Reflective hot-melt marking paint composition

A technology of hot-melt marking paint and composition, applied in the field of paint, can solve the problems of slow traffic opening, slow drying, and no reminder for drivers, and achieve the effect of fast hot-melt speed and fast drying speed

Inactive Publication Date: 2016-02-24
WUHAN ZONGHENG TRAFFIC ENG CO LTD
View PDF3 Cites 10 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

The currently used traffic paint dries slowly during use, which makes traffic open slowly and affects traffic
And the traffic paint that is used at present is after the traffic mark is done, the driver will not produce strange feeling when the car travels to the mark, and the driver does not have a reminding effect.

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0021] The present embodiment provides a reflective hot-melt marking paint composition, by weight, the paint composition includes:

[0022] 200 parts of fine powder, 75 parts of coarse powder, 70 parts of C5 petroleum resin, 100 parts of quartz sand, 15 parts of titanium dioxide, 10 parts of polyethylene wax, 12 parts of plasticizer, 2 parts of leveling agent, 50 parts of glass beads, EVA8 Parts, wherein the particle size of the fine powder is 400 mesh, the particle size of the coarse powder is 100 mesh, and the particle size of the quartz sand is 80 mesh.

[0023] Both fine powder and coarse powder are calcium carbonate; the plasticizer is oily, which is dioctyl sebacate, dioctyl adipate, dinonyl phthalate, dioctyl terephthalate, phthalate One or more of dioctyl dicarboxylate and vegetable oil.

Embodiment 2

[0025] The present embodiment provides a reflective hot-melt marking paint composition, by weight, the paint composition includes:

[0026] 250 parts of fine powder, 70 parts of coarse powder, 65 parts of C5 petroleum resin, 105 parts of quartz sand, 16 parts of titanium dioxide, 12 parts of polyethylene wax, 13 parts of plasticizer, 1.8 parts of leveling agent, 60 parts of glass beads, EVA7 Parts, wherein the particle size of the fine powder is 400 mesh, the particle size of the coarse powder is 100 mesh, and the particle size of the quartz sand is 80 mesh.

[0027] Both fine powder and coarse powder are zeolites; plasticizers are oily, which are dioctyl sebacate, dioctyl adipate, dinonyl phthalate, dioctyl terephthalate, phthalate One or more of dioctyl formate and vegetable oil.

Embodiment 3

[0029] The present embodiment provides a reflective hot-melt marking paint composition, by weight, the paint composition includes:

[0030] 150 parts of fine powder, 80 parts of coarse powder, 75 parts of C5 petroleum resin, 95 parts of quartz sand, 18 parts of titanium dioxide, 9 parts of polyethylene wax, 10 parts of plasticizer, 2.4 parts of leveling agent, 45 parts of glass beads, EVA9 Parts, wherein the particle size of the fine powder is 400 mesh, the particle size of the coarse powder is 100 mesh, and the particle size of the quartz sand is 80 mesh.

[0031] Both fine powder and coarse powder are kaolin; the plasticizer is oily, which is dioctyl sebacate, dioctyl adipate, dinonyl phthalate, dioctyl terephthalate, phthalate One or more of dioctyl formate and vegetable oil.

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

PUM

PropertyMeasurementUnit
particle size (mesh)aaaaaaaaaa
particle size (mesh)aaaaaaaaaa
particle size (mesh)aaaaaaaaaa
Login to view more

Abstract

The invention relates to the technical field of paints, specifically to a reflective hot-melt marking paint composition. The paint composition comprises, by weight, 150 to 250 parts of fine powder, 67.5 to 82.5 parts of coarse powder, 63 to 77 parts of C5 petroleum resin, 92 to 108 parts of quartz sand, 12 to 18 parts of pigment, 8 to 12 parts of polyethylene wax, 10 to 15 parts of a plasticizer, 1.5 to 2.5 parts of a leveling agent, 40 to 60 parts of a glass bead and 7 to 9 parts of EVA. The reflective hot-melt marking paint composition contains the fine powder, the coarse powder and the glass bead; and through adjusting the proportion of each component of the marking paint composition, the marking paint composition is allowed to have the beneficial effects of a fast hot melting speed, a fast drying speed, wear resistance and crack resistance.

Description

technical field [0001] The invention relates to the technical field of coatings, in particular to a reflective hot-melt marking coating composition. Background technique [0002] Paint is a material that can be coated on the surface of an object by different construction techniques to form a solid film with firm adhesion, certain strength, and continuity. . At present, the application fields of coatings are very extensive, such as coatings for home decoration and coatings for traffic roads. In traffic coatings, it is mainly used for road marking. Currently used traffic paints dry slowly during use, which slows traffic opening and affects traffic. And the currently used traffic paint is used after the traffic marks are done, the driver will not feel strange when the car travels to the mark, and the driver does not have a reminding effect. [0003] In view of this, to overcome the above defects in the prior art and to provide a new reflective hot-melt marking paint composi...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

Application Information

Patent Timeline
no application Login to view more
Patent Type & Authority Applications(China)
IPC IPC(8): C09D157/02C09D123/06C09D123/08C09D5/22
Inventor 杨松林
Owner WUHAN ZONGHENG TRAFFIC ENG CO LTD
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Try Eureka
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap