Cermet material

A cermet and raw material technology, applied in the field of cermet materials, can solve the problems of restricting the development of ceramics, high temperature resistance, corrosion resistance, water seepage prevention, strength not meeting the needs of users, general performance, etc.

Inactive Publication Date: 2016-11-09
青岛燕园海洋生物科技有限公司
View PDF0 Cites 4 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

[0002] At present, cermet materials are being used more and more in our lives. Because cermet materials have many advantages of ceramics and metals, they are favored by users. However, the existing ceramic metal materials

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0011] A cermet material, made of the following raw materials in parts by mass:

[0012] 50 parts of kaolin, 12 parts of quartz sand, 8 parts of zircon, 5 parts of alumina, 10 parts of anorthite, 9 parts of albite, 12 parts of talc powder, 8 parts of mica powder, 5 parts of zirconia powder, and 6 parts of lithium , 7 parts of sodium borohydride, 1 part of calcium hydrogen phosphate, 4 parts of agate stone, 5 parts of borax, 2 parts of nano-iron dioxide, 7 parts of glass fiber, 5 parts of magnesium oxide, and 2 parts of barium hydroxide.

Embodiment 2

[0014] A cermet material, made of the following raw materials in parts by mass:

[0015] 55 parts of kaolin, 14 parts of quartz sand, 10 parts of zircon, 6 parts of alumina, 13 parts of anorthite, 10 parts of albite, 13 parts of talc powder, 9 parts of mica powder, 7 parts of zirconia powder, and 7 parts of lithium , 8 parts of sodium borohydride, 2 parts of calcium hydrogen phosphate, 4.5 parts of agate stone, 5.5 parts of borax, 3 parts of nanometer iron dioxide, 10 parts of glass fiber, 6 parts of magnesium oxide, and 4 parts of barium hydroxide.

Embodiment 3

[0017] A cermet material, made of the following raw materials in parts by mass:

[0018] 60 parts of kaolin, 16 parts of quartz sand, 11 parts of zircon, 7 parts of alumina, 15 parts of anorthite, 11 parts of albite, 14 parts of talc powder, 10 parts of mica powder, 9 parts of zirconia powder, and 8 parts of lithium , 10 parts of sodium borohydride, 3 parts of calcium hydrogen phosphate, 5 parts of agate stone, 6 parts of borax, 4 parts of nanometer iron dioxide, 12 parts of glass fiber, 7 parts of magnesium oxide, and 5 parts of barium hydroxide.

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

PUM

No PUM Login to view more

Abstract

The invention discloses a cermet material. The cermet material is prepared from the following raw materials in parts by mass: 50 to 60 parts of kaolin, 12 to 16 parts of quartz sand, 8 to 11 parts of zircon, 5 to 7 parts of aluminum oxide, 10 to 15 parts of anorthite, 9 to 11 parts of albite, 12 to 14 parts of talcum powder, 8 to 10 parts of mica powder, 5 to 9 parts of zirconia powder, 6 to 8 parts of lithium, 7 to 10 parts of sodium borohydride, 1 to 3 parts of calcium hydrophosphate, 4 to 5 parts of agate, 5 to 6 parts of borax, 2 to 4 parts of nano ferrum dioxide, 7 to 12 parts of glass fiber, 5 to 7 parts of magnesium oxide and 2 to 5 parts of barium hydroxide. The cermet material has the advantages of high temperature resistance, corrosion resistance, water seepage prevention and high strength.

Description

technical field [0001] The invention relates to a ceramic material, in particular to a cermet material. Background technique [0002] At present, cermet materials are being used more and more in our lives. Because cermet materials have many advantages of ceramics and metals, they are favored by users. However, the existing ceramic metal materials have general performance, high temperature resistance and corrosion resistance. , anti-seepage and strength are far from meeting the needs of users. These problems restrict the development of the entire ceramic industry. Contents of the invention [0003] In order to solve the above existing problems, the present invention provides a cermet material capable of high temperature resistance, corrosion resistance, water seepage resistance and high strength. [0004] The technical solution adopted by the present invention to solve the above technical problems is: a cermet material made of the following raw materials in parts by mass: ...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

Application Information

Patent Timeline
no application Login to view more
IPC IPC(8): C22C49/00C22C101/06
CPCC22C49/00
Inventor 陆明军
Owner 青岛燕园海洋生物科技有限公司
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Try Eureka
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap