Sound insulation corrosion-resistant thermal insulation wallboard and manufacturing method therefor

A thermal insulation wallboard and corrosion-resistant technology, applied in the field of building thermal insulation materials, can solve the problems of fiber tensile strength decline, discontinuity, moisture absorption, etc., achieve the effects of reducing water absorption, low cost, and solving environmental pollution

Inactive Publication Date: 2016-03-16
冯丹
View PDF4 Cites 4 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

However, it also causes the disadvantages of moisture absorption and water seepage. On the one hand, the plant fibers will be depolymerized by microorganisms in a water-soaked environment, which will reduce the tensile strength of the fibers; A large number of monosaccharides, oligosaccharides, lignin, etc. are proposed to cause serious retardation of cement. Therefore, it is necessary to modify the existing plant fibers to waterproof and improve the structure of the board wall so that the bone is continuous when the finished product is finished. The discontinuous structure of most of the pores ensures the solidity, waterproof and air permeability of the wall

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Examples

Experimental program
Comparison scheme
Effect test

Embodiment Construction

[0012] A sound-proof, corrosion-resistant and thermal insulation wallboard, made of the following raw materials in parts by weight: cement 13, aluminum clay 37, medical stone 28, micron-sized hollow ceramic beads 20, wheat straw fiber 36, sodium citrate 1.3, asbestos Fiber 7, silicon nitride whisker 2, butyl acrylate 8, polyphenylene sulfide particles 13, iron sulfate 0.7, tea saponin 2.4, waterproofing agent 41, acetic acid 43; the waterproofing agent is made of the following raw materials in parts by weight : Epoxy resin emulsion 25, vinyl acetate 18, isocyanate 26, CSA expansion agent clinker 3, slag powder 4, dimethyl silicone oil 7, polyethylene wax 2, potassium chloride 0.2, sodium lignosulfonate 1.3, hard Calcium fatty acid 0.9, gelatin emulsion 11, the preparation method is: add vinyl acetate, dimethyl silicone oil and water to ultrasonic dispersion for 20-30 minutes, add sodium lignosulfonate, heat up to 50-70°C and stir at high speed for 10-20 minutes and Keep warm f...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

No PUM Login to View More

Abstract

The invention discloses a sound insulation corrosion-resistant thermal insulation wallboard and a manufacturing method therefor. On the one hand, wheat straw fibers are subjected to high temperature steam pretreatment, then part of pectin is removed, acetic acid is added, acetylation treatment is carried out, free hydroxide radicals in cellulose are enclosed, the hydrophobic performance and the thermal stability of the material are raised, then a waterproof agent immersion method is employed for processing, the material water absorption is lowered, the alkali corrosion resistance of the material in a cement-based material is raised and the capability of resisting microorganisms from depolymerization is raised. On the other hand, bauxite clay, Chinese medical stone and the like are modified, utilized, and blended with polyphenylene sulfide particles, granulation is carried out, the intensity and the toughness of the product are raised, the product is not easy to fracture, the thermal insulation wallboard prepared according to the method is low in cost, the added modified wheat straw fibers can absorb released energy when a cement-based material cracks, therefore extension of the crack in the cement-based material is stopped, namely, the toughness of the material is raised, the compression toughness index is raised, and the provided thermal insulation wallboard has characteristics of light weight, thermal insulation, sound insulation, corrosion resistance, convenient installation and the like.

Description

technical field [0001] The invention relates to the technical field of building thermal insulation materials, in particular to a sound-insulating, corrosion-resistant and thermal-insulation wallboard and a manufacturing method thereof. Background technique [0002] At present, external wall insulation is mainly used for external wall insulation in my country. Compared with internal insulation, it effectively reduces the "thermal bridge" of the building structure, increases the effective space of the building, eliminates condensation, and improves the comfort of living. Moreover, the external thermal insulation technology is not only applicable to new structural projects, but also to renovation projects of old buildings, with a wider scope of application and higher technical content. Currently used external wall insulation materials such as EPS, etc., whose raw materials come from petroleum. Under the environment of a sharp increase in the price of petroleum products, EPS / XPS...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
IPC IPC(8): C04B28/00C04B24/42C04B24/32C04B18/24C04B103/65C04B111/52C04B111/20
CPCY02W30/91
Inventor 冯丹
Owner 冯丹
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Eureka Blog
Learn More
PatSnap group products