Casting sand for pump body sand mold casting
A technology of sand casting and foundry sand, which is applied in casting molding equipment, molds, cores, etc., can solve the problems of increased production cost, high price, and is not suitable for small-scale foundries, and achieves reduced gas generation and excellent refractoriness. and thermal stability, air permeability and resistance to liquid metal penetration
- Summary
- Abstract
- Description
- Claims
- Application Information
AI Technical Summary
Problems solved by technology
Method used
Examples
Example Embodiment
[0016] Example 1
[0017] (1) Add 10 parts of sodium carboxymethyl cellulose and 8 parts of plant ash to 130 parts of water, stir to form a uniform slurry, add 15 parts of ore powder and 12 parts of asbestos powder, mix well, and mix the mixture at a microwave frequency of 2450MHz and a power of 600W Microwave treatment for 15 minutes, after the treatment liquid is naturally cooled to room temperature, material I is obtained;
[0018] (2) Heat 120 parts of silica sand, 8 parts of white carbon black and 3 parts of graphite powder to 100-110℃ for 10 minutes, then add 5 parts of magnesium stearate and 6 parts of pectin, continue to heat to 120-130℃ Mix for 10 minutes to obtain material II;
[0019] (3) Add material I, 6 parts of coconut bran and 2 parts of nano alumina to material II, mix them evenly and send them to a freeze dryer, and finally make particles with 50-100 meshes by a crusher.
[0020] SiO in silica sand 2 The content is higher than 98%.
[0021] Preparation of ore powder:...
Example Embodiment
[0023] Example 2
[0024] (1) Add 15 parts of sodium carboxymethyl cellulose and 10 parts of plant ash into 150 parts of water, stir to form a uniform slurry, add 20 parts of ore powder and 10 parts of asbestos powder, and mix well. The mixture is at a microwave frequency of 2450MHz and a power of 600W. Microwave treatment for 15 minutes, after the treatment liquid is naturally cooled to room temperature, material I is obtained;
[0025] (2) Heat 130 parts of silica sand, 10 parts of white carbon black and 5 parts of graphite powder to 100-110℃ and keep mixing for 10min, then add 7 parts of magnesium stearate and 5 parts of pectin, continue heating to 120-130℃ Mix for 10 minutes to obtain material II;
[0026] (3) Add material I, 8 parts of coconut bran and 3 parts of nano alumina to material II, mix them evenly and send them to a freeze dryer, and finally make particles of 50-100 mesh through a crusher.
[0027] SiO in silica sand 2 The content is higher than 98%.
[0028] Preparatio...
PUM
Abstract
Description
Claims
Application Information
- R&D Engineer
- R&D Manager
- IP Professional
- Industry Leading Data Capabilities
- Powerful AI technology
- Patent DNA Extraction
Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic.
© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap