Light environment-friendly rock glaze imitated ceramic and preparation process
What is Al technical title?
Al technical title is built by PatSnap Al team. It summarizes the technical point description of the patent document.
A preparation process and imitation rock technology, which is applied in the field of ceramics, can solve the problems of fragility, light porcelain and brittle texture, and achieve the effects of light weight, increased strength, and enhanced toughness
Active Publication Date: 2016-07-27
FUJIAN PROVINCE DEHUA COUNTY LUXURIES CERAMICS CO LTD
View PDF3 Cites 14 Cited by
Summary
Abstract
Description
Claims
Application Information
AI Technical Summary
This helps you quickly interpret patents by identifying the three key elements:
Problems solved by technology
Method used
Benefits of technology
Problems solved by technology
[0004] The existing light porcelain has the following two disadvantages: one is that it needs to be fired twice, and the other is that the texture of light porcelain is relatively brittle and fragile.
Method used
the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more
Examples
Experimental program
Comparison scheme
Effect test
specific Embodiment 1
[0028] Lightweight and environmentally friendly rock-like glaze ceramics, the bottom glaze is prepared from the following raw materials in parts by weight: feldspar 28, dolomite 23, kaolin 12, talc 6, iron oxide 10, manganese oxide 10, volcanic stone 5, double fly powder 2. Sepiolite 4; surface glaze is prepared from the following raw materials in parts by weight: feldspar 22, quartz 20, double fly powder 18, zinc oxide 11, dolomite 6, wood fish stone 6, medical stone 8, zirconiumsilicate 7. Iron oxide 2.
specific Embodiment 2
[0029] Lightweight and environmentally friendly rock-like glaze ceramics, the bottom glaze is prepared from the following raw materials in parts by weight: feldspar 22, dolomite 27, kaolin 18, talc 6, iron oxide 6, manganese oxide 5, volcanic stone 8, double fly powder 3. Sepiolite 5; surface glaze is prepared from the following raw materials in parts by weight: feldspar 25, quartz 16, double fly powder 12, zinc oxide 18, dolomite 8, wood fish stone 5, medical stone 6, zirconiumsilicate 5. Iron oxide5.
specific Embodiment 3
[0030] Lightweight and environmentally friendly rock-like glaze ceramics, the bottom glaze is prepared from the following raw materials in parts by weight: feldspar 25, dolomite 24, kaolin 20, talc 8, iron oxide 7, manganese oxide 3, volcanic stone 6, double fly powder 5. Sepiolite 2; the surface glaze is prepared from the following raw materials in parts by weight: feldspar 24, quartz 17, double fly powder 16, zinc oxide 10, dolomite 8, wood fish stone 6, medical stone 7, siliconZirconium acid 8, iron oxide 4.
[0031] The preparation technology of light-weight environment-friendly rock-like glaze ceramics is characterized in that, using the light-weight environment-friendly rock-like glaze ceramics described in any one of the above specific embodiments 1 to 3, the specific steps are as follows:
[0032] Step 1, according to the raw materials of the bottom glaze and the top glaze, prepare the bottom glaze and the top glaze respectively. The bottom glaze is made by wet ball m...
the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More
PUM
Login to View More
Abstract
The invention relates to the technical field of ceramics, in particular to a light environment-friendly rock glaze imitated ceramic and a preparation process.The light environment-friendly rock glaze imitated ceramic comprises a ceramic body, ground glaze and cover glaze.The ground glaze is prepared from feldspar, dolomite, kaolin, talc, ferricoxide, pelelith, heavy calciumcarbonatepowder and sepiolite.The cover glaze is prepared from feldspar, quartz, calciumcarbonatepowder, zincoxide, dolomite, limonite, medical stone, zirconiumsilicate and ferricoxide.The light environment-friendly rock glaze imitated ceramic is similar to common basalt and limestone, the glaze surface touch sense is rough, and rough and plain visual perception is given to people.The ceramic body of the light environment-friendly rock glaze imitated ceramic is low in mass, the ceramic body is combined with the appearance of rock glaze, a distinct conflict is formed, and a special effect is achieved.The rock glaze imitated ceramic is high in strength and good in toughness, and is fired at a time, energy saving and environment friendliness are achieved, and the production cost is reduced.
Description
technical field [0001] The invention relates to the technical field of ceramics, in particular to a light-weight and environment-friendly imitation rock glaze ceramic and a preparation process. Background technique [0002] With the progress of society and the development of science and technology, the awareness of environmental protection and use safety is becoming stronger and stronger. Compared with plastic tableware, ceramic tableware has the advantages of good wear resistance, easy cleaning, and durability. However, ceramic tableware is brittle and durable. Low impact capacity, brittle, and difficult to degrade after broken, so there is an urgent need to develop an environmentally friendly ceramic that improves toughness and is easy to degrade. [0003] Lightweight ceramics have the characteristics of strong plasticity, high ornamental value, environmental protection, and safety, and are widely favored in the world. Lightweight ceramics are environmentally friendly. Un...
Claims
the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More
Application Information
Patent Timeline
Application Date:The date an application was filed.
Publication Date:The date a patent or application was officially published.
First Publication Date:The earliest publication date of a patent with the same application number.
Issue Date:Publication date of the patent grant document.
PCT Entry Date:The Entry date of PCT National Phase.
Estimated Expiry Date:The statutory expiry date of a patent right according to the Patent Law, and it is the longest term of protection that the patent right can achieve without the termination of the patent right due to other reasons(Term extension factor has been taken into account ).
Invalid Date:Actual expiry date is based on effective date or publication date of legal transaction data of invalid patent.
Login to View More 
Login to View More