Composite for manufacturing yoga ball and preparation method of composite

A technology of composite materials and yoga balls, which is applied in the field of composite materials, can solve the problems of non-wear resistance, surface adhesion, and yoga ball odor, etc., and achieve the effect of long service life and excellent toughness

Inactive Publication Date: 2015-12-23
SUZHOU NETABHAPE COMPOSITE MATERIALS
View PDF3 Cites 17 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

[0004]Technical problem to be solved: Aiming at the shortcomings of the existing materials for making yoga balls, which have peculiar smell, are not wear-resistant, have surface adhesion, and do not have the effect of repelling mosquitoes and insects, this The invention provides a composite material for making yoga balls and its preparation method

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0020] A composite material for manufacturing a yoga ball, which contains the following components in parts by mass: 60 parts of TPE rubber particles, 10 parts of aramid fiber, 15 parts of mica powder, 2 parts of azodicarbonamide, diisopropyl peroxydicarbonate 1 part, 0.3 part of antimony oxide, 0.1 part of coumarone resin, 0.7 part of titanium dioxide, 0.1 part of ethylene-vinyl acetate copolymer, 1 part of masterbatch, 10 parts of lavender, and 10 parts of geranium.

[0021] A preparation method for making a composite material for a yoga ball, the steps of the preparation method are as follows:

[0022] Step 1: Grind lavender and geranium to 90 mesh respectively. After crushing, hot-dip and extract with pure water respectively. After hot-dip and extract, filter with filter cloth. The solvent flows out, and then mixed evenly to obtain the extract of traditional Chinese medicine, wherein the weight ratio of solid to liquid is 1:3, the extraction time is 2 hours, and the extrac...

Embodiment 2

[0027] A composite material for manufacturing a yoga ball, which contains the following components in parts by mass: 80 parts of TPE rubber particles, 25 parts of aramid fiber, 30 parts of mica powder, 9 parts of azodicarbonamide, diisopropyl peroxydicarbonate 5 parts, 0.8 parts of antimony oxide, 0.5 parts of coumarone resin, 2 parts of titanium dioxide, 0.5 parts of ethylene-vinyl acetate copolymer, 2.5 parts of masterbatch, 20 parts of lavender, and 20 parts of geranium.

[0028] A preparation method for making a composite material for a yoga ball, the steps of the preparation method are as follows:

[0029] Step 1: Grind lavender and geranium to 110 mesh respectively. After crushing, hot-dip and extract with pure water respectively. The solvent flows out, and then mixed evenly to obtain the extract of traditional Chinese medicine, wherein the weight ratio of solid to liquid is 1:3, the extraction time is 2 hours, and the extraction temperature is 70°C;

[0030] Step 2: Ad...

Embodiment 3

[0034] A composite material for making a yoga ball, which contains the following components in parts by mass: 75 parts of TPE rubber particles, 22 parts of aramid fiber, 25 parts of mica powder, 7 parts of azodicarbonamide, diisopropyl peroxydicarbonate 4 parts, 0.7 parts of antimony oxide, 0.4 parts of coumarone resin, 1.7 parts of titanium dioxide, 0.4 parts of ethylene-vinyl acetate copolymer, 2.2 parts of masterbatch, 18 parts of lavender, and 18 parts of geranium.

[0035] A preparation method for making a composite material for a yoga ball, the steps of the preparation method are as follows:

[0036] Step 1: Grind lavender and geranium to 100 mesh respectively. After crushing, hot-dip with pure water, filter with a filter cloth after hot-dip, collect the filtrate after filtration, and then vacuum-concentrate the filtrate to nothing. The solvent flows out, and then mixed evenly to obtain the extract of traditional Chinese medicine, wherein the weight ratio of solid to liq...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

No PUM Login to View More

Abstract

The invention relates to a composite for manufacturing a yoga ball and a preparation method of the composite. The composite is prepared from, by mass, 60-80 parts of TPE colloidal particles, 10-25 parts of aramid fibers, 15-30 parts of mica powder, 2-9 parts of azodicarbonamide, 1-5 parts of di-isopropyl peroxydicarbonate, 0.3-0.8 part of antimony oxide, 0.1-0.5 part of coumarone resin, 0.7-2 parts of titanium dioxide, 0.1-0.5 part of ethylene-vinyl acetate copolymer, 1-2.5 parts of color master batches, 10-20 parts of lavender and 10-20 parts of geranium. The composite has excellent toughness and elasticity, the yoga ball made of the composite is free of peculiar smell and wear resistant, the mosquito repelling and mothproof effects can be achieved in summer, the yoga ball is not prone to being stuck to the skin when a person sweats, and the service life is long.

Description

technical field [0001] The invention relates to the technical field of composite materials, in particular to a composite material for making yoga balls and a preparation method thereof. Background technique [0002] Yoga balls are also known as exercise balls or yoga exercise balls. The utility model is a ball game tool matched with sports and fitness. Most of the materials are made of soft PVC material. When the human body is in contact with it, the inflated fitness ball inside will evenly touch the contact parts of the human body to produce a massage effect, which is beneficial to promote blood circulation. The movement arrangement of the yoga ball is aimed at the main parts such as the abdomen, back, waist, etc. When practicing, it should be stretched and squeezed with slow and rhythmic breathing, so that the muscles can be effectively massaged, relaxed, and consume fat. A kind of ability to improve concentration, reduce mental stress, and enhance the endurance of limbs...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
IPC IPC(8): C08L101/00C08L77/10C08L23/08C08L45/02C08K13/02C08K3/34C08K5/14C08K3/22
Inventor 刘莉王爽邱晶
Owner SUZHOU NETABHAPE COMPOSITE MATERIALS
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Patsnap Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Patsnap Eureka Blog
Learn More
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic, Popular Technical Reports.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap|About US| Contact US: help@patsnap.com