Preparation method of intumescent fire-retardant paint

A kind of fireproof coating and expansion type technology, applied in the direction of fireproof coating, coating, etc., can solve the problems that are not conducive to widespread application, increase management costs, and require a variety of equipment, etc., to achieve low toxicity, no fire hazard, and low cost Effect

Inactive Publication Date: 2016-11-23
泉州市合创涂料科技有限公司
View PDF0 Cites 3 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

This brings technological complexity to its production and engineering construction, requires a variety of equipment, increases management costs, and increases costs, which is not conducive to widespread application

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Examples

Experimental program
Comparison scheme
Effect test

example 1

[0029] Ethylene-vinyl acetate copolymer emulsion 2.1;

[0030] Modified resin 7.5;

[0031] Ammonium polyphosphate 20.8;

[0032] Chlorinated paraffin 2.1;

[0033] Pentaerythritol 10.0;

[0034] Melamine 8.3;

[0035] Cyanoguanidine 4.2;

[0036] Silica 4.2;

[0037] Titanium dioxide 1.7;

[0038] Silicone oil 1.6;

[0039] Sodium hexametaphosphate (10% concentration solution) 4.2;

[0040] water 33.3;

[0041] Tributyl phosphate 0.007;

[0042] Sodium pentachlorophenate 0.035;

[0043] Sodium Benzoate 0.035.

example 2

[0045] Ethylene-vinyl acetate copolymer emulsion 3.0;

[0046] Modified resin 7.2;

[0047] Ammonium polyphosphate 20.8;

[0048] Chlorinated paraffin 2.1;

[0049] Pentaerythritol 10.0;

[0050] Melamine 8.3;

[0051] Cyanoguanidine 4.2;

[0052] Silica 4.2;

[0053] Titanium dioxide 1.7;

[0054] Silicone oil 1.0;

[0055] Sodium hexametaphosphate (10% concentration solution) 4.2;

[0056] water 33.3;

[0057] Tributyl phosphate 0.007;

[0058] Sodium pentachlorophenate 0.035;

[0059] Sodium Benzoate 0.035.

example 3

[0061] Ethylene-vinyl acetate copolymer emulsion 5.0;

[0062] Modified resin 5.7;

[0063] Ammonium polyphosphate 20.8;

[0064] Chlorinated paraffin 2.1;

[0065] Pentaerythritol 10.0;

[0066] Melamine 8.3;

[0067] Cyanoguanidine 4.2;

[0068] Silica 8.0;

[0069] Titanium dioxide 1.7;

[0070] Sodium hexametaphosphate (10% concentration solution) 4.2;

[0071] water 30.0;

[0072] Tributyl phosphate 0.007;

[0073] Sodium pentachlorophenate 0.035;

[0074] Sodium Benzoate 0.035.

[0075] After the ingredients are selected, prepare according to the following process:

[0076] (1) sodium hexametaphosphate (10% concentration solution) and water are put into the container as a dispersant, and stirred evenly for subsequent use;

[0077] (2) Pour the uniformly stirred dispersant and water into the ball mill, start the machine, and while grinding, add ammonium polyphosphate, paraffin wax, pentaerythritol, melamine, cyanoguanidine, sili...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

No PUM Login to View More

Abstract

The invention discloses a preparation method of intumescent fire-retardant paint. The intumescent fire-retardant paint is prepared from an ethene-vinyl acetate copolymer emulsion and modified resin as base materials, melamine and cyanoguanidine as foaming agents, pentaerythritol as a charring agent, ammonium polyphosphate as a dehydration charring catalyst, chlorinated paraffin as a fire retardant, silica and titanium dioxide as filling materials and other auxiliary agents. The aqueous emulsion and modified resin are blended to form the base materials so that xylene release damage is prevented in fireproof paint production, storage, transport, construction and use. The preparation method saves a production cost, is convenient for production construction and has no fire hazard risk. The intumescent fire-retardant paint has excellent performances and a wide application range. The intumescent fire-retardant paint satisfies requirements in the finishing fire-retardant paint general technical specification GB 12441-1998, exceeds standard technical indexes of the finishing fire-retardant paint general technical specification GB 12441-1998, satisfies requirements in the steel structure fire-retardant paint general technical specification GB 14907-94 and exceeds standard technical indexes of the steel structure fire-retardant paint general technical specification GB 14907-94.

Description

technical field [0001] The invention relates to the production technology category of fireproof coatings, in particular to a preparation method of intumescent fireproof coatings. Background technique [0002] At present, the intumescent fireproof coatings used in building fireproofing projects at home and abroad can be divided into two categories: facing fireproofing coatings and steel structure fireproofing coatings, each of which has many varieties. Generally speaking, the reason why fire retardant coatings can prevent fire is that after the coating is formed into a film, it is an ordinary paint film at room temperature. Under flame or high temperature, the coating expands and carbonizes, forming a hard film dozens of times thicker than the original film. Burning spongy carbonaceous layer. It can isolate the heat transfer and flame retardancy of the base material from the external fire source. The components of the coating undergo physical and chemical changes under the...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
Patent Type & Authority Applications(China)
IPC IPC(8): C09D123/08C09D5/18C09D7/12
Inventor 陈登龙
Owner 泉州市合创涂料科技有限公司
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Patsnap Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Patsnap Eureka Blog
Learn More
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic, Popular Technical Reports.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap|About US| Contact US: help@patsnap.com