Multifunctional plastic promoter and preparation method thereof

A plastic additive and multi-functional technology, applied in the field of multi-functional plastic additive and its preparation, can solve the problems of no anti-oxidation function, electrostatic leakage, inability to facilitate plastic demolding, etc., and achieve good molding effect and convenient demoulding. Modular, easy-to-save effects

Inactive Publication Date: 2016-11-09
WUHU TIANXIONG NEW MATERIAL TECH
View PDF3 Cites 8 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

[0004] At present, the existing plastic additives do not have anti-oxidation function, cannot make static electricity leak in time, and cannot facilitate the demoulding of plastics

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0021] A multifunctional plastic additive, made of the following raw materials in parts by weight: 18 parts of dioctyl phthalate, 10 parts of butyl benzyl phthalate, 8 parts of dibutyl phthalate, 13 parts of phosphite, 10 parts of mercapto ester, 6 parts of mica powder, 8 parts of quartz powder, 4 parts of carbon fiber, 2 parts of trioctyl ester, 10 parts of benzotriazole, 20 parts of salicylate, 4 parts of aluminum hydroxide 6 parts, 6 parts of nano titanium dioxide, 13 parts of ethoxylated alkyl polyamine, 17 parts of alkyl trimethyl quaternary ammonium, 5 parts of ethoxylated lauryl amide, 2 parts of 8-hydroxyquinoline copper, 13 parts of sodium fluoride 2 parts and 2 parts of methyl silicone oil.

[0022] A preparation method of multifunctional plastic additives, comprising the following steps:

[0023] 1) Mix 18 parts of dioctyl phthalate, 10 parts of butyl benzyl phthalate, 8 parts of dibutyl phthalate, 13 parts of phosphite, 10 parts of mercapto ester, 6 parts of mica ...

Embodiment 2

[0031] A multifunctional plastic additive, made of the following raw materials in proportions by weight: 21.5 parts of dioctyl phthalate, 12.5 parts of butyl benzyl phthalate, 9 parts of dibutyl phthalate, 14 parts of phosphite, 12.5 parts of mercapto ester, 8 parts of mica powder, 10.5 parts of quartz powder, 5.5 parts of carbon fiber, 3 parts of trioctyl ester, 12.5 parts of benzotriazole, 22.5 parts of salicylate, 7 parts of aluminum hydroxide 7.5 parts of nano titanium dioxide, 14.5 parts of ethoxylated alkylpolyamine, 18.5 parts of alkyl trimethyl quaternary ammonium, 7.5 parts of ethoxylated lauryl amide, 3 parts of 8-hydroxyquinoline copper, 15 parts of sodium fluoride 4 parts and 4 parts of methyl silicone oil.

[0032] A preparation method of multifunctional plastic additives, comprising the following steps:

[0033] 1) Mix 21.5 parts of dioctyl phthalate, 12.5 parts of butyl benzyl phthalate, 9 parts of dibutyl phthalate, 14 parts of phosphite, 12.5 parts of mercapt...

Embodiment 3

[0041] A multifunctional plastic additive, made of the following raw materials in proportions by weight: 25 parts of dioctyl phthalate, 15 parts of butyl benzyl phthalate, 10 parts of dibutyl phthalate, 15 parts of phosphite, 15 parts of mercapto ester, 10 parts of mica powder, 13 parts of quartz powder, 7 parts of carbon fiber, 4 parts of trioctyl ester, 15 parts of benzotriazole, 25 parts of salicylate, 10 parts of aluminum hydroxide 9 parts of nano titanium dioxide, 16 parts of ethoxylated alkylpolyamine, 20 parts of alkyl trimethyl quaternary ammonium, 10 parts of ethoxylated lauryl amide, 4 parts of 8-hydroxyquinoline copper, 17 parts of sodium fluoride 6 parts and 6 parts of methyl silicone oil.

[0042] A preparation method of multifunctional plastic additives, comprising the following steps:

[0043] 1) Mix 25 parts of dioctyl phthalate, 15 parts of butyl benzyl phthalate, 10 parts of dibutyl phthalate, 15 parts of phosphite, 15 parts of mercapto ester, 10 parts of mi...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

PUM

No PUM Login to view more

Abstract

The invention discloses a multifunctional plastic promoter. The multifunctional plastic promoter is prepared from the following raw materials in parts by weight: 18-25 parts of dioctyl phthalate, 10-15 parts of butyl benzyl phthalate, 8-10 parts of dibutyl phthalate, 13-15 parts of phosphite, 10-15 parts of mercaptan acid ester, 6-10 parts of mica powder, 8-13 parts of quartz powder, 4-7 parts of carbon fibers, 2-4 parts of trioctyl, 10-15 parts of benzotriazole, 20-25 parts of salicylate, 4-10 parts of aluminum hydroxide, 6-9 parts of nano-titanium dioxide, 13-16 parts of alkylpolyamine ethoxylate, 17-20 parts of alkyl trimethyl ammonium, 5-10 parts of ethyoxyl lauramide, 2-4 parts of copper 8-hydroxyquinoline, 13-17 parts of sodium fluoride and 2-6 parts of methylsilicone oil. The multifunctional plastic promoter has an antioxidation function, can be used for timely leaking static electricity, and is beneficial to demolding of plastics.

Description

technical field [0001] The invention relates to a multifunctional plastic additive and a preparation method thereof. Background technique [0002] Plastic additives, also known as plastic additives, are some compounds that must be added to improve the processing performance of polymers (synthetic resins) or to improve the performance of the resin itself. For example, plasticizers are added to reduce the molding temperature of polyvinyl chloride resin and make the product soft; another example is to add foaming agents to prepare lightweight, vibration-resistant, heat-insulating, and sound-insulating foamed plastics; The decomposition temperature is very close to the molding processing temperature, and it cannot be molded without adding a heat stabilizer. Therefore, plastic additives occupy a particularly important position in plastic molding processing. A large class of additives used in plastic molding products, including plasticizers, heat stabilizers, antioxidants, light...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

Application Information

Patent Timeline
no application Login to view more
Patent Type & Authority Applications(China)
IPC IPC(8): C08K13/04C08K7/06C08K5/12C08K3/34C08K3/36C08L83/04
CPCC08K13/04C08K3/34C08K3/36C08K5/12C08K7/06C08K2201/011C08K2201/014C08L2201/04C08L2201/08C08L83/04
Inventor 黄雄关
Owner WUHU TIANXIONG NEW MATERIAL TECH
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Try Eureka
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap