High-speed tinning solution and preparation method thereof

A high-speed plating and solution technology, applied in the field of electroplating, can solve the problems of poor uniformity and singleness of grains, and achieve the effect of uniform grains, uniform color and control of the formation of tin whiskers

Inactive Publication Date: 2016-06-08
济南德锡科技有限公司
View PDF9 Cites 21 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

[0005] The purpose of the present invention is to provide a high-speed tin plating solution and its preparation method, aiming to solve the problem that the existing high-speed tin plating technology uses a single grain refiner, resulting in poor uniformity of the grains, and the coating is divided into high, medium and low areas. problem with partitioning

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • High-speed tinning solution and preparation method thereof
  • High-speed tinning solution and preparation method thereof
  • High-speed tinning solution and preparation method thereof

Examples

Experimental program
Comparison scheme
Effect test

Embodiment Construction

[0038] In order to make the object, technical solution and advantages of the present invention more clear, the present invention will be further described in detail below in conjunction with the examples. It should be understood that the specific embodiments described here are only used to explain the present invention, not to limit the present invention.

[0039] The application principle of the present invention will be described in detail below in conjunction with the accompanying drawings.

[0040] The high-speed tin plating solution 1L of the embodiment of the present invention includes: stannous methanesulfonate 100ml / L~300ml / L, methanesulfonic acid 70wt% 75ml / L~150ml / L, solvent 10g / L~30g / L, Low foam surfactant 1g / L~10g / L, antioxidant 0.5g / L~3g / L, combined grain refiner 0.02g / L~0.5g / L.

[0041] The high-speed tin plating solution 1L optimized composition of the embodiment of the present invention is as follows: stannous methanesulfonate 150ml / L~250ml / L, methanesulfonic ...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

No PUM Login to View More

Abstract

The invention discloses a high-speed tinning solution and a preparation method thereof. Deionized water is added to a clean beaker until the volume of the water accounts for 1 / 2 that of the beaker; a required amount of methanesulfonic acid is measured through a measuring cylinder and put in the beaker, and the mixture is stirred uniformly; a required amount of tin methanesulfonate is measured through the measuring cylinder and put in the beaker, and the mixture is stirred uniformly; additives with the concentration being 60-100 ml / L are added to a tin methanesulfonate solution and stirred uniformly; the deionized water is added until the mixture is in a predetermined volume, and the high-speed tinning solution is prepared. Plating with uniform color and consistent crystal grains is obtained in a wider current density range, formation of tin whisker is effectively controlled, the anti-tarnishing capability and the excellent weldable performance of the plating are guaranteed, the current density can be increased to the greatest extent, the anti-tarnishing capability and the weldable performance are guaranteed, meanwhile, a defoaming agent is not used, and fewer organic impurities are mixed in the plating.

Description

technical field [0001] The invention belongs to the technical field of electroplating, and in particular relates to a high-speed tin plating solution and a preparation method thereof. Background technique [0002] Tin coating has good stability, strong corrosion resistance and discoloration resistance, non-toxic, soft coating, good solderability and ductility, so it is widely used in industry. Tin plating on steel or copper substrates is a cathodic coating. The thin tin layer has a good protective effect on the substrate and is non-toxic. Therefore, tin plating is often used in the production of steel strips and the canning industry. Early tin plating often used hot-dipping process. This production method consumes more energy. Not only is it difficult to obtain a uniform and smooth coating, but it is also easy to cause tin waste. People have successfully studied alkaline tin plating and neutral plating. Tin and acid tin plating are used stably in production practice. [00...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
IPC IPC(8): C25D3/32
CPCC25D3/32
Inventor 朱艳丽王鲁艳
Owner 济南德锡科技有限公司
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Patsnap Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Patsnap Eureka Blog
Learn More
PatSnap group products