A kind of imitation jade Longquan celadon, glaze, billet and preparation method of Longquan celadon

A technology of imitating jade and celadon, applied to clay products, other household utensils, household utensils, etc., can solve the problems of being corroded by acid and alkali, easy to be oxidized by air, and low simulation degree, so as to reduce the melting temperature and improve the glaze surface The effect of glossiness and color stability

Active Publication Date: 2018-10-30
龙泉市土圭垚文化创意有限公司
View PDF6 Cites 0 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

The above-mentioned imitation jade guardrails, imitation jade glass products and other imitation jade materials are not only expensive, but also mainly use organic materials, which not only have low degree of simulation, but are also easily oxidized by air, corroded by acid and alkali; Making imitation jade products, especially imitation jade Longquan celadon, is rarely reported in the prior art

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • A kind of imitation jade Longquan celadon, glaze, billet and preparation method of Longquan celadon
  • A kind of imitation jade Longquan celadon, glaze, billet and preparation method of Longquan celadon
  • A kind of imitation jade Longquan celadon, glaze, billet and preparation method of Longquan celadon

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0038] Embodiment 1: A kind of glaze imitating jade Longquan celadon is made by following glaze, and described glaze is made up of component A and component B; Component A is ultra-white basic material colored glaze, according to component A The total amount is 100% by weight, component A is: potassium feldspar 41%, quartz 18%, talc 24%, calcium borate 8%, bone ash 4%, bentonite 5%; component B is colored glaze Material, component B is: potassium feldspar 49%, quartz 10%, glaze fruit 10%, dolomite 7%, limestone 15%, strontium carbonate 8%, CuO 1%. The glaze imitation jade obtained by this ratio has a high degree of imitation, fine texture and good effect.

Embodiment 2

[0039] Embodiment 2: A kind of glaze imitating jade Longquan celadon is made of the following glaze, the glaze is composed of component A and component B; component A is the ultra-white base color glaze, according to the total amount of component A 100% by weight, component A is: potassium feldspar 44%, quartz 17%, talc 25%, calcium borate 9%, bone ash 2%, bentonite 3%; component B is color glaze, Component B is: potassium feldspar 43%, quartz 10%, glaze fruit 12%, dolomite 10%, limestone 20%, strontium carbonate 4%, CuO 1%. The glaze imitation jade obtained by this ratio has a high degree of imitation, fine texture and good effect.

Embodiment 3

[0040]Embodiment 3: A kind of glaze imitating jade Longquan celadon is made of the following glaze, the glaze is composed of component A and component B; component A is the ultra-white base color glaze, according to the total amount of component A 100% by weight, component A is: potassium feldspar 35%, quartz 21%, talc 28%, calcium borate 10%, bone ash 3%, bentonite 3%; component B is colored glaze, Component B is: potassium feldspar 60%, quartz 7%, glaze fruit 7%, dolomite 5%, limestone 16.5%, strontium carbonate 4%, CuO 0.5%. The glaze imitation jade obtained by this ratio has a high degree of imitation, fine texture and good effect.

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

No PUM Login to View More

Abstract

The invention relates to a blank material and glaze material of a jade-imitated Longquan celadon and a preparation method of the product. The jade-imitated Longquan celadon comprises a glaze and a blank; the glaze material is composed of a component A and a component B; the component A comprises, by weight, 35-45% of potassium feldspar, 15-21% of quartz, 20-28% of talc, 6-10% of calcium borate, 2-6% of bone ash, and 3-7% of bentonite; the component B is a color glaze material and comprises, by weight, 40-60% of feldspar, 7-13% of quartz , 7-13% of glaze paste, 5-10% of dolomite, 10-20% of limestone, 4-12% of strontium carbonate, and 0.5-1.5% of CuO. The blank of the jade-imitated Longquan celadon is prepared from the following blank material by weight: 30-50% of Longquan porcelain clay, 40-60% of Longyan kaolin, and 5-15% of limestone. The product is a Longquan celadon product which is sintered in a 1200 DEG C oxidation atmosphere, presents calm and steady color and luster and greasy texture and is similar to jades but superior to jades.

Description

technical field [0001] The invention relates to a blank, glaze and a preparation method of jade-like Longquan celadon. Background technique [0002] Since ancient times, jade wares have had a very high aesthetic value and a very strong decorative effect. Especially in jewelry decoration, the inlay of jade improves the economic value and decorative effect of jewelry. However, jade is a non-renewable resource, especially high-quality jade, which is too expensive for ordinary people to catch up with. Ordinary imitation jade decoration materials are mostly organic materials, and the surface effect will deteriorate with time. And ceramic material has good physical stability and chemical stability after high-temperature firing, therefore, it is particularly important to develop a blank, glaze and preparation method of a jade-like Longquan celadon with stable color and natural effect. [0003] At present, the Chinese invention patent database mainly discloses imitation jade guard...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
Patent Type & Authority Patents(China)
IPC IPC(8): C03C8/22C04B33/00C04B33/34C04B33/24
CPCC03C8/22C03C2209/02C04B33/00C04B33/24C04B33/34C04B2235/3208C04B2235/349
Inventor 吴艳芳吴三保张敏华张建平俞锦辉李德胜吴新伟沈其旺许灵雨翁妙妙
Owner 龙泉市土圭垚文化创意有限公司
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Patsnap Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Patsnap Eureka Blog
Learn More
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic, Popular Technical Reports.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap|About US| Contact US: help@patsnap.com