Environment-friendly type solar thermal-insulation building material

A technology of building materials and solar energy, which is applied in the field of environmentally friendly solar thermal insulation building materials, can solve problems such as poor thermal insulation performance, and achieve the effects of increased closed cell rate, improved dimensional stability, and excellent performance

Inactive Publication Date: 2016-07-20
毛文辉
View PDF4 Cites 0 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

[0002] When the existing solar thermal insulation building materials are applied to the water tank of the solar water heater, the thermal insulation performance is not good, and it needs to be tightly closed

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0016] This embodiment provides an environmentally friendly solar thermal insulation building material, which is obtained by mixing and foaming the following raw materials in parts by weight: 120 parts of polyether foaming agent, 50 parts of polyether polyol I, polyether 35 parts of polyol II, 3 parts of expanded vermiculite, 5 parts of nano-silica, 10 parts of monochlorodifluoroethane, 5 parts of dimethyl methyl phosphate, 1 part of diethanol monoisopropanolamine, silicone foam 1 part of stabilizer;

[0017] The polyether foaming agent is made according to the following raw materials in parts by weight: 5 parts of glycerol polyether resin, 3 parts of glycol ether resin, 0.2 part of foam stabilizer water-soluble silicone oil, catalyst N, N-dimethylcyclo 0.1 part of hexylamine, 0.1 part of curing agent dibutyltin dilaurate, 10 parts of polyphenyl polyisocyanate, 1 part of hydrogen peroxide, 3 parts of water;

[0018] The functionality of the polyether polyol I is 4.5, and its ...

Embodiment 2

[0025] This embodiment provides an environmentally friendly solar thermal insulation building material, which is obtained by mixing and foaming the following raw materials in parts by weight: 140 parts of polyether foaming agent, 70 parts of polyether polyol I, polyether 50 parts of polyol II, 6 parts of expanded vermiculite, 8 parts of nano-silica, 20 parts of chlorodifluoroethane, 6 parts of dimethyl methyl phosphate, 5 parts of diethanol monoisopropanolamine, silicone foam 5 parts of stabilizer;

[0026] The polyether foaming agent is made according to the following raw materials in parts by weight: 7 parts of glycerol polyether resin, 5 parts of glycol ether resin, 0.3 part of foam stabilizer water-soluble silicone oil, catalyst N, N-dimethyl ring 0.3 parts of hexylamine, 0.3 parts of curing agent dibutyltin dilaurate, 10 parts of polyphenyl polyisocyanate, 3 parts of hydrogen peroxide, 5 parts of water;

[0027] The functionality of the polyether polyol I is 5.0, and its...

Embodiment 3

[0034] This embodiment provides an environmentally friendly solar thermal insulation building material, which is obtained by mixing and foaming the following raw materials in parts by weight: 130 parts of polyether foaming agent, 60 parts of polyether polyol I, polyether 40 parts of polyol II, 5 parts of expanded vermiculite, 6 parts of nano-silica, 15 parts of monochlorodifluoroethane, 5.5 parts of dimethyl methyl phosphate, 3 parts of diethanol monoisopropanolamine, silicone foam 3 parts of stabilizer;

[0035] The polyether foaming agent is made according to the following raw materials in parts by weight: 6 parts of glycerol polyether resin, 4 parts of glycol ether resin, 0.25 part of foam stabilizer water-soluble silicone oil, catalyst N, N-dimethyl ring 0.2 parts of hexylamine, 0.2 parts of curing agent dibutyltin dilaurate, 10 parts of polyphenyl polyisocyanate, 2 parts of hydrogen peroxide, 4 parts of water;

[0036] The functionality of the polyether polyol I is 4.8, ...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

PropertyMeasurementUnit
hydroxyl valueaaaaaaaaaa
hydroxyl valueaaaaaaaaaa
hydroxyl valueaaaaaaaaaa
Login to View More

Abstract

The invention discloses an environment-friendly type solar thermal-insulation building material. The environment-friendly type solar thermal-insulation building material is characterized by being obtained by mixing, foaming and curing the following raw materials in parts by weight: 120-140 parts of a polyether foaming agent, 50-70 parts of polyether polyol I, 35-50 parts of polyether polyol II, 3-6 parts of expanded vermiculite, 5-8 parts of nano silicon dioxide, 10-20 parts of monochlorodifluoroethane, 5-6 parts of dimethyl methylphosphate, 1-5 parts of diethanol monoisopropanolamine and 1-5 parts of an organic silicon foam stabilizer, wherein the polyether polyol I is lignin polyether polyol, and the polyether polyol II is polyether polyol which is polymerized by taking modified peanut oil as an initiator and by taking epoxypropane as a polymerization monomer. Indexes such as a heat conduction efficient, compressive strength, tensile adhesive strength, dimension stable performance and porosity by closed pore of the environment-friendly type solar thermal-insulation building material are obviously improved in comparison with those of a current thermal-insulation building material; and the environment-friendly type solar thermal-insulation building material is a thermal-insulation building material which is free of phenomena such as shrinkage, deformation, expansion and cracking under a freezing or high-temperature condition, and is excellent in performance.

Description

technical field [0001] The invention relates to the technical field of solar thermal insulation building materials, in particular to an environment-friendly solar thermal insulation building material. Background technique [0002] Existing solar thermal insulation building materials have poor thermal insulation performance when applied to the water tank of the solar water heater, and need to be tightly covered. Contents of the invention [0003] The technical problem to be solved by the present invention is to provide an environment-friendly solar thermal insulation building material to solve the above technical problems. [0004] In order to solve the above technical problems, an embodiment of the present invention provides an environmentally friendly solar thermal insulation building material, which is obtained by mixing and foaming the following raw materials in parts by weight: 120-140 parts of polyether foaming agent , 50-70 parts of polyether polyol I, 35-50 parts o...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
Patent Type & Authority Applications(China)
IPC IPC(8): C08G18/48C08J9/08C08J9/14C08K7/10C08K3/36C08G65/28
CPCC08G18/4816C08G18/4829C08G18/4891C08G65/2609C08G2101/00C08J9/08C08J9/144C08J2203/02C08J2203/142C08J2203/184C08J2205/052C08J2375/08C08K3/36C08K7/10C08K2201/011
Inventor 毛文辉
Owner 毛文辉
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Eureka Blog
Learn More
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic, Popular Technical Reports.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap|About US| Contact US: help@patsnap.com