Novel artificial carbonized wood production method

A production method and technology of artificial charcoal, which is applied in the direction of manufacturing tools, charcoal burning/combustion, wood processing appliances, etc., can solve the problems of flame retardancy and poor waterproof performance, and achieve improved waterproof performance, good heat resistance, and improved water resistance. The effect of weathering ability

Inactive Publication Date: 2016-02-03
黄万忠
View PDF12 Cites 1 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

[0006] Aiming at the above-mentioned technical problems of artificial carbonized wood with poor flame retardancy and poor waterproof performance in the prior art, the technical problem to be solved by the present invention is to propose a novel artificial carbonized wood production method with good flame retardancy and waterproof performance and environmental protection

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0033] A novel artificial carbonized wood production method, the steps are as follows:

[0034] 1. Selection: SiO of silica sol 2 The content is 40%, the particle size range is 30-70nm; the modulus of sodium silicate is 2.4; the particle size range of nano titanium dioxide powder is 20-80nm.

[0035] 2. Raw material processing

[0036] a) Crushing process: pine wood waste (shavings, sawn wood, wood chips, etc.) is roughly processed into 25 purpose coarse pine wood powder with a pulverizer, and then pulverized with a fine pulverizer to obtain 160 purpose fine pine wood powder;

[0037] b) Centrifugal filtration: under the state of stirring, dissolve fine pine wood powder in the sodium chloride solution, after the fine pine wood powder is fully dissolved, then the mixture is centrifuged, filtered, and dried, and repeated 3 times to obtain a purity rate of 93 % fine pine wood flour;

[0038]c) Proportion stirring: according to the ratio by weight: pure fine pine wood powder: s...

Embodiment 2

[0049] A novel artificial carbonized wood production method, the steps are as follows:

[0050] 1. Selection: SiO of silica sol 2 The content is 30%, the particle size range is 20-80nm; the modulus of sodium silicate is 2.2; the particle size range of nano titanium dioxide powder is 1-100nm.

[0051] 2. Raw material processing

[0052] a) Crushing process: pine wood waste (shavings, sawn wood, wood chips, etc.) is roughly processed into 20 purpose coarse pine wood powder with a pulverizer, and then pulverized with a fine pulverizer to obtain 150 purpose fine pine wood powder;

[0053] b) Centrifugal filtration: under the state of stirring, dissolve fine pine wood powder in sodium chloride solution, after fine pine wood powder is fully dissolved, then the mixture is centrifuged, filtered, and dried, and repeated 3 times to obtain a purity rate of 93.5 % fine pine wood flour;

[0054] c) Proportion stirring: according to the ratio by weight: pure fine pine wood powder: sodium...

Embodiment 3

[0065] A novel artificial carbonized wood production method, the steps are as follows:

[0066] 1. Selection: SiO of silica sol 2 The content is 50%, the particle size range is 25-75nm; the modulus of sodium silicate is 2.6; the particle size range of nano titanium dioxide powder is 10-90nm.

[0067] 2. Raw material processing

[0068] a) Crushing process: pine wood waste (shavings, sawn wood, wood chips, etc.) is roughly processed into 30 purpose coarse pine wood powder with a pulverizer, and then pulverized with a fine pulverizer to obtain 170 purpose fine pine wood powder;

[0069] b) Centrifugal filtration: Dissolve the fine pine wood powder in the sodium chloride solution while stirring, and after the fine pine wood powder is fully dissolved, the mixture is centrifuged, filtered, and dried, and repeated 3 times to obtain a purity rate of 93.8 % fine pine wood flour;

[0070] c) Proportion stirring: according to the ratio by weight: pure fine pine wood powder: sodium si...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

PUM

PropertyMeasurementUnit
particle diameteraaaaaaaaaa
particle diameteraaaaaaaaaa
particle diameteraaaaaaaaaa
Login to view more

Abstract

The invention discloses a novel artificial carbonized wood production method. The novel artificial carbonized wood production method includes the four steps of raw material processing, hot-pressing forming, carbonizing and surface processing. In the matching and stirring step in raw material processing, a mixture prepared from, by weight, pure fine pine powder, a sodium silicate solution, silica soil, nanometer titanium dioxide powder and sodium lignosulfonate according to the ratio of 6-8 to 2-4 to 0.3-0.5 to 0.1-0.3 to 0.05-0.07 is evenly stirred under the heated state so as to obtain a blank with the moisture content of 8-12%, the stirring speed is 200-250 r/min, and the stirring time is 15-20 min. Artificial carbonized wood has the beneficial effects of being good in flame-retardant performance and waterproof performance and environment-friendly, is suitable for various fields and is particularly suitable for the working environment where the artificial carbonized wood makes contact with water for a long time. Therefore, the artificial carbonized wood is a wood material having good application prospects.

Description

technical field [0001] The invention relates to a novel artificial carbonized wood production method, which belongs to the technical field of wood material production. Background technique [0002] Wood is an anisotropic porous material, which not only has the characteristics of sound insulation, heat insulation, good elasticity and high strength-to-weight ratio, but also has good tactile and visual effects. Therefore, wood is often used as sound insulation materials, building construction materials and wood products. With the rapid development of economic construction and the remarkable improvement of people's living standards, people's demand for wood is increasing day by day. Although wood is a renewable resource, the speed of supply is far slower than the speed of demand, which has led to an increasingly tense contradiction between wood supply and demand. In order to alleviate the tense situation of wood, people have adopted wood-based panel measures. [0003] Wood-ba...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

Application Information

Patent Timeline
no application Login to view more
Patent Type & Authority Applications(China)
IPC IPC(8): B27M1/06B27M1/08B27N3/08
Inventor 黄万忠
Owner 黄万忠
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Try Eureka
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap