Self-repair reaction type polymer cement waterproof coating and method for preparing same

A waterproof coating and polymer technology, which is applied in the field of architectural waterproof coatings, can solve problems such as coating leakage, deformation and cracking of the base layer, and achieve the effects of reducing harsh requirements, improving utility, and facilitating technical solutions

Active Publication Date: 2016-09-28
浙江鲁班建筑防水有限公司
View PDF6 Cites 15 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

[0006] In order to solve the leakage problem after the coating is cracked due to the deformation and cracking of the base layer, the first purpose of the present invention is to provide a self-repairing reactive polymer cement waterproof coating

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0028] The proportion of each component of the raw materials of the self-repairing polymer cement waterproof coating of the present invention is as follows:

[0029] Polyurethane liquid material 41%

[0030] Cement 25%

[0031] Filler 20%

[0032] Microcapsule material 14%

[0033] Formulation of microcapsule material:

[0034] Activated silica powder 16.

[0035] High aluminate cement 67

[0036] Propylene glycol 16

[0037] gum arabic 1

[0038] The preparation method of the above-mentioned self-repairing polymer cement waterproof coating is as follows:

[0039] 1) Dissolve gum arabic in propylene glycol, and adjust the amount of solvent according to the viscosity;

[0040] 2) The core material of the microcapsules is mixed evenly with activated silica powder and high aluminate cement in a ratio of 2:8;

[0041] 3) The wall material and core material enter the fluidized bed coater at a ratio of 1:5-6 respectively, and enter the solvent collector after sieving, and d...

Embodiment 2

[0050] The ratio of each component of the raw materials of the self-repairing polymer cement waterproof coating that can be used in the present invention is as follows:

[0051] Polyurethane liquid material 36%

[0052] Cement 28%

[0053] Filler 23%

[0054] Microcapsule material 13%

[0055] Formulation of microcapsule material:

[0056] Activated silica powder 16.

[0057] High aluminate cement 67

[0058] Propylene glycol 16

[0059] gum arabic 1

[0060] The preparation method of the above-mentioned self-repairing polymer cement waterproof coating is as follows

[0061] The preparation method of the above-mentioned self-repairing polymer cement waterproof coating is as follows:

[0062] 1) Dissolve gum arabic in propylene glycol, and adjust the amount of solvent according to the viscosity;

[0063] 2) The wrapped core material is mixed evenly with activated silica powder and high aluminate cement in a ratio of 4:6;

[0064] 3) Enter the fluidized bed coater respec...

Embodiment 3

[0072] The ratio of each component of the raw materials of the self-repairing polymer cement waterproof coating that can be used in the present invention is as follows:

[0073] Epoxy resin liquid material 45%

[0074] Cement 17%

[0075] Filler 26%

[0076] Microcapsule material 12%

[0077] Formulation of microcapsule material:

[0078] Activated silica powder 16

[0079] High aluminate cement 67

[0080] Propylene glycol 16

[0081] gum arabic 1

[0082] The preparation method of the above-mentioned self-repairing polymer cement waterproof coating is as follows

[0083] The preparation method of the above-mentioned self-repairing polymer cement waterproof coating is as follows:

[0084] 1) Dissolve the gum arabic in a solvent, and adjust the amount of solvent according to the viscosity;

[0085] 2) The wrapped core material is mixed evenly with activated silica powder and high aluminate cement in a ratio of 2:8;

[0086] 3) Enter the fluidized bed coater respectiv...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

PropertyMeasurementUnit
tensile strengthaaaaaaaaaa
tensile strengthaaaaaaaaaa
tensile strengthaaaaaaaaaa
Login to View More

Abstract

The invention discloses self-repair reaction type polymer cement waterproof coating and a method for preparing the same. The self-repair reaction type polymer cement waterproof coating comprises double components including liquid and powder, and particularly comprises, by weight, 35-50% of polymer liquid, 15-30% of cement, 10-30% of powdery fillers and 5-15% of micro-capsule materials on the basis of the total weight of 100%. According to the technical scheme, the self-repair reaction type polymer cement waterproof coating and the method have the advantages that water absorption materials with swelling properties wrap materials with quick curing and gelating properties by the aid of micro-capsule technologies, the materials with the quick curing and gelating properties can be uniformly dispersed in the self-repair reaction type polymer cement waterproof coating, capsules inside the self-repair reaction type polymer cement waterproof coating can be exposed from fracture when the self-repair reaction type polymer cement waterproof coating is broken by base layers by means of drawing, the water absorption wall materials of the self-repair reaction type polymer cement waterproof coating can be softened, swollen and broken after absorbing water, internal repair materials can flow out and can be quickly cured and gelated when in contact with the water, accordingly, crack can be blocked, self-repair effects can be conveniently, easily, timely and automatically realized without influence on the quality of polymers in the self-repair reaction type polymer cement waterproof coating and the performance of the self-repair reaction type polymer cement waterproof coating, and the self-repair reaction type polymer cement waterproof coating and the method are applicable to polyurethane, acrylic acid and epoxy polymers.

Description

technical field [0001] The invention belongs to the field of architectural waterproof coatings, in particular to a self-repairing reactive polymer cement waterproof coating and a preparation method thereof. Background technique [0002] Waterproof coating The waterproof film formed by the coating on the base layer after curing has certain strength, good extensibility, crack resistance, impermeability and weather resistance, and has good temperature adaptability, easy operation and easy maintenance. and maintenance. Compared with the waterproof membrane, the waterproof coating has strong adaptability to the base layer, and the waterproof layer has no seams, which is more reliable. Due to the above characteristics, waterproof coating is one of the main waterproof materials often used in waterproofing projects. [0003] Reactive polymer cement waterproof coating, as an improved variety of polymer cement waterproof coating, is a high-solid content coating that reacts and solid...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
Patent Type & Authority Applications(China)
IPC IPC(8): C09D175/04C09D163/00C09D7/12
CPCC08K3/24C08K3/34C08K3/36C08K9/10C08K13/06C09D7/61C09D7/62C09D163/00C09D175/04
Inventor 杨杨项晓睿周振哲魏红超
Owner 浙江鲁班建筑防水有限公司
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Eureka Blog
Learn More
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic, Popular Technical Reports.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap|About US| Contact US: help@patsnap.com