Manufacturing method of carbon fiber ecological decorating plate

A manufacturing method and decorative board technology, which is applied in the field of board manufacturing, can solve the problems of single application and failure to fully develop, and achieve the effects of good durability, low density and high strength

Active Publication Date: 2016-12-21
广西贺州恒达板业股份有限公司
View PDF20 Cites 6 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

Carbon fiber also has an important application in the field of sheet material manufacturing, but it is mostly used in the preparation of thermal insulation panels at present, such as the carbon fiber electric heating decorative panel with the application number CN00211458.5, and the carbon fiber insulating refractory electric heating decorative panel with the application number CN01241498. Single, and only utilizes the electrical and thermal conductivity of carbon fiber, but fails to give full play to its role

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0020] A method for manufacturing a carbon fiber ecological decorative panel, the method comprising the following steps:

[0021] a. Board core treatment: The board core is made of plates with a width of 30mm, a thickness of 10mm, and a length of 500mm and two layers of carbon fiber. Microwave treatment for 10 minutes, and then ultrasonic treatment for 10 minutes. After dipping treatment, take it out and place it in a cool and ventilated place for 0.5 hours, then dry it at 45°C, and repeat it twice; the flame retardant consists of ultrafine aluminum hydroxide 6 parts, 0.5 parts of phosphorus-containing flame retardant, the antibacterial agent is made from the raw materials of 10 parts by weight of Artemisia Artemisiae, 4 parts of Glycyrrhizae, 3 parts of Aloe Vera, 4 parts of tea leaves, and 80 parts of water. The preparation method is Artemisia Artemisiae, Glycyrrhizae, aloe vera, and tea leaves are chopped and dried, add water and cook on high heat for 15 minutes, and then c...

Embodiment 2

[0025] A method for manufacturing a carbon fiber ecological decorative panel, the method comprising the following steps:

[0026] a. Board core treatment: The board core is made of plates with a width of 40mm, a thickness of 15mm, and a length of 600mm and 3 layers of carbon fiber. After gluing, high-pressure impregnation with flame retardants and antibacterial agents is carried out; high-pressure impregnation is also performed. Treat for 12 minutes, then conduct ultrasonic treatment for 18 minutes. After dipping, take it out and place it in a cool and ventilated place for 1 hour, then dry it at 55°C, and repeat 3 times; the flame retardant is 7 parts by weight of ultrafine aluminum hydroxide, Made from 1.5 parts of phosphorus-containing flame retardant; traditional Chinese medicine antibacterial agent is made of 13 parts by weight of mugwort, 6 parts of licorice, 5 parts of aloe, 5 parts of tea, and 90 parts of water; the preparation method is mugwort, licorice, aloe 1. Chop ...

Embodiment 3

[0030] A method for manufacturing a carbon fiber ecological decorative panel, the method comprising the following steps:

[0031] a. Board core treatment: The board core is made of plates with a width of 60mm, a thickness of 18mm, and a length of 800mm and 4 layers of carbon fiber. After gluing, high-pressure impregnation with flame retardants and antibacterial agents is carried out; high-pressure impregnation is also performed. Treat for 15 minutes, then conduct ultrasonic treatment for 25 minutes. After dipping, take it out and place it in a cool and ventilated place for 2 hours, then dry it at 65°C, and repeat 4 times; the flame retardant is 9 parts by weight of ultrafine aluminum hydroxide, 3 parts of phosphorus-containing flame retardants are made; the traditional Chinese medicine antibacterial agent is made of 15 parts by weight of mugwort, 8 parts of licorice, 6 parts of aloe, 5 parts of tea leaves, and 100 parts of water. The preparation method is mugwort, licorice, alo...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

PUM

No PUM Login to view more

Abstract

The invention discloses a manufacturing method of a carbon fiber ecological decorating plate. The manufacturing method comprises three steps of plate core treatment, decorating plate treatment, and blank combination and gluing. During plate core gluing, carbon fibers are added, so that the performance of a product can be improved by using such characteristics of the carbon fibers as small density, high intensity, high durability, high resistant to corrosion, high strain capacity and the like; meanwhile, in a manufacturing process, a plate core and a decorating plate are respectively subjected to flame retardant and antibacterial treatment, so that the product is safer and more sanitary to use, and the competitiveness of the product in the market is enhanced.

Description

technical field [0001] The invention relates to the field of plate manufacturing, in particular to a method for manufacturing a carbon fiber ecological decorative plate. Background technique [0002] Carbon fiber is a new type of fiber material with high strength and high modulus fiber containing more than 95% carbon. It is a microcrystalline graphite material obtained by stacking organic fibers such as flake graphite microcrystals along the axial direction of the fiber, and undergoing carbonization and graphitization. Carbon fiber is "soft on the outside and rigid on the inside", lighter than metal aluminum, but stronger than steel, and has the characteristics of corrosion resistance and high modulus. It is an important material in national defense and civilian applications. It not only has the inherent intrinsic characteristics of carbon materials, but also has the softness and processability of textile fibers. It is a new generation of reinforcing fibers. [0003] Carbo...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

Application Information

Patent Timeline
no application Login to view more
Patent Type & Authority Applications(China)
IPC IPC(8): B27D1/06B27D1/08B27D5/00B27K3/52B27K5/00
CPCB27D1/06B27D1/08B27D5/00B27D5/006B27K3/52B27K5/001B27K2240/20B27K2240/30
Inventor 黄俊刘献奇陶晟蔡国雄
Owner 广西贺州恒达板业股份有限公司
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Try Eureka
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap