant. At present, although there are many types of surface insulation materials on the market, their performance is relatively single, and their uses are highly targeted. They cannot meet the...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

Application Information

Patent Timeline
no application Login to view more
IPC IPC(8): C08L23/06C08L61/06C08L83/04C08L69/00C08L71/08C08K13/02C08K3/36C08K3/22C08K3/34C08K3/26
CPCC08L23/06C08K2201/011C08K2201/014C08L2201/08C08L2205/025C08L2205/035C08L61/06C08L83/04C08L69/00C08L71/02C08K13/02C08K3/36C08K2003/2227C08K3/346C08K3/34C08K2003/265
Inventor 李雄斌
Owner CHONGQING YANGDI ELECTROMECHANICAL
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Try Eureka
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap