Welding flux for molten salt corrosion resistant nickel-base superalloy fusion welding

A nickel-based superalloy and molten salt corrosion technology, applied in the direction of welding/cutting medium/material, welding medium, welding equipment, etc., can solve the problems of increased sensitivity of weld cracks, achieve improved inclusions, low crack sensitivity, Effect of high elongation at break

Active Publication Date: 2016-11-09
SHANGHAI INST OF APPLIED PHYSICS - CHINESE ACAD OF SCI
View PDF5 Cites 18 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

[0003] Usually, in order to ensure that the high-temperature nickel-based alloy has the same molten salt corrosion resistance as the base metal, the main constituent elements of the solder must remain the same as the base metal, but due to the high content of Mo and Cr in the molten-salt corrosion-resistant nickel-based superalloy, The toughness of the weld will be lower than that of the base metal, resulting in increased weld crack susceptibility

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • Welding flux for molten salt corrosion resistant nickel-base superalloy fusion welding
  • Welding flux for molten salt corrosion resistant nickel-base superalloy fusion welding
  • Welding flux for molten salt corrosion resistant nickel-base superalloy fusion welding

Examples

Experimental program
Comparison scheme
Effect test

Embodiment Construction

[0026] The technical scheme of the present invention is described in detail below in conjunction with accompanying drawing:

[0027] In order to meet the safety and reliability of welded structural parts for molten salt stacking, the present invention proposes a solder for molten salt corrosion-resistant nickel-based superalloy fusion welding, and its components (percentage by weight) are specifically as follows:

[0028] The content of C is controlled between 0.03% and 0.06%, preferably between 0.05% and 0.06%, and C within this range makes the weld seam have better strength and toughness matching. The higher the C content, the strength of the weld will increase, but the plasticity will decrease accordingly. In addition, if the C content is too large, a large number of carbides will be formed in the weld, which will reduce the stability of the weld structure. If the carbon content is too low, It will reduce the strength of the weld.

[0029] The content of Mn is controlled b...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

PropertyMeasurementUnit
tensile strengthaaaaaaaaaa
yield strengthaaaaaaaaaa
tensile strengthaaaaaaaaaa
Login to View More

Abstract

The invention discloses a welding flux formolten salt corrosion resistant nickel-base superalloy fusion welding and belongs to the technical field of welding materials. The welding flux comprises the following components in percentage by weight: 0.03%-0.06% of C, 0.04%-0.10% of Mn, 0.3%-0.5% of Si, not greater than 0.10% of Cu, not greater than 0.20% of Co, not greater than 0.015% of P, not greater than 0.015% of S, 0.01%-0.05% of rare earth element, 1.0%-5.0% of Fe, 6.0%-8.0% of Cr, 12.0%-18.0% of Mo, not greater than 0.3% of Al, not greater than 0.2% of Ti, 1.0%-2.0% of Nb and the balance of Ni, wherein Ti+Nb+Al is not greater than 2%. The invention also discloses a welding material for molten salt corrosion resistant nickel-base superalloy fusion welding, a connecting method of a molten salt corrosion resistant nickel-base superalloy and a structural member of the molten salt corrosion resistant nickel-base superalloy. According to the welding flux for molten salt corrosion resistant nickel-base superalloy fusion welding, the toughness and the oxidation resistance of a welded joint can be effectively improved, the excellent molten salt corrosion resistance and the excellent high temperature mechanical property can be guaranteed, the usage demands of molten salt and radiation environments with high usage temperature and performance requirements can be satisfied, and the welding flux is suitable for welding of a molten salt reactor structural material.

Description

technical field [0001] The invention relates to the technical field of welding materials, in particular to a solder used for fusion welding of nickel-based superalloys resistant to molten salt corrosion. Background technique [0002] The molten salt reactor belongs to the fourth generation nuclear energy system, which has a series of unique advantages, including high inherent safety, flexible fuel cycle characteristics, availability of thorium-based fuel, and prevention of nuclear proliferation. However, due to the use of molten salt as the coolant, the structural materials of the molten salt reactor must be resistant to molten salt corrosion, high temperature and radiation interaction. Foreign alloys resistant to molten salt corrosion are mainly Hastelloy N alloys, and my country has also studied the corresponding domestic high-temperature nickel-based alloy-GH3535. In order to ensure that the welded structure has reliable high-temperature strength and has high-temperature...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
Patent Type & Authority Applications(China)
IPC IPC(8): B23K35/30
CPCB23K35/3033
Inventor 黎超文李志军蒋力玉昆陈双建梁建平
Owner SHANGHAI INST OF APPLIED PHYSICS - CHINESE ACAD OF SCI
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Patsnap Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Patsnap Eureka Blog
Learn More
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic, Popular Technical Reports.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap|About US| Contact US: help@patsnap.com