A kind of ceramic dispersant and preparation method thereof

A technology of ceramic dispersant and initiator, applied in the field of ceramic dispersant and its preparation, can solve the problems of side effects, easy solidification, narrow debonding range, etc., and achieves good fluidity and viscosity, simple production process, and easy control of conditions. Effect

Active Publication Date: 2018-12-21
广东枫树陶瓷原料有限公司
View PDF3 Cites 2 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

These dispersants have disadvantages such as narrow dissolving range, easy solidification in a short time, poor adaptability and side effects.
A small number of ceramic enterprises use organic dispersants and inorganic dispersants in combination. Although it can achieve certain effects, the dispersants developed are not universal and cannot be applied to various clay mineral raw materials, so it is difficult to popularize and use them.

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • A kind of ceramic dispersant and preparation method thereof
  • A kind of ceramic dispersant and preparation method thereof
  • A kind of ceramic dispersant and preparation method thereof

Examples

Experimental program
Comparison scheme
Effect test

preparation example Construction

[0026] A kind of preparation method of ceramic dispersant, realizes by following steps:

[0027] (1) After adding allyl thiourea, sodium cardanol sulfonate, acid regulator and water into the reactor, start stirring, and start heating;

[0028] (2) When the temperature rises to 100-120°C, start to add glyoxal dropwise for 1-5 hours;

[0029] (3) Add cardanol epoxy propylene ether and isopentenol polyoxyethylene ether in the reaction kettle again, start to drip the initiator solution that mass percent concentration is 1~10% after waiting to stir, this initiator solution It is prepared from the initiator and part of the water; the dropping time is controlled at 0.5-3 hours, and the temperature is controlled at 95-120°C during the dropping;

[0030] (4) After the dropwise addition, keep the temperature and continue to react for 1 to 4 hours, add an alkaline regulator for neutralization, add the remaining water after the neutralization is completed, cool down and discharge the mat...

Embodiment 1

[0033] A kind of ceramic dispersant of the present invention is made of the raw material components of following proportioning by weight:

[0034]

[0035] Its preparation method is realized through the following steps:

[0036] (1) Add 2 parts of allylthiourea, 6 parts of sodium cardanol sulfonate, 3 parts of hydroxyethylidene diphosphonic acid and 10 parts of water into the reactor, start stirring, and start heating;

[0037] (2) When the temperature rises to 110°C, start to add 9 parts of glyoxal dropwise for 1.5 hours;

[0038] (3) add 2 parts of cardanol epoxy propylene ethers, 1 part of isopentenol polyoxyethylene ethers in the reaction kettle again, start to drip the sodium persulfate solution that mass percentage concentration is 5% after waiting to be stirred evenly, this The sodium persulfate solution is prepared from 1 part of sodium persulfate and 19 parts of water; the dropping time is controlled at 1.5 hours, and the temperature is controlled at 110°C during ...

Embodiment 2

[0041] A ceramic dispersant, made of the following raw material components in parts by weight:

[0042]

[0043] Its preparation method is realized through the following steps:

[0044] (1) Add 3 parts of allyl thiourea, 7 parts of sodium cardanol sulfonate, 3 parts of 2-phosphonic acid butane-1,2,4-tricarboxylic acid and 10 parts of water into the reaction kettle and start stirring, and start to heat up;

[0045] (2) When the temperature rises to 112°C, start to drop 10 parts of glyoxal for 2 hours;

[0046] (3) add 2 parts of cardanol epoxy propylene ethers, 1 part of isopentenol polyoxyethylene ethers in the reaction kettle again, begin to drip the sodium persulfate solution that mass percent concentration is 2% after the stirring is uniform, this The sodium persulfate solution is prepared from 1 part of sodium persulfate and 49 parts of water; the dropping time is controlled at 2 hours, and the temperature is controlled at 115°C during the dropping;

[0047] (4) Afte...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

No PUM Login to View More

Abstract

The invention provides a ceramic dispersing agent and a preparation method thereof. The preparation method comprises the following steps that 1, allylthiourea, cardanol sodium sulfonate, an acidity regulating agent and water are added into a reaction kettle, stirring is started, and heating is started to increase the temperature; 2, when the temperature is increased to 100 DEG C-120 DEG C, glyoxal starts to be dropwise added, and the dropwise adding time is 1-5 h; 3, cardanol epoxy propyl ether and prenol polyoxyethylene ether are added into the reaction kettle, and after the materials are stirred to be uniform, an initiator solution with the mass percent concentration of 1%-10% starts to be dropwise added, wherein the initiator solution is prepared from an initiator and part of water, the dropwise adding time is controlled to be 0.5-3 h, and the dropwise adding temperature is controlled to be 95 DEG C-120 DEG C; 4, after dropwise adding is completed, reacting continues to be conducted for 1-4 h by keeping the temperature, an alkalinity regulating agent is added for neutralization, after neutralization is completed, retaining water is added, cooling and discharging are conducted, and then the ceramic dispersing agent is obtained.

Description

technical field [0001] The invention belongs to the technical field of ceramic dispersant preparation, in particular to a ceramic dispersant and a preparation method thereof. Background technique [0002] Ceramic dispersant, also known as ceramic decoagulant, debonding agent, water reducer and diluent, etc., refers to a surface that can quickly wet the surface of solid particles and raise the energy barrier between solid particles to a high enough level. active agent. The main purpose is to keep the ceramic slurry with good fluidity within a certain period of time, that is, to reduce the surface energy of the particles, to reduce the interfacial tension between solid and liquid, to better and effectively infiltrate small solid particles, and to obtain high solid content and Good fluidity mud. In the preparation of special ceramic slurry, excellent dispersants can not only affect the surface charge of particles, but also change the chemical bond structure on the surface of ...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
Patent Type & Authority Patents(China)
IPC IPC(8): C08F299/02C08G14/08C04B35/634
CPCC04B35/63444C08F299/022C08G14/08
Inventor 刘碧霞
Owner 广东枫树陶瓷原料有限公司
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Patsnap Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Patsnap Eureka Blog
Learn More
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic, Popular Technical Reports.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap|About US| Contact US: help@patsnap.com