Method for forming structural color metal surface based on blazed grating structure through grinding with grinding wheel

A blazed grating and metal surface technology, which is applied to machine tools, grinding/polishing equipment, and metal processing equipment suitable for grinding workpiece planes, can solve problems such as large flow resistance, weak corrosion resistance, and poor hydrophobicity, and achieve Good hydrophobicity, low fluid flow resistance, and strong corrosion resistance

Inactive Publication Date: 2016-11-09
ZHEJIANG UNIV OF TECH
View PDF4 Cites 0 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

[0005] In order to overcome the deficiencies of the existing metal surface treatment process, such as no structural color, poor hydrophobicity, weak corrosion resistance, and large flow resistance, the present invention provides a structurally colored metal surface formed by grinding wheel grinding based on a blazed grating structure Methods

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • Method for forming structural color metal surface based on blazed grating structure through grinding with grinding wheel
  • Method for forming structural color metal surface based on blazed grating structure through grinding with grinding wheel

Examples

Experimental program
Comparison scheme
Effect test

Embodiment Construction

[0016] The present invention will be further described below in conjunction with embodiment.

[0017] A method for grinding and forming a structured color metal surface based on a blazed grating structure, comprising the following steps:

[0018] (1) Smooth the surface of the metal workpiece so that the surface roughness does not exceed 100nm;

[0019] (2) Use a grinding wheel to grind a specific set of parallel grooves on the surface of the metal workpiece according to specific process parameters.

[0020] The processing object of the inventive method is a metal workpiece made of cemented carbide (such as abrasive tool steel, titanium alloy, etc.); the grinding relevant process parameters in the step (2) of the inventive method are as follows: the selection specification for grinding is grinding Choose a grinding wheel with a diamond particle size of 1000#-8000# and a resin bonded abrasive with a concentration of 100%-150%. When grinding, the angle between the grinding wheel...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

No PUM Login to View More

Abstract

A method for forming a structural color metal surface based on a blazed grating structure through grinding with a grinding wheel comprises the following steps that (1) the surface of a metal workpiece is flattened, so that the surface roughness of the metal workpiece does not exceed 100 nm, and the metal workpiece is made of cemented carbide; and (2) the grinding wheel is used for grinding a parallel groove set in the surface of the metal workpiece according to set process parameters; the process parameters are shown as follows: the included angle between the grinding wheel and the surface of the workpiece is 5-30 degrees, the rotating speed of the grinding wheel is 1000-3000 rpm, the feed speed is 20-100 mm / min, and the grinding depth is 1-5 microns; and once grinding of a groove is completed, the grinding wheel is shifted by 3-20 microns relative to the workpiece, and grinding of the next groove is conducted. The metal surface formed through the method is of a specific micro structure and can not only show structural color as a blazed grating but also have better hydrophobicity compared with the pre-machined surface, thereby having higher corrosion resistant ability and lower fluid flow resistance.

Description

technical field [0001] The invention relates to the field of metal surface finishing, in particular to a method for grinding and shaping a structural color metal surface based on a blazed grating structure with a grinding wheel. Background technique [0002] For decorative purposes, changing the color of metal appearance at this stage relies on dyes. Dyeing with dyes will not only cause environmental pollution, but also easily fade and fade (especially when encountering certain chemical reagents). It can be seen that it is of great significance to study how to overcome the above-mentioned disadvantages or deficiencies in dyeing. [0003] Structural color, also known as physical color, is a luster caused by the wavelength of light and has nothing to do with pigment coloring. It will not fade or fade even when it encounters chemical reagents. It can be seen that if a microstructure capable of showing structural color can be processed on the metal surface, and the metal surfa...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
Patent Type & Authority Applications(China)
IPC IPC(8): B24B7/16B44C5/00
CPCB24B7/16B44C5/00
Inventor 吕冰海翁海舟邓乾发邵琦戴伟涛陈正华杭伟
Owner ZHEJIANG UNIV OF TECH
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Patsnap Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Patsnap Eureka Blog
Learn More
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic, Popular Technical Reports.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap|About US| Contact US: help@patsnap.com