A kind of transparent solvent-free one-component waterproof coating and preparation method thereof

A waterproof coating, solvent-free technology, applied in the direction of polyurea/polyurethane coatings, coatings, etc., can solve the problems of entering human blood through the suction tract or skin, lack of human body mechanisms, etc., to achieve good waterproof effect and prolong service life. Effect

Active Publication Date: 2018-11-27
河北朴智伟业防水材料有限公司
View PDF4 Cites 0 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

However, inorganic pigments are pigments extracted from minerals, which contain chemical elements such as selenium, cadmium, and chromium. If the human body takes a long-term intake or works in such an environment for a long time, elements such as selenium and cadmium can easily enter through the respiratory tract or skin. Human blood, resulting in the absence or failure of human mechanisms

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • A kind of transparent solvent-free one-component waterproof coating and preparation method thereof
  • A kind of transparent solvent-free one-component waterproof coating and preparation method thereof

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0038] In order to solve the problem that low-grade coal tar, asphalt, coumarone and other petroleum products are added to existing waterproof coatings, which first seriously pollute the environment and endanger human health, and secondly produce products with poor quality and are easy to counterfeit. The present invention provides a transparent solvent-free The one-component polyurethane waterproof coating comprises the following raw materials in parts by weight:

[0039] Combined polyether polyol: 30-45 parts; isocyanate: 10 parts; polymerization inhibitor: 0.01 part; plasticizer: 10 parts; wetting and dispersing agent: 0.1 part; catalyst: 0.04 part; There are no solid pigments and no solvents of any kind in the described protocol.

[0040] The combined polyether polyol described in the present invention is a mixture of polyether triol 330N, polyether PZ-200 and polyether diol 1000D; the hydroxyl value of the polyether triol 330N is 32.5-35.5 mgKOH / g; the hydroxyl value of ...

Embodiment 2

[0059] A transparent solvent-free one-component polyurethane waterproof coating, comprising the following raw materials in parts by weight:

[0060] Combined polyether polyol: 40 parts; isocyanate: 15 parts; polymerization inhibitor: 0.015 parts; plasticizer: 15 parts; wetting and dispersing agent: 0.15 parts; catalyst: 0.06 parts; carbon dioxide inhibitor: 0.2 parts. There are no solid pigments and no solvents of any kind in the described protocol.

[0061] The combined polyether polyol described in the present invention is a mixture of polyether triol 330N, polyether PZ-200 and polyether diol 1000D; the hydroxyl value of the polyether triol 330N is 32.5-35.5 mgKOH / g; the hydroxyl value of the polyether PZ-200 is 53.5-58.5mgKOH / g; the hydroxyl value of the polyether diol 1000D is 109-115mgKOH / g;

[0062] Polyether PZ-200 is obtained by modifying low-molecular-weight polyether and a curing agent containing -NCO groups, and its functionality is 2.

[0063] The isocyanate is o...

Embodiment 3

[0071] In order to solve the problem that low-grade coal tar, asphalt, coumarone and other petroleum products are added to existing waterproof coatings, which first seriously pollute the environment and endanger human health, and secondly produce products with poor quality and are easy to counterfeit. The present invention provides a transparent solvent-free The one-component polyurethane waterproof coating comprises the following raw materials in parts by weight:

[0072] Combined polyether polyol: 45 parts; isocyanate: 20 parts; polymerization inhibitor: 0.02 parts; plasticizer: 20 parts; wetting and dispersing agent: 0.2 parts; catalyst: 0.08 parts; carbon dioxide inhibitor: 0.3 parts. There are no solid pigments and no solvents of any kind in the described protocol.

[0073] The combined polyether polyol described in the present invention is a mixture of polyether triol 330N, polyether PZ-200 and polyether diol 1000D; the hydroxyl value of the polyether triol 330N is 32.5-...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

PUM

PropertyMeasurementUnit
hydroxyl valueaaaaaaaaaa
hydroxyl valueaaaaaaaaaa
hydroxyl valueaaaaaaaaaa
Login to view more

Abstract

The invention provides a transparent solvent-free single-component waterproof paint and a preparation method thereof. The transparent solvent-free single-component waterproof paint comprises the following raw materials in parts by weight: 30-45 parts of combined polyether polyol, 10-20 parts of isocyanate, 0.01-0.02 parts of a polymerization inhibitor, 10-20 parts of a plasticizer, 0.1-0.2 parts of a wetting dispersant, 0.04-0.08 parts of a catalyst, and 0.1-0.3 parts of a carbon dioxide inhibitor. According to the invention, the environmental protection raw materials substitute toxic solvents, a reaction-type antifoaming agent is employed for preparing the high-solid content environment-friendly type transparent solvent-free single-component waterproof paint, and the waterproof paint has the advantages of excellent coating performance, low cost, safety, environmental protection, and non pollution.

Description

technical field [0001] The invention relates to a transparent one-component polyurethane waterproof coating and a preparation method thereof. Background technique [0002] The transparent one-component polyurethane waterproof coating is made of polyether polyol and isocyanate as the main raw materials together with special additives and plasticizers through polymerization reaction. After the coating is painted, it reacts with moisture in the environment to form a layer Tough, seam-free waterproof protective film with excellent comprehensive performance. Because of its advantages of simple construction and good mechanical properties, it has become the development direction of polyurethane waterproof coatings. [0003] The transparent one-component polyurethane waterproof coating is still blank in China. The bottleneck encountered is how to make the film without air bubbles and make its mechanical properties meet the requirements of the national standard; secondly, the cost i...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

Application Information

Patent Timeline
no application Login to view more
Patent Type & Authority Patents(China)
IPC IPC(8): C09D175/08C09D7/63C09D7/65C08G18/48
CPCC08G18/4812C09D7/40C09D175/08
Inventor 杨飞籍姣青周传强牛泽斌
Owner 河北朴智伟业防水材料有限公司
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Try Eureka
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap