Preparation method of pleonaste-containing artificial stone

A spinel and artificial stone technology, which is applied in the preparation of alkaline earth metal aluminate/alumina/aluminum hydroxide, magnesium aluminate, etc., can solve the problems of poor flame retardancy and heat resistance, poor surface gloss, surface resistance Improve the anti-aging performance, optimize the charcoal performance, and improve the flame retardant performance

Active Publication Date: 2016-09-21
佛山市阿德曼特科技有限公司
View PDF3 Cites 0 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

However, the current artificial stone still has the disadvantages of low strength, poor surface abrasion resistance, weak flame retardancy and heat resistance, and poor surface gloss.

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0018] (1) Preparation of composite magnesium iron spinel MgAl 2 o 4 / ZIF-90:

[0019] (a)MgAl 2 o 4 Preparation: weigh 0.02molMg(NO 3 ) 2 · 6H 2 O, 0.04molAl(NO 3 ) 3 9H 2 O was dissolved in 50ml of deionized edema to prepare a mixed salt solution. Take 0.04molNa2CO3 and 0.06molNaOH and dissolve them in 50ml of deionized water, then stir rapidly, add the salt solution to the alkali solution, keep the pH at 9-11, mix well, and The precipitate was filtered and washed with deionized water until neutral. Dry in an oven at 80°C for 8 hours. Then bake in a muffle furnace at 800°C for 4-6h.

[0020] (b) Preparation of ZIF-90: Zn(NO 3 ) 2 6H 2 O (2.1mmol) and imidazole-2-carboxaldehyde ICA (3.0mmol) were dissolved in 30mL of DMF and stirred evenly. The resulting reaction solution was transferred to a 40mL polytetrafluoroethylene-lined reactor and reacted at 100°C for 18h and naturally cooled. to room temperature for later use;

[0021] (c) MgAl 2 o 4 Add it into t...

Embodiment 2

[0024] (1) Preparation of composite magnesium iron spinel MgAl 2 o 4 / ZIF-90:

[0025] (a)MgAl 2 o 4Preparation: Weigh 0.02molMg(NO3)2 6H2O and 0.04molAl(NO3)3 9H2O and dissolve them in 50ml of deionized edema respectively to obtain a mixed salt solution. Take 0.04molNa2CO3 and 0.06molNaOH and dissolve them in 50ml of deionized water, and then stir rapidly. Add the salt solution to the alkaline solution to keep the pH at 9-11, mix well, filter the precipitate, and wash with deionized water until neutral. Dry in an oven at 100°C for 10 hours. Then it was fired in a muffle furnace at 800°C for 4h.

[0026] (b) Preparation of ZIF-90: Zn(NO 3 ) 2 · 6H 2 O (2.1mmol) and imidazole-2-carboxaldehyde ICA (3.0mmol) were dissolved in 30mL of DMF and stirred evenly. The resulting reaction solution was transferred to a 40mL polytetrafluoroethylene-lined reactor and reacted at 100°C for 18h and naturally cooled. to room temperature for later use;

[0027] (c) MgAl 2 o 4 Add it i...

Embodiment 3

[0030] (1) Preparation of composite magnesium iron spinel MgAl 2 o 4 / ZIF-90:

[0031] (a)MgAl 2 o 4 Preparation: weigh 0.02molMg(NO3) respectively 2 6H 2 O, 0.04molAl(NO 3 )3 9H2O was dissolved in 50ml of deionized edema to prepare a mixed salt solution. Take 0.04molNa2CO3 and 0.06molNaOH and dissolve them in 50ml of deionized water, then stir rapidly, add the salt solution to the alkali solution, keep the pH at 9-11, and mix well , filter the precipitate, and wash with deionized water until neutral. Dry in an oven at 80°C for 10 hours. Then it was fired in a muffle furnace at 800°C for 6h.

[0032] (b) Preparation of ZIF-90: Zn(NO 3 ) 2 6H 2 O (2.1mmol) and imidazole-2-carboxaldehyde ICA (3.0mmol) were dissolved in 30mL of DMF and stirred evenly. The resulting reaction solution was transferred to a 40mL polytetrafluoroethylene-lined reactor and reacted at 100°C for 18h and naturally cooled. to room temperature for later use;

[0033] (c) MgAl 2 o 4 Add it in...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

No PUM Login to View More

Abstract

The invention relates to a preparation method of pleonaste-containing artificial stone. The nano magnesia alumina spinel MgAl2O4 has the special structure, and can be added into talcum powder / phenolic resin / quartz as a high-grade inorganic nano oxide material to enhance the heat resistance and strength of the artificial stone and shorten the aging time of the artificial stone. The nano magnesia alumina spinel MgAl2O4 can keep undegraded for a long time under the action of high temperature, can keep favorable flame-retardant effects, increases the carbon residue quantity, and greatly enhances the LOI (loss on ignition) index.

Description

technical field [0001] The invention relates to a method for preparing artificial stone containing nano-magnesium-aluminum spinel, which belongs to the field of building materials. Background technique [0002] With the improvement of people's living standards and living conditions, the interior decoration industry is developing rapidly, and the amount of decoration building materials is huge. Among them, stone is one of the most commonly used and most basic building materials, widely used in floors, walls and The paving of the countertop. The mining cost of natural stone is high, the pollution is large, and it contains a large amount of natural radioactive substances, which is harmful to human health. With the continuous development of the material field, the performance of artificial stone has gradually improved, approaching or even surpassing natural stone, and it is more and more accepted by the market and users, and is widely used in cabinets, bathrooms, floors, and wa...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
Patent Type & Authority Applications(China)
IPC IPC(8): C08L61/06C08L87/00C08K13/02C08K3/22C08K3/34C08K3/38C08K3/36C08K5/3492C08K3/32C08K5/521C08G83/00C01F7/16
CPCC01F7/162C04B26/122C04B2201/50C08G83/008C08K2201/011C08L61/06C08L2201/02C08L2201/08C08L2201/14C08L87/00C08K13/02C08K2003/2227C08K3/34C08K3/38C08K3/36C08K5/34922C08K2003/325C08K5/521C04B14/042C04B22/0013C04B14/06C04B14/18C04B24/128C04B24/003C04B14/366C04B14/20C04B14/36C04B22/085
Inventor 骆佳豪
Owner 佛山市阿德曼特科技有限公司
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Patsnap Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Patsnap Eureka Blog
Learn More
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic, Popular Technical Reports.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap|About US| Contact US: help@patsnap.com