High-performance non-sintered sliding plate joint material and preparation method thereof

A high-performance, joint material technology, applied in the field of high-temperature materials and metallurgy, can solve the problems of affecting production safety, difficult to dismantle, not resistant to erosion and erosion, etc., to improve construction performance, improve bonding performance, and increase density. Effect

Active Publication Date: 2016-05-04
HENAN XIBAO METALLURGICAL MATERIALS GROUP
View PDF2 Cites 7 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

The disadvantages of this kind of joint material are: it is easy to shrink and crack under the action of temperature; it is not resistant to the erosion and erosion of molten steel, and it is prone to steel penetration and leakage during use, which affects production safety, and the maintenance frequency is high during use. It affects the service life of the ladle; in addition, it is not easy to dismantle when replacing the nozzle block, and it cannot be replaced quickly, which increases the labor intensity of the operator and affects the construction efficiency

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • High-performance non-sintered sliding plate joint material and preparation method thereof

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0024] A high-performance non-sintered sliding board joint material comprises, in parts by weight: 40 parts of corundum, 6 parts of flake graphite, 1.5 parts of silane coupling agent, 15 parts of nano oxide powder and 6 parts of aggregate.

[0025] in:

[0026] Corundum includes fine corundum material and coarse corundum material, the weight ratio of fine corundum material and coarse corundum material is 1:1.2, the particle size of fine corundum material is 300~360 mesh, and the coarse corundum material includes 1mm<grain size≤3mm, 0.5mm<grain size ≤1mm and particle size ≤0.5mm three kinds of coarse granular materials, the weight ratio of the three kinds of coarse granular materials is 1:1.2:2;

[0027] Aggregate includes magnesium aluminum spinel, metal magnesium powder and metal aluminum powder, the weight ratio of magnesium aluminum spinel, metal magnesium powder and metal aluminum powder is 1.5:1:1, and the particle size of magnesium aluminum spinel is 10~ 12mm, the parti...

Embodiment 2

[0035] A high-performance non-sintered sliding board joint material comprises, in parts by weight: 65 parts of corundum, 12 parts of flake graphite, 3.0 parts of silane coupling agent, 15 parts of nano oxide powder and 10 parts of aggregate.

[0036] in:

[0037] Corundum includes fine corundum material and coarse corundum material, the weight ratio of fine corundum material and coarse corundum material is 1:1.2, the particle size of fine corundum material is 300~360 mesh, and the coarse corundum material includes 1mm<grain size≤3mm, 0.5mm<grain size ≤1mm and particle size ≤0.5mm three kinds of coarse granular materials, the weight ratio of the three kinds of coarse granular materials is 1:1.8:2;

[0038] Aggregate includes magnesium aluminum spinel, metal magnesium powder and metal aluminum powder, the weight ratio of magnesium aluminum spinel, metal magnesium powder and metal aluminum powder is 2.5:1:1, and the particle size of magnesium aluminum spinel is 10~ 12mm, the parti...

Embodiment 3

[0046] A high-performance joint material for non-sintered skateboards comprises, in parts by weight, 56 parts of corundum, 8 parts of flake graphite, 2.3 parts of silane coupling agent, 21 parts of nano oxide powder and 7 parts of aggregate.

[0047] in:

[0048] Corundum includes fine corundum material and coarse corundum material, the weight ratio of fine corundum material and coarse corundum material is 1:1.2, the particle size of fine corundum material is 300~360 mesh, and the coarse corundum material includes 1mm<grain size≤3mm, 0.5mm<grain size ≤1mm and particle size ≤0.5mm three kinds of coarse granular materials, the weight ratio of the three kinds of coarse granular materials is 1:1.5:2;

[0049] Aggregate includes magnesium aluminum spinel, metal magnesium powder and metal aluminum powder, the weight ratio of magnesium aluminum spinel, metal magnesium powder and metal aluminum powder is 2.1:1:1, and the particle size of magnesium aluminum spinel is 10~ 12mm, the par...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

PropertyMeasurementUnit
particle sizeaaaaaaaaaa
particle sizeaaaaaaaaaa
particle sizeaaaaaaaaaa
Login to View More

Abstract

The invention discloses a high-performance non-sintered sliding plate joint material and a preparation method thereof. The High-performance non-sintered sliding plate joint material is prepared from the following components in parts by weight: 40-65 parts of corundum, 6-12 parts of flake graphite, 1.2-3.8 parts of silane coupling agent, 15-28 parts of nano oxide powder, and 6-10 parts of aggregate. The preparation method of the high-performance non-sintered sliding plate joint material comprises the following steps: (1) dissolving the silane coupling agent in solvent water, carrying out ultrasonic treatment, adding to a high-speed dispersing machine together with the nano oxide powder, sufficiently stirring, filtering and standing in a sealing manner for later use; and (2) adding the corundum and the aggregate to the high-speed dispersing machine, stirring for mixing, adding the nano oxide powder treated in the step (1) and flake graphite to the high-speed dispersing machine, stirring for mixing and discharging. The high-performance non-sintered sliding plate joint material and the preparation method thereof have the advantages that the preparation process is simple, the product is high in volume density, low in porosity, and excellent in adhesion property, erosion resistance and mechanical property at a high temperature, and the bleeding and leaking phenomena are reduced.

Description

technical field [0001] The invention relates to the technical field of high-temperature materials and metallurgy, in particular to a high-performance non-sintered slide joint material and a preparation method thereof. Background technique [0002] With the development of the steelmaking industry, sliding nozzles have become one of the important innovative technologies in the steel industry. Now most of the ladles and tundishes at home and abroad are equipped with sliding nozzle systems. The slide plate is a key component of the sliding nozzle, an important part that directly controls the molten steel and determines the function of the sliding nozzle. During the use of the skateboard, it needs to withstand the chemical erosion and physical erosion of high-temperature molten steel for a long time, and it is subjected to intense and transient thermal shock and mechanical wear, so the service conditions are extremely harsh; The thickness and the size of the board are strictly r...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
Patent Type & Authority Applications(China)
IPC IPC(8): C04B35/103C04B35/66
CPCC04B35/103C04B35/66C04B2235/3206C04B2235/3217C04B2235/3418C04B2235/401C04B2235/402C04B2235/425C04B2235/5454
Inventor 李伟锋李书成查新光
Owner HENAN XIBAO METALLURGICAL MATERIALS GROUP
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Patsnap Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Patsnap Eureka Blog
Learn More
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic, Popular Technical Reports.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap|About US| Contact US: help@patsnap.com