Looking for breakthrough ideas for innovation challenges? Try Patsnap Eureka!

Steel slag vegetation concrete

A technology of planting concrete and steel slag, applied in the field of ecological concrete, can solve the problems of complex process, high cost, and reduction, and achieve the effects of reducing production cost, good compressive strength, and improving landscape

Active Publication Date: 2016-02-03
宝武环科武汉金属资源有限责任公司
View PDF4 Cites 16 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

[0005] However, in the existing technology, acidic soil and the addition of weakly acidic substances are used to neutralize the dissolved alkali to reduce the alkalinity value in the pores. Although the alkalinity of the pores of porous concrete can be reduced to a certain extent, its dosage has no effect on the strength. The reduction effect is obvious, FeSO 4 The amount of acidic substances should not be too much
The pH value of the pore water environment of ecological concrete treated with wax sealing is only reduced by 0.5-1, and the overall process is complicated and the cost is high, and the industrialization prospect is not optimistic

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0023] A kind of steel slag planting concrete, its raw material comprises steel slag aggregate, composite steel slag powder, strengthening agent, coloring agent, and the ratio of each raw material is counted as: steel slag aggregate 75%, composite steel slag powder 24%, strengthening agent 0.5%, Iron oxide red 0.5%, wherein, the fineness standard of described composite steel slag powder is that specific surface area is 320m 2 / kg, the composite steel slag powder comprises 30% steel slag tailings powder, 20% cement clinker and 50% blast furnace granulated slag powder by mass ratio, and the specific composition of the reinforcing agent is 1 part of manganese slag, 5 parts of Bayer red mud, 2 parts of fly ash, and 1 part of dihydrate gypsum.

[0024] The production method of the above-mentioned steel slag plant-grown concrete is as follows: the steel slag aggregate is uniformly mixed with composite steel slag powder, reinforcing agent, and colorant, and water is added according t...

Embodiment 2

[0036] A kind of steel slag planting concrete, its raw material comprises steel slag aggregate, composite steel slag powder, strengthening agent, coloring agent, and the ratio of each raw material is counted as: steel slag aggregate 83%, composite steel slag powder 15%, reinforcing agent 0.5%, Iron oxide yellow 1.5%, wherein, the fineness standard of described composite steel slag powder is that specific surface area is 350m 2 / kg, the composite steel slag powder comprises 32% steel slag tailings powder, 20% cement clinker and 48% blast furnace granulated slag powder by mass ratio, and the specific composition of the reinforcing agent is 2 parts manganese slag, Bayer 4 parts of red mud, 1 part of fly ash, 2 parts of industrial gypsum (desulfurization gypsum).

[0037] The production method of the above-mentioned steel slag planting concrete, the specific process is as follows: the steel slag aggregate is uniformly mixed with composite steel slag powder, reinforcing agent, and ...

Embodiment 3

[0043] A kind of steel slag planting concrete, its raw material comprises steel slag aggregate, composite steel slag powder, strengthening agent, coloring agent, and the ratio of each raw material is counted as: steel slag aggregate 82%, composite steel slag powder 15%, strengthening agent 1.5%, Iron oxide red 1.5%, wherein the fineness standard of the composite steel slag powder is that the specific surface area is greater than 380m 2 / kg, the composite steel slag powder is formed by mixing 35% steel slag tailings powder, 12% cement clinker and 53% blast furnace granulated slag powder according to the mass ratio, and the specific composition of the reinforcing agent is 4 parts of manganese slag, Bayer 3 parts of red mud, 2 parts of fly ash, 2 parts of dihydrate gypsum.

[0044] The production method of the above-mentioned steel slag planting concrete, the specific processing process is as follows: the steel slag aggregate is mixed with composite steel slag powder, reinforcing...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

PropertyMeasurementUnit
particle sizeaaaaaaaaaa
specific surface areaaaaaaaaaaa
specific surface areaaaaaaaaaaa
Login to View More

Abstract

The invention provides steel slag vegetation concrete, which is prepared from the following components in parts by weight: 75 to 83 parts of steel slag aggregate, 15 to 24.5 parts of composite steel slag powder and 0.5 to 2 parts of strengthening agent. A preparation method comprises the steps of uniformly stirring and mixing the steel slag aggregate and the composite steel slag powder as well as the strengthening agent proportionally, and adding water to produce the steel slag vegetation concrete. The steel slag vegetation concrete prepared by utilizing steel slag is high in strength, large in porosity and an acid-base environment can meet the requirement of growth of plants.

Description

technical field [0001] The invention belongs to the field of ecological concrete, and mainly relates to a steel slag planting concrete and a preparation method thereof. Background technique [0002] Under the concept of actively advocating green life, energy saving and environmental protection, our country is not only focusing on the structural performance of concrete in the past, but also gradually developing towards the direction of functional concrete such as environmental friendliness and resource conservation. Plant-growing concrete, which originated in Japan, not only has the function of concrete, but also has the function of environmental regulation, and realizes the needs of ecologicalization. Vegetative concrete is used on both sides of the city's roads, highway slope protection and central isolation belt, waterside slope protection, roof parking lot and other parts, which can increase the water permeability and air permeability of the surface of the concrete materi...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
Patent Type & Authority Applications(China)
IPC IPC(8): C04B28/14C04B18/14C04B38/08C04B111/40
CPCY02W30/91
Inventor 李灿华华洲连李晖刘思焦立新习嘉晨向晓东李军
Owner 宝武环科武汉金属资源有限责任公司
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Patsnap Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Patsnap Eureka Blog
Learn More
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic, Popular Technical Reports.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap|About US| Contact US: help@patsnap.com