Multifunctional microporous styptic powder and preparation method thereof
A technology of hemostatic powder and starch, which is applied in the field of natural biomedical materials, can solve the problems of limited liquid absorption effect and low porosity of composite microporous polysaccharide particles, and achieve a simple method, enhanced hemostatic effect, and strong controllability Effect
- Summary
- Abstract
- Description
- Claims
- Application Information
AI Technical Summary
Problems solved by technology
Method used
Image
Examples
Embodiment 1
[0048] Embodiment 1, preparation multifunctional microporous hemostatic powder
[0049] (1) Preparation of carboxymethyl starch paste: carboxymethyl starch (2% aqueous solution viscosity at 25°C is 500mpas, degree of substitution is 0.5) is mixed with water in a mass ratio of 1:40, and placed in a 30°C Stir in a water bath to make it fully dissolved to obtain a carboxymethyl starch paste.
[0050] (2) Preparation of carboxymethyl chitosan solution: carboxymethyl chitosan (at 25°C, viscosity of 1% aqueous solution is 100mpas, degree of substitution is 80%) is mixed with water in a mass ratio of 1:60 and Fully dissolve, and filter the insoluble matter to obtain a carboxymethyl chitosan solution for subsequent use.
[0051] (3) The carboxymethyl starch paste liquid and the carboxymethyl chitosan solution were blended at a ratio of 1:1 to obtain a blended solution.
[0052] (4) Dispersed porogen: disperse corn gluten with a particle size of 5 μm into the blended solution in step...
Embodiment 2
[0057] Example 2, preparation of multifunctional microporous hemostatic powder
[0058] (1) Preparation of pregelatinized starch paste: mix pregelatinized starch (the viscosity of 2% aqueous solution at 25°C is 200mpas) with water at a mass ratio of 1:25, and place it in a water bath at 50°C to stir and swell fully A pregelatinized starch paste is prepared.
[0059] (2) Preparation of carboxymethyl chitosan solution: carboxymethyl chitosan (at 25°C, the viscosity of 1% aqueous solution is 200mpas, and the degree of substitution is 80%) is mixed with water in a mass ratio of 1:30 and fully dissolve, and filter the insoluble matter to obtain a carboxymethyl chitosan solution for subsequent use.
[0060] (3) The starch paste liquid and the carboxymethyl chitosan solution were blended at a ratio of 1:1 to obtain a blended solution.
[0061] (4) Dispersed porogen: CaCO with a particle size of 2 μm 3 Disperse into the blended solution in step (3), porogen: polysaccharide solid co...
Embodiment 3、 Embodiment 1 and Embodiment 2
[0066] The performance test of embodiment 3, embodiment 1 and embodiment 2 multifunctional microporous hemostatic powder
[0067] (1) Water absorption rate test
[0068] Water absorption rate test: Weigh 0.1g sample (W 0 ) into about 10.0 g of purified water, and after the hemostatic powder swells for about 5 minutes to saturate the water absorption, it is centrifuged at 500 rpm for 10 minutes, and weighed to obtain W 1 . Water absorption ratio = (W 1 -W 0 ) / W 0 ×100%. The samples were the hemostatic powder prepared in Example 1, the hemostatic powder prepared in Example 2, and a certain compound hemostatic powder on the market (Shandong Saikesaisi Pharmaceutical Technology Co., Ltd. "instantaneous" composite microporous polysaccharide hemostatic powder ) and a certain starch hemostatic powder on the market (Hangzhou Xiehe Medical Supplies Co., Ltd. "Xinsuling" MPH absorbable hemostatic microspheres).
[0069] Table 1. Results of water absorption ratio
[0070] ...
PUM
Property | Measurement | Unit |
---|---|---|
Viscosity | aaaaa | aaaaa |
Viscosity | aaaaa | aaaaa |
Particle size | aaaaa | aaaaa |
Abstract
Description
Claims
Application Information
- R&D Engineer
- R&D Manager
- IP Professional
- Industry Leading Data Capabilities
- Powerful AI technology
- Patent DNA Extraction
Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic, Popular Technical Reports.
© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap|About US| Contact US: help@patsnap.com