A technology of compound heat stabilizer and auxiliary heat stabilizer, which is applied in the field of powder zinc-based compound heat stabilizer for polyvinyl chloride and its preparation, can solve the problems of restricting the wide application in the field of PVC, and achieves improvement of initial colorability and phase increase. Effects of capacitive, good initial and long-term stability

Inactive Publication Date: 2016-12-07
ZHEJIANG HIMPTON NEW MATERIAL
View PDF4 Cites 6 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

Because fatty acid calcium salts have serious pressure-separation properties, and fatty-acid zincs have serious blooming phenomena, the existing calcium

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • Powdery zinc base composite heat stabilizer and preparation method thereof
  • Powdery zinc base composite heat stabilizer and preparation method thereof
  • Powdery zinc base composite heat stabilizer and preparation method thereof

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0045] A powder zinc-based composite thermal stabilizer, the composite thermal stabilizer is processed from the following components: 35g of zinc-based complexes, 10g of zinc burning inhibitors, 10g of auxiliary thermal stabilizers, 5g of compatibilizers, inorganic auxiliary 5g of diethylene glycol butyl ether, 5g of diethylene glycol butyl ether; the zinc-based complex is formed by mixing the following components: 30g of zinc acetylacetonate, 5g of zinc glycinate, 3g of zinc p-tert-butylbenzoate and 2g of zinc thioglycolate reverse thioester , the auxiliary heat stabilizer is composed of three (epoxypropyl) isocyanurate 5g and methyl silicone oil 5g, and the zinc alkane inhibitor is pentaerythritol di-tert-butylbenzoate, sodium citrate and 4A Molecular sieve is a compound with a mass ratio of 1:2:3, the compatibilizer is maleic anhydride monomer graft PVC-g-MAH, and the inorganic additive is an equal proportion mixture of attapulgite and calcium oxide.

[0046] Accurately wei...

Embodiment 2

[0048] A powder zinc-based composite thermal stabilizer, the composite thermal stabilizer is processed from the following components: 55g of zinc-based complexes, 20g of zinc burning inhibitors, 20g of auxiliary thermal stabilizers, 10g of compatibilizers, inorganic auxiliary 15g of diethylene glycol butyl ether, 10g of diethylene glycol butyl ether; the zinc-based complex is formed by mixing the following components: 45g of zinc acetylacetonate, 15g of zinc glycinate, 10g of zinc p-tert-butylbenzoate and 8g of zinc thioglycolate , the auxiliary heat stabilizer is composed of three (glycidyl) isocyanurate 10g and benzyl carbazate 10g, and the zinc alkane inhibitor consists of pentaerythritol di-tert-butylbenzoate, sodium citrate It is a compound with 4A molecular sieve at a mass ratio of 1:5:5, the compatibilizer is PE wax graft PVC-g-PEW, and the inorganic additive is an equal proportion mixture of attapulgite and sodium bicarbonate.

[0049] Accurately weigh zinc-based compl...

Embodiment 3

[0051] A powder zinc-based composite thermal stabilizer, the composite thermal stabilizer is processed from the following components: 40g of zinc-based complexes, 15g of zinc burning inhibitors, 10g of auxiliary thermal stabilizers, 5g of compatibilizers, inorganic auxiliary 5g of diethylene glycol butyl ether, 5g of diethylene glycol butyl ether; the zinc-based complex is formed by mixing the following components: 30g of zinc acetylacetonate, 5g of zinc glycinate, 3g of zinc p-tert-butylbenzoate and 2g of zinc thioglycolate reverse thioester , the auxiliary heat stabilizer is composed of three (glycidyl) isocyanurate 5g and benzyl carbazate 5g, and the zinc alkane inhibitor consists of pentaerythritol di-tert-butylbenzoate, sodium citrate and 4A molecular sieve in a mass ratio of 1:5:5, the compatibilizer is maleic anhydride monomer graft PVC-g-MAH2.5g and PE wax graft PVC-g-PEW2.5g, inorganic auxiliary The agent is a mixture of attapulgite and sodium bicarbonate in equal pro...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

PUM

No PUM Login to view more

Abstract

The invention relates to a powdery zinc base composite heat stabilizer and a preparation method thereof, and especially relates to a powdery zinc base composite heat stabilizer for polyvinyl chloride and a preparation method thereof. The composite heat stabilizer is prepared from the following components in parts by weight: 35 to 55 parts of zinc base complex, 10 to 20 parts of zinc burning inhibitor, 10 to 20 parts of auxiliary heat stabilizer, 5 to 10 parts of compatilizer, 5 to 15 parts of inorganic aid, and 5 to 10 parts of diethylene glycol monobutyl ether; wherein the zinc base complex is a composition of zinc acetylacetonate, zinc glycinate, zinc p-tert-butyl benzoate, and mercaptoacetic acid reverse thioester zinc; and the auxiliary heat stabilizer is a mixture composed of any two components of tri(glycidyl) isocyanurate, methyl silicone oil, benzyl carbazate according to any ratio. Compared with the conventional powdery calcium-zinc heat stabilizers, the provided powdery zinc base composite heat stabilizer does not contain any sodium aliphatate or zinc aliphatate, thus the heat stabilizer will not be precipitated easily, the blooming is difficult to happen, and the problem that conventional calcium-zinc heat stabilizers are precipitated and bloomed on the surface of colorful PVC products is solved.

Description

technical field [0001] The invention relates to a powder zinc-based composite thermal stabilizer and a preparation method, in particular to a powder zinc-based composite thermal stabilizer for polyvinyl chloride and a preparation method. Background technique [0002] At present, the heat stabilizer with the largest amount of use in my country's polyvinyl chloride (PVC) product industry is lead-containing heat stabilizer, with an annual consumption of about 600,000 tons. As the global awareness and requirements for ecological environmental protection increase, lead-containing heat stabilizers will face a situation of being completely banned. The development of high-efficiency green stabilizers has become a major technical bottleneck restricting the sustainable and healthy development of the PVC product industry. Calcium-zinc composite heat stabilizer has been highly valued by the industry due to its good thermal stability efficiency and environmental friendliness, and has a g...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

Application Information

Patent Timeline
no application Login to view more
IPC IPC(8): C08L27/06C08L51/00C08L83/04C08L87/00C08K13/02C08K5/07C08K5/17C08K5/098C08K5/3492C08K5/103C08K3/34C08K3/22C08K3/26C08K5/372
CPCC08L27/06C08K3/22C08K3/26C08K3/346C08K5/0091C08K5/098C08K5/103C08K5/34924C08K13/02C08K2003/2206C08K2201/014C08L51/00C08L87/00C08L2201/08
Inventor 唐伟高尔金瞿英俊孟建新廖永林陈森方
Owner ZHEJIANG HIMPTON NEW MATERIAL
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Try Eureka
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap