An environmental-friendly type steel decontamination rust remover and a preparing method thereof

An environment-friendly, rust-removing agent technology, applied in the field of environment-friendly steel cleaning and rust-removing agent and its preparation, can solve problems such as endangering the use safety, over-corrosion of the outer layer of metal products, shortening the service life, etc. High rust removal efficiency and less pollution

Inactive Publication Date: 2016-11-30
WUXI EPIC TECH
View PDF3 Cites 2 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

However, the cleaning and descaling agents currently on the market use hydrochloric acid, nitric acid, sulfuric acid or other inorganic strong acids to clean and descale the scale on the inner and outer surfaces of metal products, resulting in serious three waste pollution. Brittle, endangering the safety of use and shortening the service life

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0011] The environment-friendly steel decontamination and derusting agent of the present embodiment is made by the following components by weight: 68 parts of deionized water, 10 parts of sodium tripolyphosphate, 15 parts of pentaerythritol fatty acid ester, dodecenyl succinic acid 13 parts, 5 parts of konjac gum, 10 parts of sodium alginate, 2 parts of polyacrylamide, 2 parts of potassium oxalate, 4 parts of zinc dialkyl dithiophosphate, 5 parts of benzotriazole, 22 parts of ethylene glycol.

[0012] Each component is weighed according to the above-mentioned weight fraction ratio, and then mixed and stirred, and stirred evenly to completely dissolve each component, so as to obtain the environment-friendly steel decontamination and rust remover.

[0013] The environment-friendly decontamination and derusting agent for steel in this embodiment can be directly soaked and sprayed to derust the surface of the workpiece.

Embodiment 2

[0015] The environment-friendly steel decontamination and derusting agent of the present embodiment is made by the following components by weight: 88 parts of deionized water, 14 parts of sodium tripolyphosphate, 18 parts of pentaerythritol fatty acid ester, dodecenyl succinic acid 16 parts, 8 parts of konjac gum, 14 parts of sodium alginate, 6 parts of polyacrylamide, 6 parts of potassium oxalate, 10 parts of zinc dialkyldithiophosphate, 11 parts of benzotriazole, 25 parts of ethylene glycol, 13 parts of vinyltrimethoxysilane.

[0016] Each component is weighed according to the above-mentioned weight fraction ratio, and then mixed and stirred, and stirred evenly to completely dissolve each component, so as to obtain the environment-friendly steel decontamination and rust remover.

[0017] The environment-friendly decontamination and derusting agent for steel in this embodiment can be directly soaked and sprayed to derust the surface of the workpiece.

Embodiment 3

[0019] The environment-friendly steel decontamination and derusting agent of the present embodiment is made by the following components by weight: 68 parts of deionized water, 10 parts of sodium tripolyphosphate, 15 parts of pentaerythritol fatty acid ester, dodecenyl succinic acid 13 parts, 5 parts of konjac gum, 10 parts of sodium alginate, 2 parts of polyacrylamide, 2 parts of potassium oxalate, 4 parts of zinc dialkyldithiophosphate, 5 parts of phenylacryltriazole, 22 parts of ethylene glycol, 3 parts of vinyltrimethoxysilane and 3 parts of diphenolic propane.

[0020] Each component is weighed according to the above-mentioned weight fraction ratio, and then mixed and stirred, and stirred evenly to completely dissolve each component, so as to obtain the environment-friendly steel decontamination and rust remover.

[0021] The environment-friendly decontamination and derusting agent for steel in this embodiment can be directly soaked and sprayed to derust the surface of the...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

No PUM Login to View More

Abstract

The invention discloses an environment-friendly decontamination and derusting agent for steel and a preparation method thereof, which is prepared from the following raw materials in parts by weight: 68-88 parts of deionized water, 10-14 parts of sodium tripolyphosphate, and 15 parts of pentaerythritol fatty acid ester ‑18 parts, 13‑16 parts of dodecenyl succinic acid, 5‑8 parts of konjac gum, 10‑14 parts of sodium alginate, 2‑6 parts of polyacrylamide, 2‑6 parts of potassium oxalate, dialkyl di Zinc thiophosphate 4‑10 parts, benzotriazole 5‑11 parts, ethylene glycol 22‑25 parts. The environment-friendly decontamination and derusting agent for steel prepared by the invention is non-toxic, environmentally friendly and energy-saving, and has little pollution to the environment; the derusting efficiency is high, and it can quickly remove oil stains, rust, oxide films, etc. on the metal surface; There is basically no over-corrosion and hydrogen embrittlement.

Description

technical field [0001] The invention relates to an environment-friendly steel decontamination and derusting agent and a preparation method thereof. Background technique [0002] Steel is the most used metal in human history, especially after entering industrialization, the demand for steel is increasing day by day. At present, the proven reserves of steel are very limited, and the amount of human mining remains high. If this pair of contradictions cannot be alleviated, it will largely restrict the further development of human beings. And the loss of steel due to corrosion every year is very alarming, resulting in the waste of a lot of resources. During the production process or the use of finished products, steel is easily oxidized and rusted when it encounters humid air and rainy days, which affects the appearance quality of the product. The easiest way to prevent steel from rusting is to isolate the steel from water and air, and keep the surface of the steel dry and clea...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
Patent Type & Authority Applications(China)
IPC IPC(8): C23G1/00
CPCC23G1/00
Inventor 尤为
Owner WUXI EPIC TECH
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Patsnap Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Patsnap Eureka Blog
Learn More
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic, Popular Technical Reports.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap|About US| Contact US: help@patsnap.com