Seawater-resistant antibiosis oiling agent used for polyester fiber

A polyester fiber, seawater-resistant technology, applied in fiber type, fiber treatment, biochemical fiber treatment and other directions, can solve the problems of insufficient silver ion stability, decreased antibacterial performance, blackened products, etc., to reduce the use of raw materials, antistatic The effect of improved performance, improved durability

Active Publication Date: 2016-08-31
ZHEJIANG SCI-TECH UNIV
View PDF3 Cites 5 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

However, the silver ions in the material are not stable enough, and the silver ions are easily reduced to metallic silver under ultraviolet radiation. After the silver is oxidized, the product turns black and gray, and the antibacterial performance decreases.

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • Seawater-resistant antibiosis oiling agent used for polyester fiber
  • Seawater-resistant antibiosis oiling agent used for polyester fiber
  • Seawater-resistant antibiosis oiling agent used for polyester fiber

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0027] The formula of the seawater-resistant antibacterial oil agent for polyester fiber: the weight ratio range of each component is 15 parts of five-member copolymerized block silicone oil, 3 parts of diisononyl phthalate, 3 parts of nonylphenol polyethylene oxide Ether accounts for 2 parts, polyquaternium-11 accounts for 1 part, polysiloxane quaternary ammonium-16 accounts for 20 parts, distilled water accounts for 50 parts, and polyoxyethylene ether accounts for 9 parts.

Embodiment 2

[0029] The formula of the seawater-resistant antibacterial oil agent for polyester fiber: the weight ratio range of each component is 15 parts of five-member copolymerized block silicone oil, 3 parts of diisononyl phthalate, 3 parts of nonylphenol polyethylene oxide Ether accounts for 2 parts, polyquaternium-11 accounts for 6 parts, polysiloxane quaternium-16 accounts for 15 parts, distilled water accounts for 50 parts, and polyoxyethylene ether accounts for 9 parts.

Embodiment 3

[0031] The formula of the seawater-resistant antibacterial oil agent for polyester fiber: the weight ratio range of each component is 15 parts of five-member copolymerized block silicone oil, 3 parts of diisononyl phthalate, 3 parts of nonylphenol polyethylene oxide Ether accounts for 2 parts, polyquaternium-11 accounts for 11 parts, polysiloxane quaternary ammonium-16 accounts for 10 parts, distilled water accounts for 50 parts, and polyoxyethylene ether accounts for 9 parts.

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

No PUM Login to View More

Abstract

The invention relates to a seawater-resistant antibiosis oiling agent used for polyester fiber. The seawater-resistant antibiosis oiling agent is prepared from the following components in parts by weight: 10-80 parts of surface activator, 1-25 parts of plasticizer, 1-18 parts of wetter, 1-35 parts of antistatic agent, 0.5-22 parts of preservative, 2-31 parts of viscosity blender and 10-90 parts of water. The preservative and the surface activator are added into the ingredients of the seawater-resistant antibiosis oiling agent, so that the seawater-resistant antibiosis oiling agent can improve polyester fiber, the polyester fiber can own excellent smooth abrasive resistance, super-hydrophobicity and antifouling property and also has excellent anti-static electricity and antibacterial property.

Description

technical field [0001] The invention relates to a seawater-resistant antibacterial oil agent, in particular to a seawater-resistant antibacterial oil agent for polyester fibers. Background technique [0002] In recent years, high-strength polyester fiber materials have been used more and more widely in the ocean, mainly for fixed ropes on offshore oil platforms, ship cables, fishing nets, sails, protective clothing, kayaks, etc. However, the marine environment is a complex environment, in which salinity, seawater temperature, marine pollutants, marine organisms, dissolved oxygen, etc. will affect the performance and service life of polyester fiber materials, and restrict its application in the ocean, if there is no High-strength, strong corrosion resistance, non-toxic or low-toxic high-performance materials are used as a guarantee, and the development of the marine technology industry will be greatly restricted. Therefore, it is of great significance to strengthen the resea...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
IPC IPC(8): D06M15/643D06M15/53D06M15/356D06M13/224D06M101/32
CPCD06M13/224D06M15/3562D06M15/53D06M15/643D06M15/6436D06M16/00D06M2101/32
Inventor 韩建苏娟娟张斌
Owner ZHEJIANG SCI-TECH UNIV
Features
  • R&D
  • Intellectual Property
  • Life Sciences
  • Materials
  • Tech Scout
Why Patsnap Eureka
  • Unparalleled Data Quality
  • Higher Quality Content
  • 60% Fewer Hallucinations
Social media
Patsnap Eureka Blog
Learn More

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic, Popular Technical Reports.

© 2025 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap|About US| Contact US: help@patsnap.com