Heating device capable of simultaneously heating from bottom part and lateral parts and heating method

A heating device and side technology, applied in the direction of electric heating devices, ohmic resistance heating, heating element materials, etc., can solve the problems of sticky pot, high cost, complicated operation, etc., achieve enhanced stability and durability, and increase infrared emissivity , The effect of increasing the heating speed

Inactive Publication Date: 2015-12-09
CHENGDU LONGXIN TECH CO LTD
View PDF7 Cites 1 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

This variable power heating method has disadvantages such as high cost, complicated operation, and difficult control. It is difficult to achieve uniform heating of the heating substrate and constant temperature. The local paste pot, raw food, etc. caused by

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • Heating device capable of simultaneously heating from bottom part and lateral parts and heating method
  • Heating device capable of simultaneously heating from bottom part and lateral parts and heating method
  • Heating device capable of simultaneously heating from bottom part and lateral parts and heating method

Examples

Experimental program
Comparison scheme
Effect test

Embodiment

[0081] like figure 1 As shown, a heating device for simultaneously heating the bottom and the side, comprising a cylindrical base 1 with an upper opening, the base 1 includes a cylindrical side wall 2 and a bottom plate arranged at the bottom of the cylindrical side wall 2 3. The outer surface of the side wall 2 and the lower surface of the bottom plate 3 are provided with an electrothermal film 4, and the electrothermal film 4 is made of the following components by weight:

[0082] Tin tetrachloride 30~50,

[0083] Titanium trichloride 0.8~1.2,

[0084] Antimony trichloride 12~18,

[0085] Calcium dichloride 1.5~2.5,

[0086] Chromium trioxide 0.8~1.2,

[0087] Manganese dioxide 0.8~1.2,

[0088] Nickel trioxide 0.8~1.2,

[0089] Isopropanol 8~12,

[0090] Ethanol 3~5,

[0091] Water 20~30;

[0092] The stability of the electric heating film 4 is improved by adding antimony, the temperature resistance of the electric heating film 4 is improved by adding titanium, the...

example 1

[0103] The electrothermal film 4 is made of the following components by weight:

[0104] Tin tetrachloride 40, titanium trichloride 1, antimony trichloride 15, calcium dichloride 2, chromium trioxide 1, manganese dioxide 1, nickel trioxide 1, isopropanol 10, ethanol 4, water 25;

[0105] Its preparation method is:

[0106] S1. Weigh each component according to the above weight ratio, mix the weighed components, and continue to stir until all the solids are dissolved and the components are mixed evenly to obtain the electrothermal film treatment solution;

[0107] S2. Transport the substrate 1 into the heating chamber, the temperature in the heating chamber is controlled at 600°C, after the substrate 1 is heated to 600°C, atomize the electrothermal film treatment liquid through the spray gun and spray it on the outside of the side wall 2 of the substrate 1 respectively The surface and the lower surface of the bottom plate 3 form an electrothermal film semi-finished product, a...

example 2

[0111] The electrothermal film 4 is made of the following components by weight:

[0112] Tin tetrachloride 30, titanium trichloride 1.2, antimony trichloride 12, calcium dichloride 1.5, chromium trioxide 1.2, manganese dioxide 0.8, nickel trioxide 1.2, isopropanol 8, ethanol 5, water 20;

[0113] Its preparation method is:

[0114] S1. Weigh each component according to the above weight ratio, mix the weighed components, and continue to stir until all the solids are dissolved and the components are mixed evenly to obtain the electrothermal film treatment solution;

[0115] S2. Transport the substrate 1 to the heating chamber, the temperature in the heating chamber is controlled at 400°C, after heating the substrate 1 to 400°C, atomize the electrothermal film treatment liquid through the spray gun and spray it on the outside of the side wall 2 of the substrate 1 respectively The surface and the lower surface of the bottom plate 3 form an electrothermal film semi-finished produ...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

PUM

No PUM Login to view more

Abstract

The invention discloses a heating device capable of simultaneously heating from a bottom part and lateral parts. The heating device comprises a base body (1), wherein the base body (1) comprises a cylindrical lateral wall (2) and a bottom plate (3), wherein electrothermal films (4) are arranged on the outer surface of the lateral wall (2) and the lower surface of the bottom plate (3); each electrothermal film is prepared from the following components: stannic chloride, titanium trichloride, antimony trichloride, calcium dichloride, dichromium trioxide, manganese dioxide, nickel sesquioxide, isopropyl alcohol, ethanol and 20-30 parts of water; the components are mixed to prepare electrothermal film treating liquid; and the electrothermal film treating liquid is sprayed on the surface of the heated base body, and is annealed and processed into an electrode to obtain an electrothermal film product. The invention further discloses a heating method of the device. The heating device has the beneficial effects that the heating device is not easy to fall off; the upper temperature limit of the electrothermal film is improved; the heating base body rapidly heats; the highest surface working temperature can reach 800-1,000 DEG C; the highest power density can reach 40W/cm<2>; and the service life is greater than 30,000 hours.

Description

technical field [0001] The invention relates to the technical field of electrothermal film heating devices, in particular to a heating device and a heating method for simultaneously heating a bottom and a side. Background technique [0002] Most of the electric heating film in the prior art has the surface temperature of the electric heating film is too low, it is difficult to realize the electric heating film technology in the high temperature stage, and it is only suitable for the working conditions of low temperature and slow heating; moreover, its heating performance is unstable, and it can be used for a long time. During the working process of time use, the heating power is easy to attenuate; the adhesion between the electric heating film and the substrate is poor, it is easy to fall off, and the actual service life is short. [0003] In addition, the electric heating film variable power heating technology in the prior art, such as a multi-power energy-saving electric h...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

Application Information

Patent Timeline
no application Login to view more
Patent Type & Authority Applications(China)
IPC IPC(8): H05B3/10H05B3/20
Inventor 颜彬蒲彦军徐甜章
Owner CHENGDU LONGXIN TECH CO LTD
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Try Eureka
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap