A preparation method of flame-retardant artificial stone containing nano perovskite oxide

A nano-calcium and oxide technology, applied in chemical instruments and methods, cobalt compounds, inorganic chemistry, etc., can solve the problems of weak flame retardant and heat resistance, poor surface gloss, poor surface abrasion resistance, etc. The effect of aging, improving service life and improving loss on ignition index

Active Publication Date: 2018-07-17
GUANGXI LISHENG STONE CO LTD
View PDF3 Cites 0 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

However, the current artificial stone still has the disadvantages of low strength, poor surface abrasion resistance, weak flame retardancy and heat resistance, and poor surface gloss.

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0025] (1) Preparation of complex La 0.7 Sr 0.3 CoO 3 With UIO-66:

[0026] (a) Weigh lanthanum nitrate, cobalt nitrate, strontium nitrate and nitric acid in proportion, dissolve them in deionized water, and prepare a nitrate solution, wherein the molar ratio of nitric acid: metal ion: water is 1:4:70; Citric acid was dissolved in deionized water to prepare a citric acid solution, wherein the molar ratio of citric acid and water was 6:40;

[0027] (b) Heat the mixed nitrate solution to 70°C, add dropwise citric acid solution under stirring, the molar ratio of the amount of citric acid added to the metal ion is 1:1; mix the nitrate solution and citric acid solution thoroughly and use concentrated The pH of the solution was adjusted to 7 with ammonia water; a gel was obtained after keeping at 80°C for 2 hours;

[0028] (c) Dry the obtained gel at 100°C to form a dry gel, and then treat it at 400°C for 1 hour to obtain the nano-perovskite catalyst La 0.7 Sr 0.3 CoO 3 .

...

Embodiment 2

[0032] (1) Preparation of complex La 0.8 Sr 0.2 CoO 3 With UIO-66:

[0033] (a) Weigh lanthanum nitrate, cobalt nitrate, strontium nitrate and nitric acid in proportion, dissolve them in deionized water, and prepare a mixed nitrate solution, in which the molar ratio of nitric acid: metal ion: water is 2:4:70; otherwise known as Get citric acid and be dissolved in deionized water, be mixed with citric acid solution, wherein the mol ratio of citric acid and water is 8:40;

[0034] (b) Heat the mixed nitrate solution to 70°C, add the citric acid solution dropwise under stirring, the molar ratio of the amount of citric acid added to the metal ion is 1:2; mix the nitrate solution and citric acid solution thoroughly and use concentrated The pH of the solution was adjusted to 7 with ammonia water; a gel was obtained after being kept at 75°C for 3 hours;

[0035] (c) Dry the obtained gel at 100°C to form a dry gel, and then treat it at 350°C for 1 hour to obtain the nano-perovskit...

Embodiment 3

[0039] (1) Preparation of complex La 0.9 Sr 0.1 CoO 3 With UIO-66:

[0040] (a) Weigh lanthanum nitrate, cobalt nitrate, strontium nitrate and nitric acid in proportion, dissolve them in deionized water, and prepare a nitrate solution, wherein the molar ratio of nitric acid: metal ion: water is 1:3:70; Citric acid was dissolved in deionized water to prepare a citric acid solution, wherein the molar ratio of citric acid and water was 5:40;

[0041] (b) Heat the mixed nitrate solution to 80°C, add citric acid solution dropwise under stirring, the molar ratio of the amount of citric acid added to the metal ion is 1:1; mix the nitrate solution and citric acid solution thoroughly and use concentrated The pH of the solution was adjusted to 7 with ammonia water; a gel was obtained after keeping at 80°C for 2 hours;

[0042] (c) Dry the obtained gel at 90°C to form a dry gel, and then treat it at 400°C for 1 hour to obtain the nano-perovskite catalyst La 0.9 Sr 0.1 CoO 3 .

[...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

PropertyMeasurementUnit
particle sizeaaaaaaaaaa
Login to View More

Abstract

The invention relates to a preparation method of flame retardant artificial stone containing a nano-perovskite oxide. The nano-perovskite oxide and a metal organic skeleton UIO material are jointly added into a ternary polyene ester material (talcum powder quartz / phenolic resin), the heat resistance and strength of artificial stone are improved, the aging time of the artificial stone is shortened,the artificial stone can be kept non-degradable for a long time under the high-temperature effect, the good flame retardant effect can be kept, and the LOI (loss on ignition) index is greatly increased.

Description

technical field [0001] The invention relates to a method for preparing flame-retardant artificial stone containing nano perovskite oxide, belonging to the field of building materials. Background technique [0002] With the improvement of people's living standards and living conditions, the interior decoration industry is developing rapidly, and the amount of decoration building materials is huge. Among them, stone is one of the most commonly used and most basic building materials, widely used in floors, walls and The paving of the countertop. The mining cost of natural stone is high, the pollution is large, and it contains a large amount of natural radioactive substances, which is harmful to human health. With the continuous development of the material field, the performance of artificial stone has gradually improved, approaching or even surpassing natural stone, and it is more and more accepted by the market and users, and is widely used in cabinets, bathrooms, floors, and...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
Patent Type & Authority Patents(China)
IPC IPC(8): C08L61/06C08L87/00C08K13/02C08K3/22C08K3/34C08K5/3492C08K5/521C08K3/32C08G83/00C01G51/00
CPCC01G51/006C04B14/36C04B24/40C04B26/122C04B2103/63C04B2111/28C04B2111/542C08G83/008C08K2201/003C08K2201/011C08L61/06C08L2201/02C08L2201/08C08L2201/14C08L87/00C08K13/02C08K2003/2289C08K3/34C08K5/34922C08K5/521C08K2003/325C04B14/042C04B22/0013C04B14/06C04B14/18C04B24/128C04B24/003C04B14/366C04B14/20C04B20/008
Inventor 骆佳豪
Owner GUANGXI LISHENG STONE CO LTD
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Patsnap Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Patsnap Eureka Blog
Learn More
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic, Popular Technical Reports.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap|About US| Contact US: help@patsnap.com