PC/ABS alloy material with high welding strength

A technology of welding strength and alloy materials, applied in the field of materials science, can solve problems such as insufficient welding strength, and achieve the effects of high welding strength, excellent physical properties, and excellent blending effect.

Inactive Publication Date: 2016-08-03
中广核俊尔(上海)新材料有限公司
View PDF5 Cites 12 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

[0015] Aiming at the above-mentioned technical problems in the prior art, the present invention provides a PC / ABS alloy material with high welding strength, and the PC / ABS alloy material with high welding strength will solve the PC / ABS alloy material in the prior art. The alloy is prone to technical problems of insufficient welding strength during the welding process

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • PC/ABS alloy material with high welding strength
  • PC/ABS alloy material with high welding strength

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1--5

[0034] (Adding white oil) Add PC resin, ABS resin, and various additives to the high-speed mixer and stir for 2 minutes at high speed, then add to the main feeder of the extruder, and then add to the twin-screw extruder for basic granulation. The temperature distribution of the extruder is as follows: from the feed section to the head: 240°C, 260°C, 260°C, 260°C, 255°C, 250°C, 250°C, 250°C, 250°C, die head: 260°C , After the material is extruded, it is water-cooled, pelletized, and then packaged. The pellets were dried in a blast oven at 120°C for 4 hours, and then test specimens were prepared by an injection molding machine.

[0035] See Table 1 for the parts by weight of the raw materials in Examples 1 to 5.

[0036] Raw material parts by weight of table 1 embodiment 1~5

[0037]

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

PropertyMeasurementUnit
melt flow indexaaaaaaaaaa
impact strengthaaaaaaaaaa
Login to View More

Abstract

The invention provides a PC / ABS alloy material with high welding strength. The PC / ABS alloy material is prepared from, by weight, 30-65 parts of polycarbonate, 15-40 parts of styrene-butadiene-acrylonitrile copolymer, 10-20 parts of styrene-acrylonitrile copolymer, 3-5 parts of high rubber powder, 1-5 parts of compatilizer and 0.5-1 part of processing auxiliaries. The invention provides a preparing method for the PC / ABS alloy material with high welding strength. The invention further provides application of the PC / ABS alloy material with high welding strength to automotive upholstery (like an instrument board), domestic appliance and other components. The alloy material obtained through the method is excellent in physical property and high in welding strength, and can be used in automotive upholstery, domestic appliance and other components.

Description

technical field [0001] The invention belongs to the field of material science and relates to an alloy material, in particular to a PC / ABS alloy material with high welding strength. Background technique [0002] The alloy material of polycarbonate and acrylonitrile-butadiene-styrene copolymer is a thermoplastic plastic made of polycarbonate (Polycarbonate) and polyacrylonitrile (ABS) alloy, combining the excellent characteristics of the two materials . It has excellent formability, high impact strength and high temperature resistance, anti-ultraviolet (UV) and other properties. Due to its structural particularity, it has become the fastest growing general-purpose engineering plastic. [0003] The connection methods of plastic products include: plastic parts pressing, matching assembly, mechanical fastening, welding, etc. Welding is divided into: hot plate welding, hot air welding, hot rod and pulse welding, ultrasonic welding, infrared welding, laser welding. Plastic weld...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
Patent Type & Authority Applications(China)
IPC IPC(8): C08L69/00C08L55/02C08L25/12C08L21/00
CPCC08L69/00C08L2205/025C08L2205/035C08L2205/08C08L2207/53C08L55/02C08L25/12C08L21/00
Inventor 顾伟黄志杰杨仓先杨燕
Owner 中广核俊尔(上海)新材料有限公司
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Patsnap Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Patsnap Eureka Blog
Learn More
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic, Popular Technical Reports.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap|About US| Contact US: help@patsnap.com