Preparation method of aluminum base graphene alloy

A technology of aluminum-based olefin and aluminum alloy, applied in the field of preparation of aluminum-based olefinic alloy, can solve the problems of affecting the performance of olefinic alloy, difficult to mass-produce, small size of graphene, etc., and achieves good performance, excellent engineering application prospects, The effect of high production efficiency

Inactive Publication Date: 2015-11-18
AVIC BEIJING INST OF AERONAUTICAL MATERIALS
View PDF4 Cites 35 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

[0006] However, graphene has the problems of small size, large specific surface area, difficulty in dispersing, and easy agglomeration, which seriously affects the performance of graphene alloys.
At present, the process of graphene-reinforced metal matrix composites has the problem of low output, and it is difficult to form large-scale production

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • Preparation method of aluminum base graphene alloy
  • Preparation method of aluminum base graphene alloy
  • Preparation method of aluminum base graphene alloy

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0044] Prepare aluminum-based graphene, the specific steps are as follows:

[0045] a) Prepare graphene and aluminum mixed powder, the powder includes: graphene 10g (prepared by Hummer's method), aluminum alloy powder 1kg; copper Cu: 3.8% ~ 4.9%; manganese Mn: 0.30% ~ 1.0%; magnesium Mg: 1.2%~1.8%; Chromium Cr≤0.10%; Zinc Zn≤0.25%; Aluminum Al: balance;

[0046] a-1) preparing graphene monodisperse solution;

[0047]a-1-1) configure organic solvent aqueous solution, the weight of organic solvent is 19 times of graphene, organic solvent is ethanol solution, the mass percentage of organic solvent in organic solvent aqueous solution is 80%;

[0048] a-1-2) Graphene is dissolved in the organic solvent aqueous solution;

[0049] a-1-3) putting the graphene organic solution prepared in step a-1-2) into an ultrasonic oscillator and stirring the solution for 2 hours;

[0050] a-2) adding QZr0.2 aluminum alloy powder to the graphene monodisperse solution obtained in step a-1), the p...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

PUM

PropertyMeasurementUnit
particle diameteraaaaaaaaaa
strengthaaaaaaaaaa
electron mobilityaaaaaaaaaa
Login to view more

Abstract

The invention provides a preparation method of aluminum base graphene alloy. The method comprises the following steps: preparing graphene and aluminum and / or aluminum alloy mixed powder, filling a jacket with the mixed powder, carrying out vacuum degassing, carrying out hot isostatic pressing, re-melting, and homogenizing. A certain amount of the aluminum base graphene alloy precast ingots are re-melted in aluminum alloy melt, the content of graphene in a composite material can be well controlled through calculating, and graphene cannot float, so the content of graphene in the aluminum base graphene alloy can be accurately controlled; and the preparation method is provided on the basis of semi-continuous melting casting, and has the advantages of simple operation, high production efficiency, low preparation cost, and easy realization of large scale industrialization.

Description

technical field [0001] The invention relates to a preparation method of an olefin alloy, in particular to a preparation method of an aluminum-based olefin alloy. Background technique [0002] Graphene is a new type of two-dimensional nanomaterial. Its nanosheet is a two-dimensional material with a single atomic layer thickness composed of sp2 hybridized carbon atoms. It is the thinnest and hardest nanomaterial known in the world, with a strength as high as 1.01Tpa. , is 100 times that of structural steel, but its density is 1 / 5 of that of structural steel. The thermal conductivity is as high as 5300W / m·K, which is higher than that of carbon nanotubes and diamonds. The electron mobility at room temperature exceeds 200,000cm2 / V·S, which is higher than that of carbon nanotubes or silicon crystals. The resistivity is only about 1Ω·m, which is higher than that of aluminum or silver. Lower, the material with the smallest resistivity in the world. [0003] Graphene is a nano-scal...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

Application Information

Patent Timeline
no application Login to view more
Patent Type & Authority Applications(China)
IPC IPC(8): C22C1/10C22C1/02C22C1/05C22C21/00C22F1/04
Inventor 燕绍九洪起虎杨程陈翔戴圣龙
Owner AVIC BEIJING INST OF AERONAUTICAL MATERIALS
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Try Eureka
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap