Putty powder

A putty powder and powder technology, which is applied in the field of building decoration materials, can solve problems such as difficulty in meeting hardness requirements, human health hazards, poor crack resistance of putty, etc., and achieve good freeze-melt stability, good gloss, and interface adhesion Good results

Inactive Publication Date: 2016-02-24
许展
View PDF3 Cites 2 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

[0003] The anti-corrosion materials used in the existing putty mostly include volatile harmful substances such as formaldehyde, benzene, ammonia, etc., which are harmful to people's health
[0004] In addition, the existing putty tends to have high hardness and poor c...

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0029] A kind of putty powder, including 500kg heavy calcium carbonate, 120kg hydroxyapatite, 150kg diatom powder, 65kg asbestos fiber, 75kg plastic powder, 20kg starch ester, 45kg concrete interface agent, 12kg arrow grass, 30kg millennium health, 5kg small Wax tree, 20kg Oumian horse, 12kg fungus Artemisia annua and 5kg sage.

[0030] Among them, the hydroxyapatite, asbestos fiber, plastic powder and interface agent are crushed to a particle size of 5-8 microns by using a nano pulverizer; Giraffe is crushed to a particle size of 5-8 microns; and heavy calcium carbonate, diatom powder and starch ester are crushed to a particle size of 12-15 microns.

[0031] When preparing the putty powder of the present invention, each raw material is uniformly mixed after pulverization. When in use, add an appropriate amount of water and stir evenly until it becomes a slurry.

[0032] The bonding strength of the putty powder in this embodiment is 3.11Mpa, and the adhesion is uniform. Afte...

Embodiment 2

[0034] A kind of putty powder, including 400kg heavy calcium carbonate, 200kg hydroxyapatite, 100kg diatom powder, 100kg asbestos fiber, 50kg plastic powder, 30kg starch ester, 10kg concrete interface agent, 20kg arrow grass, 10kg millennium health, 8kg small Wax tree, 10kg Oumian horse, 20kg fungus Artemisia spp., and 2kg 菥蓂.

[0035] Among them, the hydroxyapatite, asbestos fiber, plastic powder and interface agent are crushed to a particle size of 5-8 microns by using a nano pulverizer; Grinding to a particle size of 5-8 microns; and crushing heavy calcium carbonate, diatom powder and starch ester to a particle size of 12-15 microns.

[0036] When preparing the putty powder of the present invention, each raw material is uniformly mixed after pulverization. When in use, add an appropriate amount of water and stir evenly until it becomes a slurry.

[0037] The bonding strength of the putty powder in this embodiment is 2.97Mpa, and the adhesion is even. After three years of ...

Embodiment 3

[0039] A kind of putty powder, including 600kg heavy calcium carbonate, 50kg hydroxyapatite, 200kg diatom powder, 30kg asbestos fiber, 100kg plastic powder, 10kg starch ester, 80kg concrete interface agent, 5kg arrow grass, 50kg millennium health, 2kg small Wax tree, 30kg Oumian horse, 5kg fungus Artemisia annua and 8kg sage.

[0040] Among them, the hydroxyapatite, asbestos fiber, plastic powder and interface agent are crushed to a particle size of 5-8 microns by using a nano pulverizer; Grinding to a particle size of 5-8 microns; and crushing heavy calcium carbonate, diatom powder and starch ester to a particle size of 12-15 microns.

[0041] When preparing the putty powder of the present invention, each raw material is uniformly mixed after pulverization. When in use, add an appropriate amount of water and stir evenly until it becomes a slurry.

[0042] The bonding strength of the putty powder in this embodiment is 2.91Mpa, and the adhesion is uniform. After three years o...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

PUM

PropertyMeasurementUnit
Bond strengthaaaaaaaaaa
Bond strengthaaaaaaaaaa
Bond strengthaaaaaaaaaa
Login to view more

Abstract

The invention discloses putty powder and belongs to the field of building decoration materials. The putty powder is prepared from 400-600 parts of ground limestone, 50-200 parts of hydroxyapatite, 100-200 parts of diatom powder, 30-100 parts of asbestos fiber, 50-100 parts of plastic powder, 10-30 parts of starch ester, 10-80 parts of a bonding agent, 5-20 parts of arrow grass, 10-50 parts of homalomena occulta, 2-8 parts of Ligustrum sinense, 10-30 parts of European pannum, 5-20 parts of tarragon and 2-8 parts of pennycress. Due to the hydroxyapatite, the crack resistance of the putty powder is improved, and meanwhile the hardness and glossiness of putty are improved; due to the fact that the diatom powder and asbestos fiber are porous materials, noise reduction can be achieved, and harmful gas in air can be absorbed; the plastic powder and the ground limestone are used as padding of the putty powder, so that the glossiness is good, and the putty is easier to form, good in forming performance and not prone to cracking.

Description

technical field [0001] The invention relates to the field of building decoration materials, in particular to a putty powder. Background technique [0002] Putty is a decorative material for leveling the surface of the wall. It is a thick paste paint and an indispensable product before the paint is painted. Applied on the primer or directly on the object to remove uneven defects on the surface of the object to be coated. It can fill the partially sunken working surface, or scrape off the entire surface. It is usually applied to the surface of the primer layer after the primer layer is completely dry. It is required to have good adhesion and no cracks during the baking process. [0003] Most of the anticorrosion materials used in the existing putty include formaldehyde, benzene, ammonia and other volatile harmful substances, which are harmful to people's health. [0004] In addition, the existing putty tends to have high hardness and poor crack resistance, and when the crac...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

Application Information

Patent Timeline
no application Login to view more
IPC IPC(8): C09D5/34C09D5/14
Inventor 许展
Owner 许展
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Try Eureka
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap