Falling-off-preventing metal coating and preparation method thereof

A metal coating and anti-shedding technology, applied in the direction of coatings, anti-corrosion coatings, etc., can solve the problems of poor adhesion, easy peeling of coatings, etc., and achieve the effect of preventing metal from rusting and oxidation

Inactive Publication Date: 2016-10-26
WUXI EPIC TECH
View PDF5 Cites 6 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

But the coating is easy to peel off and has poor adhesion to metal

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0017] Anti-shedding metal coating, including the following raw materials in parts by weight: 15 parts of polyether silicate, 25 parts of γ-valerolactone, 50 parts of 2-ethyl-1,6-hexanediol, 30 parts of zinc, oxide 15 parts of calcium, 3 parts of rust inhibitor, 110 parts of nano silicon dioxide, 60 parts of nano titanium dioxide, 40 parts of thiourea, 25 parts of diammonium hydrogen phosphate, 45 parts of water.

[0018] The antirust agent is a silane coupling antirust agent.

[0019] The preparation method of the above-mentioned anti-shedding metal coating comprises the following steps: polyether silicate, γ-valerolactone, 2-ethyl-1,6-hexanediol, zinc, calcium oxide, rust inhibitor, sulfur After mixing urea, diammonium hydrogen phosphate, and water evenly, add nano-silicon dioxide and nano-titanium dioxide, coat the metal surface after degreasing annealing and borax treatment, dry at 1300-1500°C for 30-40 minutes, and then dry at 900-1000 ℃ sintering for 2 to 3 minutes, tha...

Embodiment 2

[0021] Anti-shedding metal coating, including the following raw materials in parts by weight: 10 parts of polyether silicate, 20 parts of γ-valerolactone, 40 parts of 2-ethyl-1,6-hexanediol, 10 parts of zinc, oxide 10 parts of calcium, 2 parts of antirust agent, 100 parts of nano silicon dioxide, 50 parts of nano titanium dioxide, 10 parts of thiourea, 20 parts of diammonium hydrogen phosphate, 40 parts of water.

[0022] The antirust agent is a polyol ester antirust agent.

[0023] The preparation method of the above-mentioned anti-shedding metal coating comprises the following steps: polyether silicate, γ-valerolactone, 2-ethyl-1,6-hexanediol, zinc, calcium oxide, rust inhibitor, sulfur After mixing urea, diammonium hydrogen phosphate, and water evenly, add nano-silicon dioxide and nano-titanium dioxide, coat the metal surface after degreasing annealing and borax treatment, dry at 1300-1500°C for 30-40 minutes, and then dry at 900-1000 ℃ sintering for 2 to 3 minutes, that i...

Embodiment 3

[0025] Anti-shedding metal coating, including the following raw materials in parts by weight: 20 parts of polyether silicate, 30 parts of γ-valerolactone, 60 parts of 2-ethyl-1,6-hexanediol, 50 parts of zinc, oxide 20 parts of calcium, 5 parts of rust inhibitor, 120 parts of nano silicon dioxide, 80 parts of nano titanium dioxide, 60 parts of thiourea, 30 parts of diammonium hydrogen phosphate, and 50 parts of water.

[0026] The antirust agent is a silane coupling antirust agent.

[0027] The preparation method of the above-mentioned anti-shedding metal coating comprises the following steps: polyether silicate, γ-valerolactone, 2-ethyl-1,6-hexanediol, zinc, calcium oxide, rust inhibitor, sulfur After mixing urea, diammonium hydrogen phosphate, and water evenly, add nano-silicon dioxide and nano-titanium dioxide, coat the metal surface after degreasing annealing and borax treatment, dry at 1300-1500°C for 30-40 minutes, and then dry at 900-1000 ℃ sintering for 2 to 3 minutes,...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

PropertyMeasurementUnit
thicknessaaaaaaaaaa
Login to View More

Abstract

The invention discloses a falling-off-preventing metal coating and a preparation method thereof. The falling-off-preventing metal coating comprises raw materials in parts by weight as follows: 10-20 parts of polyether silicate ester, 20-30 parts of gamma-valerolactone, 40-60 parts of 2-ethyl-1,6-hexanediol, 10-50 parts of zinc, 10-20 parts of calcium oxide, 2-5 parts of an anti-rusting agent, 100-120 parts of nano-silica, 50-80 parts of nano-titania, 10-60 parts of thiourea, 20-30 parts of diammonium hydrogen phosphate and 40-50 parts of water. The preparation method of the falling-off-preventing metal coating comprises steps as follows: polyether silicate ester, gamma-valerolactone, 2-ethyl-1,6-hexanediol, zinc, calcium oxide, the anti-rusting agent, thiourea, diammonium hydrogen phosphate and water are mixed uniformly, then the remaining components are added, and a metal surface subjected to deoiling, annealing and borax processing is coated with an obtained solution and is dried and sintered. The coating can be effectively attached to the metal surface, thereby preventing metal from rusting and oxidation.

Description

technical field [0001] The invention relates to an anti-shedding metal coating and a preparation method thereof. Background technique [0002] Coating is a solid continuous film obtained by one application of paint. It is a thin plastic layer coated on metal, fabric, plastic and other substrates for the purpose of protection, insulation and decoration. The paint can be gaseous, liquid, or solid, and the type and state of the paint are usually determined according to the substrate to be sprayed. [0003] The Chinese patent application with the application number CN201410411117.9 discloses a method of arc spraying an aluminum-based corrosion-resistant metal coating on a steel structure. The aluminum-based corrosion-resistant metal coating is an aluminum-nickel composite metal coating. The spraying method It includes the following steps: (1) substrate surface pretreatment; (2) substrate surface spraying metal coating; (3) metal coating sealing treatment. Through the above m...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
Patent Type & Authority Applications(China)
IPC IPC(8): C09D1/00C09D5/08
CPCC09D1/00C09D5/08
Inventor 尤为
Owner WUXI EPIC TECH
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Patsnap Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Patsnap Eureka Blog
Learn More
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic, Popular Technical Reports.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap|About US| Contact US: help@patsnap.com