Glass lining straight tube

A technology of glass-lined and straight pipes, which is applied in the field of glass-lined straight pipes, can solve the problems that the wear-resistant and corrosion-resistant properties of glass-lined straight pipes need to be improved, and achieve good wear-resistant and corrosion-resistant effects

Inactive Publication Date: 2016-02-24
常熟市联明化工设备有限公司
View PDF1 Cites 0 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

[0002] The wear-resistant and corrosion-resistant properties of glass-lined straight pipes need to be improved

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0014] A glass-lined straight pipe, characterized in that it comprises a metal body, the surface of the metal body is attached with a glass-lined bottom glaze, and the glass-lined bottom glaze consists of the following components in parts by weight:

[0015] 1-2 parts of zinc borate, 0.7 parts of barium petroleum sulfonate, 2.2 parts of high borate calcium borate, 1.7 parts of zinc oxide, 0.9 parts of sodium silicate, 1.3 parts of Glauber's salt, 1.6 parts of sodium fluorosilicate, 0.4 parts of nickel oxide, 1.3 parts Sodium Alkylbenzene Sulfonate.

Embodiment 2

[0017] A glass-lined straight pipe, characterized in that it comprises a metal body, the surface of the metal body is attached with a glass-lined bottom glaze, and the glass-lined bottom glaze consists of the following components in parts by weight:

[0018] 1 part of zinc borate, 0.7 parts of barium petroleum sulfonate, 2.2 parts of high borate calcium borate, 1.7 parts of zinc oxide, 0.9 parts of sodium silicate, 1.3 parts of Glauber's salt, 1.6 parts of sodium fluorosilicate, 0.4 parts of nickel oxide, 1.3 parts of alkyl Sodium benzenesulfonate.

Embodiment 3

[0020] A glass-lined straight pipe, characterized in that it comprises a metal body, the surface of the metal body is attached with a glass-lined bottom glaze, and the glass-lined bottom glaze consists of the following components in parts by weight:

[0021] 2 parts of zinc borate, 0.7 parts of barium petroleum sulfonate, 2.2 parts of high borate calcium borate, 1.7 parts of zinc oxide, 0.9 parts of sodium silicate, 1.3 parts of Glauber's salt, 1.6 parts of sodium fluorosilicate, 0.4 parts of nickel oxide, 1.3 parts of alkyl Sodium benzenesulfonate.

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

No PUM Login to View More

Abstract

The invention discloses a glass lining straight tube. The glass lining straight tube comprises a metal main body, wherein a glass lining ground coat is attached to the surface of the metal main body and comprises the following ingredients in parts by weight: 1-2 parts of zinc borate, 0.7 part of barium petroleum sulfonate, 2.2 parts of high-boron calcium borate, 1.7 parts of zinc oxide, 0.9 part of sodium silicate, 1.3 parts of mirabilite, 1.6 parts of sodium fluosilicate, 0.4 part of nickel oxide and 1.3 parts of sodium alkyl benzene sulfonate. As the glass lining ground coat is attached to the surface of the metal main body, the glass lining straight tube is excellent in wear and corrosion resistance.

Description

technical field [0001] The invention relates to glass-lined straight pipes. Background technique [0002] The wear and corrosion resistance of the glass-lined straight pipe needs to be improved. Contents of the invention [0003] The object of the present invention is to provide a glass-lined straight pipe, the metal body surface of which is attached with a glass-lined bottom glaze, which has good wear resistance and corrosion resistance. [0004] In order to achieve the above object, the technical solution of the present invention is to design a glass-lined straight pipe, which is characterized in that it comprises a metal body, and a glass-lined bottom glaze is attached to the surface of the metal body, and the glass-lined bottom glaze is composed of Composed of the following components: [0005] 1-2 parts of zinc borate, 0.7 parts of barium petroleum sulfonate, 2.2 parts of high borate calcium borate, 1.7 parts of zinc oxide, 0.9 parts of sodium silicate, 1.3 parts of...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
IPC IPC(8): C03C8/04
Inventor 高卫明
Owner 常熟市联明化工设备有限公司