White latex viscosity-increasing bamboo-plastic foam composite door and window material and preparation method thereof

A white latex and bamboo-plastic technology, applied in the field of bamboo-plastic composite materials, can solve problems such as the need to improve the mechanical strength, limit the application of bamboo-plastic foam composite materials, and the functionalization of composite materials is not perfect, so as to achieve excellent formaldehyde adsorption efficiency and increase Larger formaldehyde adsorption efficiency, improved affinity and fluidity effects

Inactive Publication Date: 2016-12-07
安徽三乐节能科技有限公司
View PDF0 Cites 0 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

[0003] In "The Effect of Titanate Coupling Agent on the Properties of Bamboo-plastic Foamed Composite Materials", Zhou Xingxing prepared a bamboo-plastic foamed composite material by using bamboo powder, polypropylene, and high-melt strength polypropylene, but its The mechanical strength needs to be improved, and the functionalization of the composite material is not perfect enough, which limits the application of bamboo-plastic foam composite materials

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Examples

Experimental program
Comparison scheme
Effect test

Embodiment

[0016] A white latex thickened bamboo-plastic foam composite door and window material is characterized in that it is made of the following raw materials in parts by weight:

[0017] White latex 2, isotactic polypropylene 70, peanut shell powder 2, high melt strength polypropylene 15, bamboo powder 40, activated carbon 15, masterbatch 2, corundum powder 2, Cu(NO 3 ) 2 25, stearic acid 3, calcium stearate 3, foaming agent AC1601 3, zinc stearate 15, NaOH solution 60, polyacrylate emulsion 3;

[0018] The particle diameter of described bamboo powder is 90-350 μ m, and NaOH solution concentration is 1mol / L, and Cu(NO 3 ) 2 The concentration is 0.1 mol / L, and the solid content of the polyacrylate emulsion is 40-50%.

[0019] The preparation method of the bamboo-plastic foamed composite door and window material of described a kind of white latex viscosification is characterized in that, is made by the following steps:

[0020] a. Add activated carbon and corundum powder to NaOH...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

PropertyMeasurementUnit
particle diameteraaaaaaaaaa
bending strengthaaaaaaaaaa
Login to View More

Abstract

The invention discloses a white latex viscosity-increasing bamboo-plastic foam composite door and window material and a preparation method thereof. The white latex viscosity-increasing bamboo-plastic foam composite door and window material is characterized by being prepared from the following raw materials in parts by weight: 1 to 2 parts of white latex, 60 to 70 parts of isotatic polypropylene, 1 to 2 parts of peanut hull powder, 10 to 15 parts of high melt strength polypropylene, 30 to 40 parts of bamboo powder, 10 to 15 parts of active carbon, 1 to 2 parts of color masterbatch, 1 to 2 parts of corundum powder, 20 to 25 parts of Cu(NO3)2, 1 to 3 parts of stearic acid, 1 to 3 parts of calcium stearate, 1-3 parts of a foaming agent AC1601, 10 to 15 parts of zinc stearate, 50 to 60 parts of NaOH solution and 1 to 3 parts of polyacrylate emulsion. The active carbon and the diamond are modified by polyacrylate and Cu(NO3)2, so load of Cu(NO3)2 in the surface and the pore channels of active carbon and diamond is promoted; the white latex is added, so that the bonding strength among the components is enhanced.

Description

technical field [0001] The invention relates to a bamboo-plastic composite material, in particular to a white latex-increased bamboo-plastic foam composite door and window material and a preparation method thereof. Background technique [0002] Bamboo-plastic foam composites have attracted much attention recently because they can overcome the defects of high density and brittleness of bamboo-plastic composites. Bamboo-plastic composite materials mainly include polyvinyl chloride and polyolefin plastics. Polyvinyl chloride-based composite materials will pollute the environment during manufacture, use and disposal. Polyvinyl chloride-based composite materials have low rigidity and maximum service temperature, and are not easy to degrade. Therefore, polypropylene (PP) wood-plastic foam composites have become a recent research hotspot. Bamboo-plastic foam composite materials have a wide range of applications, involving the automobile industry and transportation industry, const...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
Patent Type & Authority Applications(China)
IPC IPC(8): C08L23/12C08L97/02C08L31/04C08K13/06C08K9/12C08K9/04C08K3/04C08K3/22C08K5/09C08K5/098C08J9/10
CPCC08L23/12C08J9/103C08J2203/04C08J2323/12C08J2497/02C08K2201/014C08L2203/14C08L2205/025C08L2205/035
Inventor 陈学军吴珍梅徐琼琼曹蕾沈中
Owner 安徽三乐节能科技有限公司
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Patsnap Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Patsnap Eureka Blog
Learn More
PatSnap group products