Method for preparing super-absorbent resin

一种超吸收性、聚合物的技术，应用在吸收垫、医药科学、假体等方向，能够解决超吸收性聚合物分离、吸收度减小、物理特性冲突等问题，达到物理特性改善的效果

Active Publication Date: 2016-07-27
LG CHEM LTD
View PDF10 Cites 16 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

[0010] However, although the permeability is improved by adding silica or clay, there is a problem that the centrifuge retention capacity or the absorbency under load decreases in proportion to it, and it is easy to occur with superabsorption due to external physical shock during transportation. Separation of Sexual Polymers
However, these physical properties conflict with each other, so it is very difficult to satisfy all of them

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • Method for preparing super-absorbent resin
  • Method for preparing super-absorbent resin
  • Method for preparing super-absorbent resin

Examples

Experimental program
Comparison scheme
Effect test

preparation example Construction

[0026] A method of preparing a superabsorbent polymer according to an embodiment of the present invention may include the following steps:

[0027] performing thermal polymerization or photopolymerization of a monomer composition comprising a water-soluble ethylenically unsaturated monomer, an internal crosslinking agent and a polymer to prepare a hydrogel polymer having a gel strength of 10000Pa to 13000Pa Initiator;

[0028] Coarsely pulverizing the hydrogel polymer;

[0029] drying the coarsely pulverized hydrogel polymer;

[0030] comminuting the dried polymer; and

[0031] The pulverized polymer is mixed with a surface crosslinking agent to perform a surface crosslinking reaction of the mixture.

[0032] The present inventors continued research on superabsorbent polymers exhibiting high absorption rate and liquid permeability while having high centrifuge retention capacity, and they found that the hydrogel polymer as the matrix resin of superabsorbent polymers When th...

Embodiment 1

[0122] In a 2L glass reactor surrounded by a jacket (heating medium pre-cooled at 25°C circulated through the jacket), 450 g of acrylic acid was mixed with 8 g of 0.5% by weight IRGACURE819 initiator diluted in acrylic acid, and 50 g of acrylic acid was injected. Diluted 5% by weight polyethylene glycol diacrylate (PEGDA, molecular weight 598g / mol, curing dose 200mJ / cm 2 ), and inject 10g of 5% by weight of 1,6-hexanediol diacrylate diluted with acrylic acid (molecular weight is 226g / mol, curing dose is 320mJ / cm 2 ), and then slowly add 660 g of 32% by weight caustic soda solution dropwise.

[0123] After confirming that the temperature of the mixture was raised to 80°C or higher by the heat of neutralization generated when the two solutions were mixed, the mixture was left to stand until the reaction temperature reached 40°C. When the reaction temperature reached 40° C., 50 g of 2% sodium persulfate solution diluted with water was injected.

[0124] The solution was poured ...

Embodiment 2

[0130] A superabsorbent polymer was prepared in the same manner as in Example 1, except that 55 g of 5% by weight polyethylene glycol diacrylate diluted with acrylic acid was used instead of 50 g thereof in Example 1, and 11 g of acrylic acid diluted Diluted 5% by weight 1,6-hexanediol diacrylate was substituted for 10 g thereof in Example 1.

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

PUM

PropertyMeasurementUnit
gel strengthaaaaaaaaaa
particle diameteraaaaaaaaaa
gel strengthaaaaaaaaaa
Login to view more

Abstract

The present invention relates to a method for preparing a super-absorbent resin. According to the method for preparing a super-absorbent resin, a super-absorbent resin which has an improved absorption rate and solution permeability, no deterioration in water retaining capacity or pressurized absorptive capacity, and improved physical properties can be provided.

Description

[0001] Background of the invention technical field [0002] The present disclosure relates to a method of preparing superabsorbent polymers, and more particularly, to a method of preparing superabsorbent polymers which can be used to obtain superabsorbent polymers exhibiting high absorption rate and liquid permeability and high centrifuge retention capacity. Absorbent polymer. [0003] This application is based on and claims priority to Korean Patent Application No. 10-2013-0153325 filed on December 10, 2013 and Korean Patent Application No. 10-2014-0172998 filed on December 4, 2014 rights, the entire contents of which are incorporated herein by reference. Background technique [0004] Super Absorbent Polymer (SAP) is a synthetic polymer material that can absorb 500 to 1000 times its own weight in water. Various developers name it different names, such as SAM (SuperAbsorbentMaterial, superabsorbent material), AGM (AbsorbentGelMaterial, absorbent gel material) and so on. ...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

Application Information

Patent Timeline
no application Login to view more
Patent Type & Authority Applications(China)
IPC IPC(8): C08F2/00C08F2/10C08F10/02C08F20/10C08J3/075C08J3/24
CPCC08F2/10C08J3/075C08F2/48C08F220/06A61L15/60C08F6/008C08J3/245C08J2333/02A61L27/20C08L1/00C08F222/102C08F2/00C08F10/02C08F20/10Y10S526/92A61L15/24A61L26/0014A61L26/0061C08J3/07C08J3/12C08J2335/02
Inventor 郑和胤韩章善柳喆熙金美永安泰彬
Owner LG CHEM LTD
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Try Eureka
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap