Manufacturing method for zirconium dioxide ceramic green-pressing

A technology of zirconia and nano zirconia, applied in the direction of ceramic molding machines, manufacturing tools, etc., can solve the problem of affecting the strength and light transmittance of nano zirconia ceramics, the inability to eliminate the uneven dispersion of powder agglomeration additives, and poor performance Difficult to meet the requirements and other problems, to achieve the effect of powder utilization rate and labor efficiency improvement, less defects, and dense ceramic body

Inactive Publication Date: 2016-08-17
LIAONING UPCERA CO LTD
View PDF4 Cites 14 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

When the above molding method is used for molding processing, problems such as powder agglomeration and uneven dispersion of additives cannot be eliminated, resulting in low density of the green body after molding and defects such as holes
These defects will directly affect the strength and light transmittance of the sintered nano-zirconia ceramics
I

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • Manufacturing method for zirconium dioxide ceramic green-pressing
  • Manufacturing method for zirconium dioxide ceramic green-pressing
  • Manufacturing method for zirconium dioxide ceramic green-pressing

Examples

Experimental program
Comparison scheme
Effect test

Example Embodiment

[0025] Example 1

[0026] (1) Dry-pressing pre-forming: Put 3 mol of yttrium stabilized nano-zirconia granulated powder (Orient Zirconium Industry, OZ-3Y) into a dry-pressing mold, and then perform dry-pressing molding to obtain a preform. The molding temperature is 25℃ and the pressure is 30MPa;

[0027] (2) Warm isostatic pressing: the preform after dry pressing is put into the warm isostatic pressing mold, and then the warm isostatic pressing is performed to obtain the zirconia ceramic green body. The temperature of the warm isostatic pressing is It is 150°C and the pressure is 180Mpa.

Example

[0028] Examples 2-8

[0029] According to the method described in Example 1, using the same raw materials as in Example 1, and using the process parameters of each step of Examples 2 to 8 in Table 1, the nano zirconia ceramics of Examples 2 to 8 were prepared respectively. Billet. It should be noted that although each embodiment of the present invention uses 3 mol of yttrium-stabilized nano-zirconia granulated powder to prepare zirconium dioxide ceramic green bodies, other types of nano-zirconia granulated powders commonly used in the ceramic field can be used. To realize the technical solution of the present invention, the present invention will not be described in detail here.

[0030] Table 1 Process parameters of each step of Examples 2-8

[0031]

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

PUM

PropertyMeasurementUnit
Thicknessaaaaaaaaaa
Login to view more

Abstract

An embodiment of the invention discloses a manufacturing method for zirconium dioxide ceramic green-pressings. The method comprises the following steps: (1) dry pressing performing: after nanometer zirconium dioxide pelleting powders are put into a dry pressing mold, performing dry pressing performing to obtain a preformed blank, wherein pressure in dry pressing performing is 2-100 MPa; (2) temperature isostatic compaction: after the preformed blank which is preformed by dry pressing is put into a temperature isostatic pressing mold, performing temperature isostatic compaction, to obtain a zirconium dioxide ceramic green-pressing. The method manufactures the zirconium dioxide ceramic green-pressing by firstly performing dry pressing performing and then performing temperature isostatic compaction. Since under the action of pressure and temperature of the temperature isostatic pressing, the preformed blank still has good fluidity, nanometer zirconium dioxide powder particles can be stacked in a compact method, and gas and molten additives among the powders are fully discharged. The method makes a ceramic body more compact and defects less, so that the intensity, density, and light transmittance of sintered nanometer zirconium dioxide ceramic are improved.

Description

technical field [0001] The invention relates to the field of preparation of ceramic materials, in particular to a preparation method of a zirconia ceramic green body. Background technique [0002] Nano-zirconium dioxide ceramics have the advantages of high toughness, high bending strength and high wear resistance, excellent thermal insulation performance, and close to negative thermal expansion coefficient, so they are widely used in the field of structural ceramics. [0003] The raw material for preparing nano-zirconia ceramics is nano-zirconia. Due to the characteristics of nano-materials, it is very difficult to directly use nano-zirconia powder for molding and processing. Therefore, in practical applications, the nano-zirconia powder is generally added to the additive for granulation treatment to form a nano-zirconia granulated powder with a particle size of 0.05-0.1 mm, and then the nano-zirconia granulated powder is used for granulation. Molding processing. The granu...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

Application Information

Patent Timeline
no application Login to view more
IPC IPC(8): B28B3/00C04B35/48
Inventor 严庆云张君锋严庆久
Owner LIAONING UPCERA CO LTD
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Try Eureka
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap