Al technical title is built by PatSnap Al team. It summarizes the technical point description of the patent document.
A technology of putty powder and interior walls, applied in the direction of filling slurry, etc., can solve the problems of mildew, easy yellowing, cracking, etc., and achieve the effects of strong adhesion, good leveling, and good water resistance
Inactive Publication Date: 2016-11-30
CHANGSHU QIYUE NEW BUILDING MATERIAL TECH CO LTD
View PDF1 Cites 2 Cited by
Summary
Abstract
Description
Claims
Application Information
AI Technical Summary
This helps you quickly interpret patents by identifying the three key elements:
Problems solved by technology
Method used
Benefits of technology
Problems solved by technology
[0002] The existing crack-resistant putty powder for interior walls needs to be improved in leveling, adhesion, water resistance, strength, abrasion resistance, acid and alkali corrosion resistance, high and low temperature resistance, and mildew resistance. After being damp, it is prone to hollowing, peeling, cracking, and shedding, and it is prone to yellowing, mold, and black spots
Method used
the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more
Examples
Experimental program
Comparison scheme
Effect test
Embodiment 1
[0053] The anti-cracking putty powder for interior walls consists of the following components by weight:
[0054] 1-2 parts polyoxyethylene oleate,
[0055] 1.8 parts polyvinylpyrrolidone,
[0056] 1.6 parts of sodium alpha-olefin sulfonate,
[0057] 0.9 parts lauryltrimethylammonium chloride,
[0058] 1.4 parts of sodium oleamide ethanesulfonate,
[0059] 0.8 parts magnesium aluminum silicate,
[0060] 3.4 parts carbon fiber filaments,
[0061] 14 parts marble flour,
[0062] 24 parts white latex,
[0063] 46 parts gray calcium.
Embodiment 2
[0065] The anti-cracking putty powder for interior walls consists of the following components by weight:
[0066] 1 part polyoxyethylene oleate,
[0067] 1.8 parts polyvinylpyrrolidone,
[0068] 1.6 parts of sodium alpha-olefin sulfonate,
[0069] 0.9 parts lauryltrimethylammonium chloride,
[0070] 1.4 parts of sodium oleamide ethanesulfonate,
[0071] 0.8 parts magnesium aluminum silicate,
[0072] 3.4 parts carbon fiber filaments,
[0073] 14 parts marble flour,
[0074] 24 parts white latex,
[0075] 46 parts gray calcium.
Embodiment 3
[0077] The anti-cracking putty powder for interior walls consists of the following components by weight:
[0078] 2 parts polyoxyethylene oleate,
[0079] 1.8 parts polyvinylpyrrolidone,
[0080] 1.6 parts of sodium alpha-olefin sulfonate,
[0081] 0.9 parts lauryltrimethylammonium chloride,
[0082] 1.4 parts of sodium oleamide ethanesulfonate,
[0083] 0.8 parts magnesium aluminum silicate,
[0084] 3.4 parts carbon fiber filaments,
[0085] 14 parts marble flour,
[0086] 24 parts white latex,
[0087] 46 parts gray calcium.
the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more
PUM
Login to view more
Abstract
The invention discloses anti-cracking putty powder for interior walls. The anti-cracking putty powder comprises, by weight, 1-2 parts of oleic acid polyoxyethylene ester, 1.8 parts of polyvinylpyrrolidone, 1.6 parts of alpha-olefin sulfonate, 0.9 part of dodecyltrimethylammonium chloride, 1.4 parts of oleoyl methylamine sodium diethylsulfonate, 0.8 part of magnesium aluminium silicate, 3.4 parts of carbon fiber yarn, 14 parts of marble powder, 24 parts of white latex and 46 parts of ash calcium. The anti-cracking putty powder for interior walls is good in levelling property, strong in adhesive force, good in water proofness, high in strength, good in sanding property, resistant to acid and alkali corrosion, resistant to high and low temperature changes and resistant to mildew, is free of hollowing, peeling, crazing and stripping after being exposed to water and damp, and is also free of yellowing, mildewing and black spot formation.
Description
technical field [0001] The invention relates to an anti-cracking putty powder for interior walls. Background technique [0002] The existing crack-resistant putty powder for interior walls needs to be improved in leveling, adhesion, water resistance, strength, abrasion resistance, acid and alkali corrosion resistance, high and low temperature resistance, and mildew resistance. After being damp, it is prone to hollowing, peeling, cracking, and shedding, and it is also prone to yellowing, mold, and black spots. Contents of the invention [0003] The object of the present invention is to provide an anti-cracking putty powder for interior walls, which has good leveling property, strong adhesion, good water resistance, high strength, abrasion resistance, acid and alkali corrosion resistance, high and low temperature resistance, and mildew resistance , No hollowing, peeling, cracking, shedding after being exposed to water and damp, and no yellowing, mildew, or black spots. [...
Claims
the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more
Application Information
Patent Timeline
Application Date:The date an application was filed.
Publication Date:The date a patent or application was officially published.
First Publication Date:The earliest publication date of a patent with the same application number.
Issue Date:Publication date of the patent grant document.
PCT Entry Date:The Entry date of PCT National Phase.
Estimated Expiry Date:The statutory expiry date of a patent right according to the Patent Law, and it is the longest term of protection that the patent right can achieve without the termination of the patent right due to other reasons(Term extension factor has been taken into account ).
Invalid Date:Actual expiry date is based on effective date or publication date of legal transaction data of invalid patent.
Login to view more
Patent Type & Authority Applications(China)
IPC IPC(8): C09D5/34
CPCC09D5/34
Inventor 范毓明
Owner CHANGSHU QIYUE NEW BUILDING MATERIAL TECH CO LTD