A production process and technology of aluminum alloy, applied in the direction of manufacturing converters, etc., can solve the problems of aluminum not reaching the ideal, aluminum is not easy to add, easy to block the nozzle, etc., to achieve stable aluminum yield, high aluminum absorption rate, avoidance of low temperature effect

Active Publication Date: 2015-12-23
ZENITH STEEL GROUP CORP +1
View PDF2 Cites 24 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

[0003] Years of production practice at the site shows that when the aluminum content of conventional steel reaches above 0.025%, the nozzle is easy to be blocked during continuous casting, while the aluminum content of high aluminum alloy structural steel is about 40 times that of conventional cold heading steel, which is currently the most One of the steel types that are difficult to continuously cast, because aluminum is extremely easy to oxidize, has a low melting point (660°C), and a small specific gravity (2.68g/cm 3 ) and other characteristics, resulting in the difficulty of adding aluminum to high aluminum alloy structural steel during smelting, and the yield is very unstable; at the same time, during the production process of high aluminum alloy steel, silicon oxide in slag is easy to reduce, aluminum in molten steel is easy to oxidize, silicon 1. The aluminum composition fluctuates greatly, the composition control is more difficult, and the molten steel is prone to secondary oxidation, and some oxides fail to float up and stay in the molten steel, which will cause blockage of the nozzle and cause flocculation, which will affect the quality of continuous pouring and steel cause great harm
[000...

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • Efficient production process of high aluminum-alloy-content structure round steel
  • Efficient production process of high aluminum-alloy-content structure round steel

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0033] Embodiment 1 (stove number 715060232)

[0034] (1) Converter smelting process

[0035] Converter smelting adopts high-quality molten iron. Among them, the mass content requirements of components in molten iron entering the furnace are: Si: 0.43%, P: 0.091%, S: 0.014%, and the temperature of molten iron entering the furnace is T = 1315°C.

[0036] Converter smelting controls tapping end point [C]=0.25%, end point [P]=0.006%, tapping temperature is 1650°C, the tapping process adopts sliding plate slag blocking operation, tapping time is 4 minutes, tapping 1 / 4 of the time in sequence Add 100Kg of calcium carbide deoxidizer and 180Kg of aluminum block;

[0037] (2) LF refining process

[0038] The ladle of the LF refining furnace is covered to ensure that the LF refining furnace is well sealed, and the furnace is a reducing atmosphere. Refining adds 50kg of aluminum particles / furnace and 60kg of calcium carbide / furnace to deoxidize the steel slag interface. In the early a...

Embodiment 2

[0047] Embodiment 2 (stove number 715060233)

[0048] This furnace is a continuous pouring furnace, the temperature of the hanging bag after soft blowing is set to 1565°C, the degree of superheat is 38°C, the casting speed is 0.76m / min, and the rest of the operations are the same as in Example 1.

Embodiment 3

[0049] Embodiment 3 (stove number 715060234)

[0050] Requirements for the mass content of the components in the molten iron: Si: 0.46%, P: 0.089%, S: 0.015%, the temperature of the molten iron in the furnace is T = 1320°C, the furnace is continuous pouring, and the temperature of the hanging ladle after soft blowing is set to 1565°C, the degree of superheat is 38°C, the casting speed is 0.75m / min, and the other operations are the same as in Example 1.

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

PUM

PropertyMeasurementUnit
Melting pointaaaaaaaaaa
Depthaaaaaaaaaa
Login to view more

Abstract

The invention relates to a production method of round steel, in particular to an efficient production process of high aluminum-alloy-content structure round steel. Al accounts for 0.70-1.20% in the round steel by weight. The preparation method comprises the converter smelting process, the LF external refining process, the VD furnace vacuum refining process, the square bloom continuous casting process and the rolling process. The high aluminum-alloy-content structure round steel produced through the method is low in cost, high in purity and good in castability, the adsorption rate of aluminum can be higher than 95%, calcium treatment is not needed, sequence casting of 12-15 times can be achieved, the production efficiency is greatly improved, the surface quality of the round steel is high, and the technical problems of high aluminum-alloy-content structure round steel produced in the prior art that the continuous castability is poor, nodulation occurs easily, the adsorption rate of aluminum is low, the yield is unstable, the purity is low, the surface quality of the round steel is low and the quality is unstable are solved.

Description

technical field [0001] The invention relates to a steel production method, in particular to a high-efficiency production process for round steel with high aluminum alloy structure. Background technique [0002] The aluminum content of high aluminum alloy structural steel is extremely high, as high as 0.70-1.20%. It usually belongs to the category of aluminum-containing nitrided steel. After nitriding treatment, an aluminum nitride layer is formed in the nitrided layer of the steel. According to the dispersion of aluminum nitride Hardening can improve the surface hardness and strength of steel, so as to obtain hard, wear-resistant and corrosion-resistant properties. It is widely used in the aviation industry, conventional weapons and machinery manufacturing industries, such as tube blank engine gas steel sleeves, screw rods and sleeves of injection molding machines. Parts with special requirements such as barrels. The domestic and foreign annual demand of the injection moldi...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

Application Information

Patent Timeline
no application Login to view more
IPC IPC(8): C21C5/28C21C7/06C21C7/10B22D11/111C21D8/00
Inventor 豆乃远万文华刘宪民王日红
Owner ZENITH STEEL GROUP CORP
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Try Eureka
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap