Anti-tear compression-resisting cable sheath material for coal mine
A cable sheath, anti-tearing technology, applied in the direction of insulating cables, cables, circuits, etc., to achieve the effect of reducing production costs, production costs, and electrical performance
- Summary
- Abstract
- Description
- Claims
- Application Information
AI Technical Summary
Problems solved by technology
Method used
Examples
Example Embodiment
[0010] Example 1
[0011] A tear-resistant and compression-resistant cable sheath material for coal mines, comprising: first weighing 50 parts by weight of EPDM, 89wt% ethylene-butene elastomer based on EPDM, and ternary Ethylene-propylene rubber is based on 4wt% chlorinated polyethylene as the base material and plasticized for 4 minutes; then add 32 parts of carbon black N330, 12 parts of nano silica, 2 parts of active zinc oxide, 1.2 parts of silane coupling agent, 2 parts of antioxidant 4,4-bis(2,2-dimethylbenzyl)diphenylamine, 2 parts stearic acid, 18 parts paraffin oil, 13 parts microcrystalline paraffin, 0.8 parts accelerator M, 1.2 parts accelerator TMTD and base The material is based on the 3.5wt% flame-retardant system and the mixture is uniformly mixed and discharged. The mixing temperature is 120°C. The flame retardant is composed of 5 parts of microencapsulated red phosphorus, 23 parts of magnesium hydroxide, and 12 parts of two Antimony and 16 parts of active kaolin...
Example Embodiment
[0012] Example 2
[0013] A tear-resistant and compression-resistant cable sheath material for coal mines, comprising: first weighing 54 parts by weight of EPDM, 82wt% ethylene-butene elastomer based on EPDM, and ternary Ethylene-propylene rubber is based on 4.5wt% chlorinated polyethylene as the base material for plasticizing for 2 minutes; then 38 parts of carbon black N330, 7 parts of nano silica, 3.5 parts of active zinc oxide, 1 part of silane coupling agent, 2.4 parts of anti-aging Agent 4,4-bis(2,2-dimethylbenzyl)diphenylamine, 1.2 parts stearic acid, 22 parts paraffin oil, 12 parts microcrystalline paraffin, 1 part accelerator M, 1 part accelerator TMTD, and The base material is based on the 3.8wt% flame retardant system after mixing uniformly, and the mixing temperature is 115℃. The flame retardant is composed of 7.8 parts by weight of microencapsulated red phosphorus, 15 parts of magnesium hydroxide, and 13 parts of trioxide. Antimony and 13 parts of active kaolin; the...
Example Embodiment
[0014] Example 3
[0015] A tear-resistant and compression-resistant cable sheath material for coal mines, comprising: first weighing 53 parts by weight of EPDM, 85wt% ethylene-butene elastomer based on EPDM, and ternary Ethylene-propylene rubber is based on 4.3t% chlorinated polyethylene as the base material for 3min mastication, the Mooney viscosity of ethylene-butene elastomer (ML121℃, 1+4) is 12.85, and the ethylene content is 68.45wt%; then 33 parts of carbon are added Black N330, 12 parts of nano silica, 2.8 parts of active zinc oxide, 1.25 parts of silane coupling agent, 2.1 parts of antioxidant 4,4-bis(2,2-dimethylbenzyl)diphenylamine, 1.5 parts of stearin Acid, 21 parts of paraffin oil, 12 parts of microcrystalline paraffin, 0.85 parts of accelerator M, 1.05 parts of accelerator TMTD, and 3.75 wt% flame retardant system based on the base material are uniformly mixed and discharged. The mixing temperature is 120°C, Among them, the flame retardant is composed of 7 parts o...
PUM
Abstract
Description
Claims
Application Information
- R&D Engineer
- R&D Manager
- IP Professional
- Industry Leading Data Capabilities
- Powerful AI technology
- Patent DNA Extraction
Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic.
© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap