Polishing liquid, preparation method and application

A polishing liquid and emulsion technology, which is applied to polishing compositions containing abrasives, etc., can solve the problems of slow production speed, poor friction resistance of waxed layers, and high cost of resin materials, achieve good wear resistance and weather resistance, and improve polishing brightness. , the preparation method is simple

Active Publication Date: 2016-03-09
GUANGZHOU GAOCHEN STONE TECH CO LTD
View PDF2 Cites 14 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

But after the material surface is waxed, the waxed layer is not resistant to friction, it is easy to fall off, and the surface effect of the material is not bright enough
The problems when using polishing fluid to treat the surface of marble or wood-based panels are as follows: (1) pads and steel wool need to be used at the same time to spread the polishing fluid on the surface of the material, and during use, the polishing cotton needs to be used frequently Replacement, not only waste of material, but also slow production
(2) Although steel wool is not required for some imported resin products, it needs more than 24 hours of drying and curing time before polishing, which greatly wastes production time, and the cost of resin materials is very high, which is caused by a long time The film is easy to yellow and difficult to repair after being scratched

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0041] A kind of polishing liquid, this polishing liquid comprises following component by mass percentage:

[0042] h 2 SO 4 : 0.8%;

[0043] Sodium oxalate: 0.2%;

[0044] Ethylene glycol: 0.3%;

[0045] Glycerin: 2%;

[0046] Zinc fluorosilicate: 10%;

[0047] Nano titanium dioxide: 2%;

[0048] Nano silica: 1%;

[0049] Coupling agent γ-(2,3-epoxypropoxy)propyltrimethoxysilane: 0.1%;

[0050] Palm wax emulsion with a solid content of 30%: 3.9%;

[0051] The balance is water.

[0052] The concrete preparation method of this polishing liquid is:

[0053] a) adding sulfuric acid to water to form an aqueous solution;

[0054] b) sodium oxalate, ethylene glycol and glycerin are added to the aqueous solution of step a), and stirred evenly;

[0055] c) adding zinc fluorosilicate, nano-titanium dioxide, nano-silicon dioxide, and coupling agent γ-(2,3-glycidoxy)propyltrimethoxysilane to the liquid obtained in step b), and stirring evenly;

[0056] d) Add the palm wax em...

Embodiment 2

[0059] A kind of polishing liquid, this polishing liquid comprises following component by mass percentage:

[0060] h 3 PO 4 : 0.5%;

[0061] Sodium oxalate: 2%;

[0062] Ethylene glycol: 0.8%;

[0063] Glycerin: 3%;

[0064] Magnesium fluorosilicate: 15%;

[0065] Nano titanium dioxide: 5%;

[0066] Nano silica: 5%;

[0067] Coupling agent γ-(2,3-epoxypropoxy)propyltrimethoxysilane: 0.5%;

[0068] Palm wax emulsion with a solid content of 30%: 11.8%;

[0069] The balance is water.

[0070] The concrete preparation method of this polishing liquid is:

[0071] a) adding phosphoric acid to water to form an aqueous solution;

[0072] b) sodium oxalate, ethylene glycol and glycerin are added to the aqueous solution of step a), and stirred evenly;

[0073] c) adding magnesium fluorosilicate, nano-titanium dioxide, nano-silicon dioxide, and coupling agent γ-(2,3-glycidoxy)propyltrimethoxysilane to the liquid obtained in step b), and stirring evenly;

[0074] d) Add the pa...

Embodiment 3

[0077] A kind of polishing liquid, this polishing liquid comprises following component by mass percentage:

[0078] Oxalic acid: 0.5%;

[0079] Sodium oxalate: 0.2%;

[0080] Ethylene glycol: 0.3%;

[0081] Glycerin: 2%;

[0082] Ammonium fluorosilicate: 10%;

[0083] Nano titanium dioxide: 2%;

[0084] Nano silica: 1%;

[0085] Coupling agent γ-(2,3-epoxypropoxy)propyltrimethoxysilane: 0.1%;

[0086] Palm wax emulsion with a solid content of 30%: 3.9%;

[0087] The balance is water.

[0088] The concrete preparation method of this polishing liquid is:

[0089] a) adding oxalic acid to water to form an aqueous solution;

[0090] b) sodium oxalate, ethylene glycol and glycerin are added to the aqueous solution of step a), and stirred evenly;

[0091] c) adding ammonium fluorosilicate, nano-titanium dioxide, nano-silicon dioxide, and coupling agent γ-(2,3-glycidoxy)propyltrimethoxysilane to the liquid obtained in step b), and stirring evenly;

[0092] d) Add the palm ...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

No PUM Login to View More

Abstract

The present invention belongs to the technical field of marble or wood-based panel surface brightening and protection treatments, in particular relating to polishing liquid, a preparation method and an application. The polishing liquid comprises a pH modifier, soluble oxalate, a lubricant, fluosilicate, nano titanium dioxide, nano silicon dioxide, a coupling agent, a palm wax emulsion and / or a paraffin emulsion and water. By applying the polishing liquid provided by the present invention to a marble or wood-based panel surface, under a series of physical and chemical actions, a thick layer of dense bright glassy substances can be generated on the surface; the bright glassy substances are hard, wear-resistant and weather-resistant, so that the 'water'-like bright mirror effect on a floor surface is achieved; and a surface scratch can be easily repaired. When the marble or wood-based panel surface is treated by the polishing liquid, the polishing liquid is only required to be poured onto the marble or wood-based panel, and is spread by a polishing pad. Polishing steel wire cotton is not needed; production efficiency is improved; cost is saved; and polishing brightness is improved.

Description

technical field [0001] The invention belongs to the technical field of surface enhancement and protective treatment of marble or wood-based panels, and in particular relates to a polishing liquid, a preparation method and an application. Background technique [0002] At present, the method for brightening the surface of materials such as marble or wood-based panels is generally to wax the surface of the material or use a polishing solution for surface treatment. But after the material surface is waxed, the waxed layer is not resistant to friction, it is easy to fall off, and the material surface effect is not bright enough. The problems when using polishing fluid to treat the surface of marble or wood-based panels are as follows: (1) pads and steel wool need to be used at the same time to spread the polishing fluid on the surface of the material, and during use, the polishing cotton needs to be used frequently Replacement, not only waste of material, but also slow productio...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
IPC IPC(8): C09G1/02B24B1/00
Inventor 刘祥刘永梅
Owner GUANGZHOU GAOCHEN STONE TECH CO LTD
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Patsnap Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Patsnap Eureka Blog
Learn More
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic, Popular Technical Reports.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap|About US| Contact US: help@patsnap.com