Releasing agent for casting

A technology of release agent and fluorosurfactant, which is applied in the direction of casting molding equipment, casting molds, casting mold components, etc., can solve the problems of non-compliance with environmental protection, poor safety, difficult processing, etc., and achieve the enhancement of self-supporting ability and production cost Low, the effect of improving the release effect

Inactive Publication Date: 2015-12-16
河北双球新材料科技有限公司
View PDF6 Cites 12 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

However, the product produces residual pollution on the surface of the product, which makes post-processing difficult, and is flammable and poor in safety; smoke is generated during use, and the environmental protection is not up to standard

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0035] A mold release agent for casting, consisting of the following components by mass percentage:

[0036] Borax 10%

[0037] Fumed silica 5%

[0038] Glass powder 27%

[0039] Anionic fluorosurfactant 13%

[0040] Polyvinyl alcohol 5%

[0041] Sodium dodecylbenzenesulfonate 20%,

[0042] The balance is methyl ethoxy silicone oil,

[0043] The particle diameter of described borax is 10um,

[0044] The particle size of the glass powder is 0.1um.

[0045] Implementation effect: It can be used normally for 4000h within the range of 530°C, without deterioration or failure.

Embodiment 2

[0047] A mold release agent for casting, consisting of the following components by mass percentage:

[0048] Borax 15%

[0049] Fumed silica 7%

[0050] Glass powder 20%

[0051] Anionic fluorosurfactant 9%

[0052] Polyvinyl alcohol 1%

[0053] Sodium dodecylbenzenesulfonate 7%

[0054] The balance is methyl trifluoropropyl silicone oil,

[0055] The particle diameter of described borax is 1mm,

[0056] The particle size of the glass powder is 50um.

[0057] Implementation effect: It can be used normally for 3900h within the range of 530°C, without deterioration or failure.

Embodiment 3

[0059] A mold release agent for casting, consisting of the following components by mass percentage:

[0060] Borax 12%

[0061] Fumed silica 6%

[0062] Glass powder 25%

[0063] Anionic fluorosurfactant 10%

[0064] Polyvinyl alcohol 3%

[0065] Sodium dodecylbenzenesulfonate 10%,

[0066] The balance is methyl vinyl silicone oil,

[0067] The particle diameter of described borax is 100um,

[0068] The particle size of the glass powder is 10um.

[0069] Implementation effect: It can be used normally for 3500h within the range of 540°C, without deterioration or failure.

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

PropertyMeasurementUnit
particle diameteraaaaaaaaaa
particle diameteraaaaaaaaaa
particle diameteraaaaaaaaaa
Login to View More

Abstract

The invention belongs to the field of hub machining, and particularly discloses a releasing agent for casting. The releasing agent is composed, by mass percent, 8%-17% of sodium borate, 5%-7% of silicon dioxide, 20%-35% of ground glass, 7%-19% of a fluorinated surfactant, 1%-5% of polyvinyl alcohol, 7%-20% of sodium dodecyl benzene sulfonate and the balance silicon oil. The aim of the releasing agent is achieved better, the preparing technology is simple, the mold releasing effect is good, the concrete surface is clean, the cost is low, operation is convenient, the releasing agent is nonflammable and does not pollute the environment, the rustproof effect on an aluminum alloy template and a steel template can be further played, and the self-curing capacity of the concrete surface is improved.

Description

technical field [0001] The invention belongs to the field of hub processing, in particular to a mold release agent for casting. Background technique [0002] Casting is one of the basic processes of the modern device manufacturing industry. It is a process in which metals are smelted into liquids that meet certain requirements and poured into molds. After cooling, solidification, and cleaning, castings with predetermined shapes, sizes, and properties are obtained. . Because the casting blank is almost formed, the purpose of free machining or a small amount of machining reduces the cost and reduces the production time to a certain extent. However, casting demoulding is an important step in the casting process, which is directly related to the quality of casting. Therefore, a mold release agent is commonly used in the casting process. A mold release agent is an interface coating used on the surface of two objects that are easy to adhere to each other. It can make the surface...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
Patent Type & Authority Applications(China)
IPC IPC(8): B22C3/00
Inventor 钱国东
Owner 河北双球新材料科技有限公司
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Patsnap Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Patsnap Eureka Blog
Learn More
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic, Popular Technical Reports.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap|About US| Contact US: help@patsnap.com