Cold-rolled silicon steel normal-temperature zero-release oil removal agent and preparation method thereof

A technology of cold-rolled silicon steel and degreaser, applied in the field of degreaser, which can solve the problems of polluting water environment and waste of water resources, and achieve the effects of reducing pollution, saving energy and saving water resources

Active Publication Date: 2016-08-31
ZHEJIANG HUAYING STEEL TECH CO LTD
View PDF3 Cites 7 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

In order to prevent sodium and other ions from remaining on the silicon steel strip, after the silicon steel strip is washed with alkali, the spray water cannot be used repeatedly, resulting in a lot of waste of water resources and serious pollution of the water environment.

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0026] A cold-rolled silicon steel room temperature zero-emission degreasing agent, the degreasing agent comprising the following weight of raw materials:

[0027] Organic biological acid 100kg, biological enzyme 80kg, biological enzyme 10kg, surfactant 5kg, bactericidal algicide 5kg, amino acid 3kg, alkyl glycoside 2kg, dispersant 1kg, stabilizer 1kg, rust inhibitor 1kg, defoamer 2kg;

[0028] The preparation method of the degreasing agent is as follows: add organic biological acid, biological enzyme and biological enzyme into the container by weight, heat up to 30°C, stir at a speed of 300r / min for 30 minutes, then add amino acid and alkyl glycoside, Continue to stir for 50 minutes, heat up to 45 ° C to obtain a mixture, then add surfactants, bactericides and algicides, dispersants, stabilizers, antirust agents and defoamers, and stir for 30 minutes at a speed of 300r / min. Cool down to room temperature, then ultrasonic for 30 minutes to obtain degreasing agent; the power of ...

Embodiment 2

[0039] A cold-rolled silicon steel room temperature zero-emission degreasing agent, the degreasing agent comprising the following weight of raw materials:

[0040] Organic biological acid 150kg, biological enzyme 120kg, biological enzyme 30kg, surfactant 10kg, bactericidal algicide 10kg, amino acid 8kg, alkyl glycoside 5kg, dispersant 3kg, stabilizer 3kg, rust inhibitor 3kg, defoamer 5kg;

[0041] The preparation method of the degreasing agent is as follows: add organic biological acid, biological enzyme and biological enzyme into the container by weight, heat up to 40°C, stir at a speed of 500r / min for 50 minutes, then add amino acid and alkyl glycoside, Continue to stir for 60 minutes, heat up to 55°C to obtain a mixture, then add surfactant, bactericide and algicide, dispersant, stabilizer, rust inhibitor and defoamer, and stir at a speed of 500r / min for 60 minutes, the temperature Cool down to room temperature, then ultrasonic for 60 minutes to obtain degreasing agent; the...

Embodiment 3

[0052] A cold-rolled silicon steel room temperature zero-emission degreasing agent, the degreasing agent comprising the following weight of raw materials:

[0053] Organic biological acid 120kg, biological enzyme 100kg, biological enzyme 20kg, surfactant 8kg, bactericide and algicide 8kg, amino acid 5kg, alkyl glycoside 3kg, dispersant 2kg, stabilizer 2kg, rust inhibitor 2kg, defoamer 3kg;

[0054]The preparation method of the degreasing agent is as follows: by weight, organic biological acid, biological enzyme and biological enzyme are added to the container, the temperature is raised to 35°C, and after stirring at a speed of 400r / min for 40 minutes, amino acid and alkyl glycoside are added, Continue to stir for 55 minutes, heat up to 50°C to obtain a mixture, then add surfactant, bactericide and algicide, dispersant, stabilizer, antirust agent and defoamer, and stir at a speed of 400r / min for 50 minutes, the temperature Cool down to room temperature, then ultrasonic for 50 m...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

PropertyMeasurementUnit
wavelengthaaaaaaaaaa
wavelengthaaaaaaaaaa
wavelengthaaaaaaaaaa
Login to View More

Abstract

The invention discloses a cold-rolled silicon steel normal-temperature zero-release oil removal agent. The oil removal agent is prepared from 100-150 parts by weight of organic bionic acid, 80-120 parts by weight of a biological ferment, 10-30 parts by weight of a bio-enzyme, 5-10 parts by weight of a surfactant and 5-10 parts by weight of a sterilization algicide. The oil removal agent does not contain phosphorus, sodium and other metal ions, does not contain persistent organic pollutants, can undergo a decomposition reaction with acid, base, oil and ferric oxide, brightens the cleaned product and produces the final decomposition products such as water and carbon dioxide. The oil removal agent does not contain any metal ions. The cleaned metal ions and calcium and magnesium ions are complexed and do not produce precipitates so that the silicon steel cleaning spray water and a cleaning agent diluent can be recycled until thorough natural consumption. The oil removal agent has a strong ion complexing capacity, hardly produces precipitates, has a strong effect of cleaning water scales and blue-green algae of a cleaning tank and does not produce built-up edges on a cleaning roller, a driving roller and a magnesium oxide coated roller.

Description

technical field [0001] The invention relates to a degreasing agent, in particular to a normal temperature zero-emission degreasing agent for silicon steel rolling and a preparation method thereof. Background technique [0002] Cold-rolled silicon steel (also known as electrical steel) is known as a "handicraft" in steel products, and has very strict requirements on the surface of the product. After the silicon steel strip is cold-rolled, there are a lot of residues on the surface of the steel strip, mainly oil, iron oxide powder, and loose impurities. If these residues are not cleaned, it will cause great harm to the performance of the silicon steel. After the magnesium oxide coating enters the bell furnace and heats up, it is easy to form black spots and water spots on the surface of the silicon steel strip. In addition, the sticky matter and iron oxide powder left when the surface of the steel strip is not cleaned will form nodules on the surface of the hearth roll. Prod...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
Patent Type & Authority Applications(China)
IPC IPC(8): C23G5/00
CPCC23G5/00
Inventor 骆光明
Owner ZHEJIANG HUAYING STEEL TECH CO LTD
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Patsnap Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Patsnap Eureka Blog
Learn More
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic, Popular Technical Reports.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap|About US| Contact US: help@patsnap.com