Matte aluminum-plated paper and preparation method thereof

An aluminized paper, matte technology, applied in the direction of paper, papermaking, paper coating, etc., can solve the problems of unstable printing adaptability, poor three-dimensional effect, rough paper surface, etc., and achieve easy recycling and printing adaptability Good, strong adhesion effect

Active Publication Date: 2016-09-07
上海睿途新材料科技有限公司
View PDF9 Cites 14 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

[0004] However, the paper produced by the existing process has a metallic texture, but the three-dimensional effect is not good, the surface of the paper is rough, not bright enough, the printing adaptability is unstable, the application range is narrow, and the cost is relatively high; in order to meet the market demand, it is planned to research and develop A dumb gold aluminized paper with stable performance and wide application range

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • Matte aluminum-plated paper and preparation method thereof
  • Matte aluminum-plated paper and preparation method thereof
  • Matte aluminum-plated paper and preparation method thereof

Examples

Experimental program
Comparison scheme
Effect test

preparation example Construction

[0043] The embodiment of the present invention provides a kind of preparation method of matte aluminized paper, and specific technological process is as follows figure 1 As shown, it specifically includes the following steps:

[0044] (1) Coating: Apply the matte transfer coating on the PET film by one-sided coating method, center the edge when coating, control the width of the edge on one side to be less than 0.5mm, and the dry coating amount is 1.45-1.55 g / m 2 , laminated to make a matte transfer film;

[0045] (2) Aluminum plating: The matte transfer film is vacuum aluminum coated on a vacuum aluminum coating machine, the vacuum degree is 0.2-0.3Pa, the temperature is -140°C to -160°C, and the thickness of the aluminum layer is controlled to be

[0046] (3) Composite: Coat the aluminum-plated matte transfer film with composite glue on a wet coating machine, and composite it with the backing paper. The wet coating amount is 7.5-8.5g / m 2 , composite drying; using the met...

Embodiment 1

[0056] The preparation of embodiment 1 matte aluminized paper specifically comprises the following steps:

[0057] (1) Prepare matte transfer coating: weigh 8 parts of acrylic resin, 12 parts of cellulose acetate butyrate, 40 parts of ethyl acetate, 2 parts of acetone, 14 parts of methyl ethyl ketone, 5 parts of n-propyl ester, ethanol 8 parts, 5 parts of butyl ester and 2 parts of butanol are placed in a reaction kettle, stirred at a constant speed of 1000-1200r / min, mixed evenly, and prepared into a coating slurry with a solid content of 18±0.5%, and then heated to 35°C, Add 2 parts of orange syrup and 4 parts of yellow syrup in the formula ratio, stir for 15 minutes, add 1.5 parts of matte powder, raise the temperature to 40°C, and stir for 2 hours to obtain a matte transfer coating with a viscosity of 20-30s;

[0058] (2) Coating: The matte transfer coating is coated on the PET film by one-side one-time coating, and the card edge is centered when coating, and the width of ...

Embodiment 2

[0062] The preparation of embodiment 2 matte aluminized paper specifically comprises the following steps:

[0063] (1) Prepare matte transfer coating: weigh 5 parts of acrylic resin, 9 parts of cellulose acetate butyrate, 40 parts of ethyl acetate, 5 parts of acetone, 16 parts of methyl ethyl ketone, 8 parts of n-propyl ester, ethanol Put 6 parts, 4 parts of butyl ester and 1 part of butanol in the reaction kettle, stir at a constant speed of 1200r / min, mix evenly, prepare a coating slurry with a solid content of 18±0.5%, then heat up to 40°C, add the formula 1 part of orange paste, 3 parts of yellow paste, after stirring for 15 minutes, add 1 part of matte powder, raise the temperature to 45°C, stir for 1.5 hours to obtain matte transfer coating with a viscosity of 20-30s;

[0064] (2) Coating: Apply the matte transfer coating on the PET film by one-sided coating method, center the card edge when coating, control the width of the card edge on one side to be less than 0.5mm, a...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

PropertyMeasurementUnit
Dry coataaaaaaaaaa
Thicknessaaaaaaaaaa
Thicknessaaaaaaaaaa
Login to View More

Abstract

The invention discloses a preparation method of matte aluminum-plated paper. The preparation method comprises the following steps of (1) coating: coating a PET (polyethylene glycol terephthalate) thin film with a matte transfer coating, so as to prepare a matte transfer film; (2) aluminum plating: performing vacuum aluminum plating on the matte transfer film by a vacuum aluminum plating machine, wherein the vacuum degree is 0.2 to 0.3Pa, the temperature is -140 to -160 DEG C, and the thickness of the aluminum layer is controlled to the value shown in the description; (3) compounding: coating the aluminum-plated matte transfer film with a composite glue on a wet coating machine, compounding with bottom paper, and coating the bottom paper with a back adhesive; (4) stripping: separating the compounded and cured aluminum-plated layer of a product from a substrate PET thin film on a stripping / coating dual-purpose machine, and transferring to the surface of the bottom paper, so as to obtain the matte aluminum-plated paper. The prepared matte aluminum-plated paper has the advantages that the color fusion of the paint film is avoided, the color phase is uniform, the printing suitability is good, the production effect is effectively improved, and the production cost is reduced.

Description

technical field [0001] The invention belongs to the field of composite packaging materials, and in particular relates to a matte aluminized paper and a preparation method thereof. Background technique [0002] Metallized packaging paper is mainly divided into: aluminum foil composite paper (first generation), 0.006mm aluminum foil and paper lamination, originated in the early 1990s, its disadvantages are that the aluminum layer and paper cannot be separated, and papermaking cannot be recycled, and the thickness of the aluminum layer is difficult Degradation; laminated paper (second generation), PET / OPP film is laminated with paper after spraying aluminum. It originated in the mid-1990s. Its disadvantage is that PET / OPP film cannot be separated from paper, and it can neither be recycled for paper making nor can it be degraded in soil ; Vacuum aluminum-coated paper (third generation), originated in the late 1990s, the thickness of the aluminum layer of vacuum metal-coated pape...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
IPC IPC(8): D21H19/82D21H19/84D21H25/06D21H19/38D21H19/44D21H19/46D21H19/52D21H19/58D21H19/08D21H23/64
CPCD21H19/08D21H19/38D21H19/44D21H19/46D21H19/52D21H19/58D21H19/828D21H19/84D21H23/64D21H25/06
Inventor 张华翟云飞
Owner 上海睿途新材料科技有限公司
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Patsnap Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Patsnap Eureka Blog
Learn More
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic, Popular Technical Reports.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap|About US| Contact US: help@patsnap.com