A kind of water-based amino baking varnish and preparation method thereof

An amino baking paint, water-based technology, used in polyurea/polyurethane coatings, epoxy resin coatings, polyester coatings and other directions, can solve the problems of environmental safety hazards, endanger the health of operators, organic solvent discharge pollution and other problems, achieve convenient construction, The construction is convenient and quick, and the effect of shielding hydrolysis

Active Publication Date: 2017-07-07
HEBEI CHENYANG INDAL & TRADE GROUP CO LTD
View PDF4 Cites 3 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

[0003] At present, paints generally use organic solvents as raw materials. This kind of paint will not only cause a large amount of organic solvents to discharge and cause pollution, but also endanger the health of operators, which has laid a major hidden danger for environmental safety issues.

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0033] A water-based amino baking varnish, the water-based amino baking varnish is made of the following raw material ratios, calculated by weight percentage: 25% water-based polyester resin, 5% water-based epoxy resin, 9% water-based amino resin, 35% Deionized water, 2% pH regulator, 0.3% wetting agent, 0.4% defoamer, 0.5% dispersant, 2% co-solvent, 17.1% pigment and filler, 2% nano-alumina , 0.5% lithium magnesium silicate, 0.4% thickener, 0.8% leveling agent.

[0034] The preparation method of the water-based polyester resin is: add the water-based branched-chain polyester resin with an acid value of 50 mgKOH / g, add glycidyl tertiary carbonic acid ester, carry out copolymerization modification at 120 ° C for 0.5 h, until the end point acid value is 40 mgKOH / g, and obtain Waterborne polyester resin. The mass ratio of water-based branched polyester resin to glycidyl tertiary carbonic acid ester is 8.5:1.

[0035] The preparation method of water-based epoxy resin is as follo...

Embodiment 2

[0043]A water-based amino baking varnish, the water-based amino baking varnish is made of the following raw material ratios, calculated as: 30% water-based polyester resin, 4% water-based epoxy resin, 7% water-based amino resin, 28.8% Deionized water, 1.5% pH adjuster, 0.4% wetting agent, 0.2% defoamer, 0.7% dispersant, 1% co-solvent, 20% pigment and filler, 5% nano-alumina , 0.4% lithium magnesium silicate, 0.3% thickener, 0.7% leveling agent.

[0044] The preparation method of the water-based polyester resin is: add the water-based branched-chain polyester resin with an acid value of 60mgKOH / g, add glycidyl tertiary carbonic acid ester, carry out copolymerization modification at 130°C for 0.5h, until the end point acid value is 50mgKOH / g, and obtain Waterborne polyester resin. The mass ratio of water-based branched polyester resin to glycidyl tertiary carbonic acid ester is 9:1.

[0045] The preparation method of water-based epoxy resin is as follows: low-iodine value fatt...

Embodiment 3

[0049] A water-based amino baking varnish, the water-based amino baking varnish is made of the following raw material ratios, calculated as: 35% water-based polyester resin, 4.5% water-based epoxy resin, 10% water-based amino resin, 26% Deionized water, 2.5% pH adjuster, 0.3% wetting agent, 0.5% defoamer, 0.8% dispersant, 5% co-solvent, 11% pigment and filler, 3% nano-alumina , 0.3% lithium magnesium silicate, 0.5% thickener, 0.6% leveling agent.

[0050] The preparation method of the water-based polyester resin is: add the water-based branched-chain polyester resin with an acid value of 55 mgKOH / g, add glycidyl tertiary carbonic acid ester, carry out copolymerization modification at 140 ° C for 0.5 h, until the end point acid value is 45 mgKOH / g, and obtain Waterborne polyester resin. The mass ratio of water-based branched polyester resin to glycidyl tertiary carbonic acid ester is 8.8:1.

[0051] The preparation method of the water-based epoxy resin is as follows: low-iodi...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

PropertyMeasurementUnit
acid valueaaaaaaaaaa
acid valueaaaaaaaaaa
acid valueaaaaaaaaaa
Login to View More

Abstract

The invention discloses a water-based amino baking varnish and a preparation method thereof, and relates to the technical field of coating compositions. It is made of the following raw material ratio, calculated by weight percentage: 25-40% water-based polyester resin, 4-5% water-based epoxy resin, 7-10% water-based amino resin, 25-35% Deionized water, 1.5‑2.5% pH adjuster, 0.3‑0.5% wetting agent, 0.2‑0.6% defoamer, 0.5‑1% dispersant, 1‑5% cosolvent, 10‑20 % pigments and fillers, 2-5% nano-alumina, 0.3-0.5% lithium magnesium silicate, 0.3-0.5% thickener, 0.5-0.8% leveling agent; made by mixing and stirring evenly. The baking paint is water-based and environmentally friendly, has good stability, high hardness, strong adhesion, fast drying, strong gloss retention, excellent aging resistance, good water resistance, convenient construction, low cost and no pollution.

Description

technical field [0001] The invention relates to the technical field of coating compositions. Background technique [0002] The ever-growing modern coating industry has higher and higher requirements for environmental protection. Reducing the discharge of organic solvents not only protects the environment, but also reduces costs, and is more secure for the health and safety of operators. [0003] At present, paints generally use organic solvents as raw materials. This kind of paint will not only cause a large amount of organic solvents to discharge and cause pollution, but also endanger the health of operators, laying a major hidden danger for environmental safety issues. Contents of the invention [0004] The technical problem to be solved by the present invention is to provide a water-based amino baking varnish and its preparation method. The water-based amino baking varnish is water-based and environmentally friendly, has good stability, high hardness, can be painted in...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
Patent Type & Authority Patents(China)
IPC IPC(8): C09D167/00C09D163/00C09D161/20C09D7/00C09D7/12
CPCC08K2201/011C08L2205/02C08L2205/025C08L2205/035C09D167/00C08L63/00C08L61/20C08L83/12C08L83/04C08L75/04C08L33/02C08K13/02C08K3/36C08K3/34C08K2003/2227C08G18/0823C08G18/4263C09D163/00C09D175/06C09D7/43C09D7/45C09D7/47C09D7/61C08K3/22C08L75/06C08G59/1472C08K5/053C08L33/08C08L33/10C08L83/06C09D5/027C09D161/20C09D163/10C09D179/02C09D7/80
Inventor 郑齐程璐胡中源董立志郭晓猛王亚轩祁艳东
Owner HEBEI CHENYANG INDAL & TRADE GROUP CO LTD