A technology for hot work die steel and thermal fatigue resistance, which is applied in the field of thermal fatigue resistance and high performance hot work die steel and its manufacturing process. problem, to achieve the effect of excellent hardenability

Inactive Publication Date: 2016-01-27
RUGAO HONGMAO HEAVY FORGING
View PDF5 Cites 19 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

This manufacturing process has the following problems: 1) The size of the electroslag ingot is small, and the small ingot size reduces the yield and manufacturing capacity of the product; 2) The original structure of the electroslag ingot has a large number of large particles or large blocks of liquefied carbo

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • Thermal fatigue resisting and high performance hot working die steel and manufacturing process thereof
  • Thermal fatigue resisting and high performance hot working die steel and manufacturing process thereof
  • Thermal fatigue resisting and high performance hot working die steel and manufacturing process thereof

Examples

Experimental program
Comparison scheme
Effect test

Example Embodiment

[0049] Example 1

[0050] The matrix of thermal fatigue resistant high performance hot work die steel is composed of the following mass percentage components: C0.30%, Si0.30%, Mn0.60%, Cr4.00%, Mo1.80%, W0.70%, V0.50%, P0.003%, S0.01%, Nb0.12%; the rest is Fe.

[0051] A manufacturing process of thermal fatigue resistant high performance hot work die steel has the following steps:

[0052] Step A. Smelting: smelt in an electric arc furnace according to the above-mentioned composition. The smelting temperature is greater than 1500℃, and cast into Ф400mm~Ф450mm steel ingots and air-cooled; the cast steel ingots are placed as consumable electrodes in the electroslag remelting device During electroslag remelting, the slagging voltage is 56~62V, the current is 3000~5000A, the electrical system voltage is 57~59V, the current is 11000~12000A, the capping voltage is 57~59V, and the electroslag is remelted to 1000Kg for 35~50 minutes. ~15000Kg steel ingot;

[0053] Step B. High temperature d...

Example Embodiment

[0059] Example 2

[0060] Thermal fatigue resistant high performance hot work die steel matrix is ​​composed of the following components by mass percentage: C0.25%, Si0.35%, Mn0.70%, Cr4.00%, Mo1.80%, W0.60%, V0.40%, P0.01%, S0.003%, Nb0.10%; the rest is Fe.

[0061] A manufacturing process of thermal fatigue resistant high performance hot work die steel has the following steps:

[0062] Step A. Smelting: smelt in an electric arc furnace according to the above-mentioned composition. The smelting temperature is greater than 1500°C, cast into a Ф400mm~Ф450mm steel ingot and air-cooled; the cast steel ingot is placed as a consumable electrode in the electroslag remelting device During electroslag remelting, the slagging voltage is 56~62V, the current is 3000~5000A, the electrical system voltage is 57~59V, the current is 11000~12000A, the capping voltage is 57~59V, and the electroslag is remelted to 1000Kg. ~15000Kg steel ingot;

[0063] Step B. High temperature diffusion heat treatment...

Example Embodiment

[0069] Example 3

[0070] Thermal fatigue resistant high performance hot work die steel matrix is ​​composed of the following components by mass percentage: C0.15%, Si0.32%, Mn0.50%, Cr4.00%, Mo1.50%, W0.50%, V0.60%, P0.01%, S0.01%, Nb0.10%; the rest is Fe.

[0071] A manufacturing process of thermal fatigue resistant high performance hot work die steel has the following steps:

[0072] Step A. Smelting: smelt in an electric arc furnace according to the above-mentioned composition. The smelting temperature is greater than 1500°C, and cast into a Ф400mm~Ф450mm steel ingot and air-cooled; the cast steel ingot is placed as a consumable electrode in the electroslag remelting device During electroslag remelting, the slagging voltage is 56~62V, the current is 3000~5000A, the electrical system voltage is 57~59V, the current is 11000~12000A, the capping voltage is 57~59V, and the electroslag is remelted to 1000Kg. ~15000Kg steel ingot;

[0073] Step B. High temperature diffusion heat treatm...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

PUM

PropertyMeasurementUnit
Phase transition pointaaaaaaaaaa
Login to view more

Abstract

The invention relates to thermal fatigue resisting and high performance hot working die steel and a manufacturing process thereof and belongs to the technical field of alloy steel manufacturing processes. A base body of the thermal fatigue resisting and high performance hot working die steel is composed of, by mass, 0.15-0.30% of C, 0.00-0.40% of Si, 0.30-1.00% of Mn, 3.50-4.50% of Cr, 1.50-2.00% of Mo, 0.20-1.00% of W, 0.40-0.80% of V, 0.00-0.02% of P, 0.00-0.02% of S, 0.00-0.15% of Nb and the balance Fe. The manufacturing process of the thermal fatigue resisting and high performance hot working die steel comprises the steps that burdening, smelting, casting, then electroslag remelting, high temperature heat diffusion heat treatment, then multidirectional forging heat machining and post-forging control cooling are conducted; secondary carbide refining heat treatment and isothermal annealing processing are conducted; finally, quenching and tempering heat processing are conducted, the steel is heated to be 950-1100 DEG C for austenitizing, and two to three times of tempering are conducted at the temperature of 540-630 DEG C after oil cooling or mist cooling. The hot working die steel has high thermal fatigue resistance, high thermal stability and high toughness.

Description

technical field [0001] The invention relates to a die steel and its manufacturing process, in particular to a thermal fatigue-resistant high-performance hot work die steel and its manufacturing process. The die steel makes full use of the alloying characteristics of Cr-Mo-W-V-Nb multi-alloy elements , to ensure high hardenability, high temperature thermal stability and thermal fatigue performance of the steel, not only can make the steel use temperature above 600 ℃, but also have higher thermal stability, good toughness and thermal fatigue performance than H13 steel, which belongs to Alloy steel technology field. Background technique [0002] Hot work die steel is a die steel used at higher temperatures (generally higher than 500 ° C), in which the alloying elements that play high temperature thermal strength and thermal stability are usually Cr, Mo, V and other alloying elements, so the current Some of the research work is mainly on the adjustment of these alloying element...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

Application Information

Patent Timeline
no application Login to view more
IPC IPC(8): C22C38/26C22C33/04
Inventor 周青春徐卫明顾金才葛建辉钱强赵博伟丁勇王小飞任志强
Owner RUGAO HONGMAO HEAVY FORGING
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Try Eureka
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap